Under high temperatures, fiber-reinforced polymers are destroyed, releasing heat, smoke, and harmful volatile substances. Therefore, composite structural elements must have sufficient fire resistance to meet the requirements established by building codes and regulations. Fire resistance of composite materials can be improved by using mineral fillers as flame-retardant additives in resin compositions. This article analyzes the effect of fire-retardant additives on mechanical properties and fire behavior of pultruded composite profiles. Five resin mixtures based on vinyl ester epoxy and on brominated vinyl ester epoxy modified with alumina trihydrate and triphenyl phosphate were prepared for pultrusion of strip profiles of 150 mm × 3.5 mm. A series of tests have been conducted to determine mechanical properties (tensile, flexural, compression, and interlaminar shear) and fire behavior (ignitability, flammability, combustibility, toxicity, smoke generation, and flame spread) of composites. It was found that additives impair mechanical properties of materials, as they the take place of reinforcing fibers and reduce the volume fraction of reinforcing fibers. Profiles based on non-brominated vinyl ester epoxy have higher tensile, compressive, and flexural properties than those based on brominated vinyl ester epoxy by 7%, 30%, and 36%, respectively. Profiles based on non-brominated epoxy resin emit less smoke compared to those based on brominated epoxy resin. Brominated epoxy-based profiles have a flue gas temperature which is seven times lower compared to those based on the non-brominated epoxy. Mineral fillers retard the spread of flame over the composite material surface by as much as 4 times and reduce smoke generation by 30%. [ABSTRACT FROM AUTHOR]

Fiber-reinforced polymer (FRP) composite materials are very versatile in use because of their high specific stiffness and high specific strength characteristics. The main limitation of this material is its brittle nature (mainly due to the low stiffness and low fracture toughness of resin) that leads to reduced properties that are matrix dominated, including impact strength, compressive strength, in-plane shear, fracture toughness, and interlaminar strength. One method of overcoming these limitations is using nanoparticles as fillers in an FRP composite. Thereby, this present paper is focused on studying the effect of nanofillers added to glass/epoxy composite materials on mechanical behavior. Multiwall carbon nanotubes (MWCNTs), nano-silica (NS), and nano-iron oxide (NFe) are the nanofillers selected, as they can react with the resin system in the present-case epoxy to contribute a significant improvement to the polymer cross-linking web. Glass/epoxy composites are made with four layers of unidirectional E-glass fiber modified by nanoparticles with four different weight percentages (0.1%, 0.2%, 0.5%, and 1.0%). For reference, a sample without nanoparticles was made. The mechanical characterizations of these samples were completed under tensile, compressive, flexural, and impact loading. To understand the failure mechanism, an SEM analysis was also completed on the fractured surface. [ABSTRACT FROM AUTHOR]