Non-oxidative propane dehydrogenation (PDH) is becoming an increasingly important approach to propylene production, while cobalt-containing catalysts have recently demonstrated great potential for use in this reaction, providing efficiencies comparable to those of industrially employed Pt- and Cr-based catalytic systems. It is therefore essential to clarify the nature of their active sites, especially since contradictory opinions on this issue are expressed in the literature. In this study, efforts were made to determine the state of Co in cobalt aluminates (CoAl2O4-Al2O3) responsible for PDH under typical operating conditions (600 °C, 1 atm). It is shown that the catalyst with a low cobalt content (Co/Al = 0.1) ensured the highest selectivity to propylene, ca. 95%, while maintaining significant propylene conversion. The structural motifs such as cobalt oxide and metallic cobalt nanoparticles, in addition to tetrahedral Co2+ species in the CoAl2O4 spinel system, were evaluated as potential active-site ensembles based on the obtained catalytic performance data in combination with the XRD, H2-TPR, TEM and XPS characteristics of as-synthesized, spent and spent–regenerated catalysts. It is revealed that the most likely catalytic sites linked to PDH are the Co-oxide forms tightly covering alumina or embedded in the spinel structure. However, additional in situ tuning is certainly needed, probably through the formation of surface oxygen vacancies rather than through a deeper reduction in Co0 as previously thought. [ABSTRACT FROM AUTHOR]

The reduction of Co-based oxides doped with Al3+ ions has been studied using in situ XRD and TPR techniques. Al3+-modified Co3O4 oxides with the Al mole fraction Al/(Co + Al) = 1/6; 1/7.5 were prepared via coprecipitation, with further calcination at 500 and 850 °C. Using XRD and HAADF-STEM combined with EDS element mapping, the Al3+ cations were dissolved in the Co3O4 lattice; however, the cation distribution differed and depended on the calcination temperature. Heating at 500 °C led to the formation of an inhomogeneous (Co,Al)3O4 solid solution; further treatment at 850 °C provoked the partial decomposition of mixed Co-Al oxides and the formation of particles with an Al-depleted interior and Al-enriched surface. It has been shown that the reduction of cobalt oxide by hydrogen occurs via the following transformations: (Co,Al)3O4 → (Co,Al)O → Co. Depending on the Al distribution, the course of reduction changes. In the case of the inhomogeneous (Co,Al)3O4 solid solution, Al stabilizes intermediate Co(II)-Al(III) oxides during reduction. When Al3+ ions are predominantly on the surface of the Co3O4 particles, the intermediate compound consists of Al-depleted and Al-enriched Co(II)-Al(III) oxides, which are reduced independently. Different distributions of elemental Co and Al in mixed oxides simulate different types of the interaction phase in Co3O4/γ-Al2O3-supported catalysts. These changes in the reduction properties can significantly affect the state of an active component of the Co-based catalysts. [ABSTRACT FROM AUTHOR]