Search

The quenching sensitivity of an Al–Zn–Mg–Cu alloy containing trace amounts of Sc and Zr is studied by interrupted quenching experiments. Electrical conductivity of the quenched samples and the hardness of the samples subjected to one-stage and two-stage aging, are measured to construct the time–temperature–transformation (TTT) curves and the time–temperature–property (TTP) curves. It is revealed that the quenching sensitivity of the alloy is mainly influenced by the precipitation of coarse η phases during slow quenching, which preferentially nucleate and grow at grain boundaries and at the Al3(Sc, Zr) dispersoids that are incoherent with the matrix. The quenching sensitivity increases with the size and quantity of the coarse η phases. The nose temperature is 290 °C for both TTT and TTP curves, where the phase transformation rate is the fastest and the quenching sensitivity is the highest. Compared to one-stage aged samples, two-stage aged samples exhibit lower quench sensitivity due to the reduced transformation rate from η′ phases to η phases after slow quenching. The quenching sensitive temperatures range from 206 to 358 °C for the one-stage aged samples and from 213 to 352 °C for the two-stage aged samples. Moreover, based on the simulated TTT and continuous cooling transformation curves, an optimized quenching process is proposed in the present work. [ABSTRACT FROM AUTHOR]

In order to improve the corrosion and heat resistance of Al-Mg-Si alloy conductor materials, Ce, Sc, Y and Zr were added in Al-Mg-Si alloy to regulate the microstructure. The Al-Mg-Si-Ce-Sc-Y alloy was designed with excellent pitting and intergranular corrosion resistance by obtaining the micron-sized Fe-containing second phase with a lower potential difference to Al matrix, more dispersed grain boundary precipitates with a higher proportion of Si particles, narrower width of PFZ and ideal distribution of intergranular precipitates. The Al-Mg-Si-Ce-Sc-Y alloy also maintained higher hardness, strength and electrical conductivity after overaging and annealing and the corrosion/heat resistance mechanisms were proposed. • The corrosion and heat resistance of Al-Mg-Si alloy conductors were further enhanced. • The mechanisms of pitting and intergranular corrosion mechanisms in Al-Mg-Si alloys were proposed. • The microalloying of Ce，Sc and Y in Al-Mg-Si alloys with high electrical conductivity was established. [ABSTRACT FROM AUTHOR]

• The effects of Sc, Y and Zr on the performances and microstructure evolution of Al-0.7Mg-0.6Si-0.2Ce alloys were studied. • An excellent combination of strength, elongation and electrical conductivity was achieved with the addition of Sc and Y. • The strengthening and electrical resistance mechanism of the studied alloys were revealed by statistical calculation. [Display omitted] In order to achieve the compatibility between excellent mechanical properties and good electrical conductivity of Al-Mg-Si alloys, detailed investigation was carried out to understand the microstructure evolution and their influences on performances of different Al-0.7Mg-0.6Si-0.2Ce-X (X Sc, Y and Zr) alloys prepared by casting, homogenization, hot extrusion, solution and aging treatments. Under aging state, Ce can form a large number of micron-sized AlCeSi and a few AlCeFeSi phase. The strength increased to 334 MPa as a result of decreased grain size and improved precipitation effect and the electrical conductivity increased up to 53.53%IACS because of lower solute Si atoms. The β" precipitates were coarsened and consequently the volume fracture was largely reduced due to the presence of Sc element, leading to the decreased strength of 311 MPa. The more solute Mg, Si and Sc atoms increased the degree of free electron scattering and the electrical conductivity decreased to 51.86%IACS. It is also found that Sc significantly enhanced the elongation of the alloy from 11.8% to 18.0%, which might be attributed to the formation of Al 3 Sc and (Al, Si) 3 Sc phases. The addition of Y raised the electrical conductivity of Al-Mg-Si-Ce alloy to 55.79%IACS by ameliorating the volume fraction and distribution of β" precipitates and decreasing the solute Si atoms. The co-addition of Sc and Y inherited the advantages of such two alloys. The ultimate tensile strength, elongation, electrical conductivity of Al-0.7Mg-0.6Si-0.2Ce-0.2Sc-0.1Y alloy processed by aging treatments is 336 MPa, 19.4% and 53.11%IACS, respectively. [ABSTRACT FROM AUTHOR]

The effects of trace Sc and Y on the corrosion behaviors of cold-drawn Al-0.2Ce alloys were revealed by scanning Kelvin probe force microscopy (SKPFM), transmission electron microscopy (TEM), scanning electron microscopy (SEM), Electron Probe Micro-analyzer (EPMA), and electrochemical measurements. The results showed that the Al 3 Sc particles not only enable the increase of subgrain boundaries in the modified alloy after cold drawing but also improve the morphology and size of the Al 13 Fe 3 Ce phase. SKPFM analysis showed that the enrichment of Y around the Al 13 Fe 3 Ce phase in the modified alloy can decrease its electrochemical inertness and thus reduce the micro-galvanic corrosion susceptibility of the alloy. The results of the electrochemical analysis showed that the individual and composite addition of Sc and Y can improve the corrosion resistance of the cold-drawn Al-0.2Ce alloy. The corrosion potential and current of Al-0.2Ce-0.2Sc alloy are −0.892 V and 0.91 μA·cm−2, while the corrosion potential and current of Al-0.2Ce-0.1Y alloy are −0.918 V and 1.08 μA·cm−2, respectively. It is obvious that Sc element improves the corrosion resistance of Al-0.2Ce alloy more effectively than Y element. The corrosion depth of Al-0.2Ce-0.2Sc-0.1Y alloy was the smallest tested by immersion under the same conditions, and its corrosion potential and corrosion current were −0.842 V and 0.79 μA·cm−2, respectively, corresponding to the best corrosion resistance. The formal mechanism of pitting corrosion in the alloys is also discussed. [Display omitted] • Effect of Sc on microstructure and corrosion of Al-0.2Ce alloy was revealed. • The enrichment of Y atoms around Al 13 Fe 3 Ce can reduce the potential difference. • The corrosion behaviors of pitting corrosion induced by Al 13 Fe 3 Ce was discussed. • The equivalent circuit of the studied alloys was identified. [ABSTRACT FROM AUTHOR]

Corrosion behaviour of 2A97-T6 Al-Cu-Li alloy was investigated by anodic polarization, immersion test and quasi-in-situ analysis with corrosion morphology characterized by a range of electron microscopy techniques. It is revealed that selective dissolution of grain interior tends to occur in grains of high stored energies, resulting in corroded bands associated with dense precipitate bands in the alloy. The evolutions of corrosion morphology during immersion test and quasi-in-situ analysis are similar, which both exhibit well-defined crystallographic pits. By contrast, crystallographic feature was less evident for localized corrosion induced by anodic polarization, which may be associated with the extensive Cu re-distribution. • Corroded bands are confined within individual grains of high stored energies. • Corroded bands are related to precipitates. • Cu re-distribution promotes the localized corrosion development but compromises its crystallographic features. [ABSTRACT FROM AUTHOR]