Search

The current study investigates the influence of hot rolling on the microstructure evolution of the near-surface region on AA7050 aluminum alloy and the corrosion performance of the alloy. It is revealed that hot rolling resulted in grain refinement in the near-surface region, caused by dynamic recrystallization, and equiaxed grains less than 500 nm can be clearly observed. Fibrous grains were evident in the hot rolled AA7050 aluminum alloy with relatively lower rolling temperature or larger rolling reduction, caused by the more severe elemental segregation at grain boundaries, which inhibited the progression of dynamic recrystallization. The density of the precipitates in the fibrous grain layer was higher, compared with those in the equiaxed grain layer, due to the increased dislocation density, combined with more severe elemental segregation, which significantly promoted the nucleation of precipitates. With the co-influence exerted by low density of precipitates and dislocations on the improvement of the corrosion performance of the alloy, the rolled AA7050 alloy with decreased density of precipitates and dislocations exhibited better corrosion resistance. [ABSTRACT FROM AUTHOR]

The quenching sensitivity of an Al–Zn–Mg–Cu alloy containing trace amounts of Sc and Zr is studied by interrupted quenching experiments. Electrical conductivity of the quenched samples and the hardness of the samples subjected to one-stage and two-stage aging, are measured to construct the time–temperature–transformation (TTT) curves and the time–temperature–property (TTP) curves. It is revealed that the quenching sensitivity of the alloy is mainly influenced by the precipitation of coarse η phases during slow quenching, which preferentially nucleate and grow at grain boundaries and at the Al3(Sc, Zr) dispersoids that are incoherent with the matrix. The quenching sensitivity increases with the size and quantity of the coarse η phases. The nose temperature is 290 °C for both TTT and TTP curves, where the phase transformation rate is the fastest and the quenching sensitivity is the highest. Compared to one-stage aged samples, two-stage aged samples exhibit lower quench sensitivity due to the reduced transformation rate from η′ phases to η phases after slow quenching. The quenching sensitive temperatures range from 206 to 358 °C for the one-stage aged samples and from 213 to 352 °C for the two-stage aged samples. Moreover, based on the simulated TTT and continuous cooling transformation curves, an optimized quenching process is proposed in the present work. [ABSTRACT FROM AUTHOR]

In order to improve the corrosion and heat resistance of Al-Mg-Si alloy conductor materials, Ce, Sc, Y and Zr were added in Al-Mg-Si alloy to regulate the microstructure. The Al-Mg-Si-Ce-Sc-Y alloy was designed with excellent pitting and intergranular corrosion resistance by obtaining the micron-sized Fe-containing second phase with a lower potential difference to Al matrix, more dispersed grain boundary precipitates with a higher proportion of Si particles, narrower width of PFZ and ideal distribution of intergranular precipitates. The Al-Mg-Si-Ce-Sc-Y alloy also maintained higher hardness, strength and electrical conductivity after overaging and annealing and the corrosion/heat resistance mechanisms were proposed. • The corrosion and heat resistance of Al-Mg-Si alloy conductors were further enhanced. • The mechanisms of pitting and intergranular corrosion mechanisms in Al-Mg-Si alloys were proposed. • The microalloying of Ce，Sc and Y in Al-Mg-Si alloys with high electrical conductivity was established. [ABSTRACT FROM AUTHOR]