Microstructures and mechanical properties of Ni matrix composites reinforced with amorphous SiO 2 particles by in-situ pyrolysis of polycarbosilane (PCS) coated on Ni powders were studied in this paper. The submicron spherical amorphous SiO 2 particles instead of traditional SiC uniformly distributing in the composites result from the generated silicon source by PCS pyrolysis combined with oxygen impurity in the preparation. The prepared composites achieve high yield strength, 172 MPa, and ultimate tensile strength, 494 MPa, as well as outstanding ductility, total elongation 28.4 %, which is improved 13.9 %, 50.6 % and 160.6 % compared with those for pure Ni samples, respectively. The effects of solid solution strengthening, grain refinement strengthening, reinforcement particle strengthening and dislocations behavior of at amorphous/crystalline interface on the combination of high strength and ductility of the composites were discussed. [Display omitted] • Amorphous SiO 2 reinforced Ni matrix composites were fabricated by in-situ pyrolysis of polycarbosilane coated on Ni powders. • Amorphous SiO 2 instead of crystalline SiC formed by the combination of silicon generated in the pyrolysis with oxygen. • The composites exhibit a combination of excellent tensile strength and ductility. [ABSTRACT FROM AUTHOR]

ZSR-P loaded nano-TiO 2 composite photocatalysts (TiO 2 /ZSR-P) have been prepared by the sol–gel method using the by-product Zr-containing silica residue (ZSR) as precursors during the production process of zirconium oxychloride, the structure and properties of TiO 2 /ZSR-P were characterized in this paper. The results showed that the TiO 2 /ZSR-P composite photocatalysts were characterized by the uniform loading of nano-TiO 2 on the surface of amorphous SiO 2 particles in ZSR-P. TiO 2 and SiO 2 were combined by forming -Ti-O-Si- bonds at the interface and the crystalline structure of TiO 2 powders was identified a mixed phase of anatase and rutile, its loading amount was 17.14%, the particle size raged from 7 to 12 nm. The degradation rate of TiO 2 /ZSR-P to the concentration of 5 ppm and 10 ppm methyl orange solution reached 99.52% and 100% respectively after 140 min of ultraviolet irradiation, and it still maintained stable performance after repetitive-use of the catalyst for 4 times. [ABSTRACT FROM AUTHOR]