In this study, to investigate the problem of contact fatigue and the damage mechanism of an AD180 high-carbon semi-steel roll, rolling contact fatigue tests were conducted using specimens cut from the periphery of a roll ring. These specimens were characterized under different contact stresses using SEM, a profile system, an optical microscope, and a Vickers hardness tester. The results indicates that the main forms of fatigue damage of an AD180 high-carbon semi-steel roll are peeling, pitting corrosion, and plowing. Moreover, the surface of the roll exhibits delamination and plastic deformation characteristics under high contact stress. Meanwhile, the size and depth of peeling, as well as the amount of pitting corrosion, increase with the contact stress. Peeling is mainly caused by a crack that originates at the edge of the specimen surface and propagates along the pearlite structure and the interface between pearlite and cementite. High contact stress can lead to an increase in the crack propagation depth and angle, resulting in the formation of larger peeling. Under cyclic loading, the near-surface microstructure of the specimen hardens due to grain refinement and dislocation strengthening, and the depth of the hardened layer increases with the increase in contact stress. When the contact stress reaches 1400 MPa, the near surface structure of the specimen changes from pearlite to troostite. [ABSTRACT FROM AUTHOR]

The azimuth track is an important component of the radio telescope wheel–rail system. During operation, the azimuth track is inevitably subject to phenomena such as track wear, track fatigue cracks, and impact damage to welded joints, which can affect observation accuracy. The 110 m QiTai radio telescope (QTT) studied in this paper is the world's largest fully steerable radio telescope at present, and its track will bear the largest load ever. Since the welded joint of an azimuth track is the weakest part, an innovative welding method (multi-layer and multi-pass weld) is adopted for the thick welding section. Therefore, it is necessary to study the contact mechanical properties between the wheel and the azimuth track in this welded joint. In this study, tensile tests based on digital image correlation technology (DIC) and Vickers hardness tests are carried out in the metal zone (BM), heat-affected zone (HAZ), modified layer, and weld zone (WZ) of the welded joint, and the measured data are used to fit the elastic–plastic constitutive model for the different zones of the welded joint in the azimuth track. Based on the constitutive model established, a nonlinear finite element model is built and used to simulate the rolling mechanical performance between the wheel and azimuth track. Through the analysis of simulated data, we obtained the stress distribution of the track under different pre-designed loads and identified the locations most susceptible to damage during ordinary working conditions, braking conditions, and start-up conditions. The result can provide a significant theoretical basis for future research and for the monitoring of large track damage. [ABSTRACT FROM AUTHOR]

Rail transportation is a pivotal mode of land transport for its efficiency in transporting passengers and freight across short or long distances; hence, the reliability and safety of rail systems are of key importance. Rolling contact fatigue (RCF), characterized by the cyclic loading of wheel-rail contacts, presents a significant challenge in the rail industry. This study presents a comprehensive numerical investigation on the influence of different crack orientations on the contact stress of the rail profile and subsequently the fatigue life. Using finite element analysis (FEA) with Abaqus and FE-safe software, the study examined different crack orientations' impact on stress distribution and fatigue life of rail profiles. Employing the extended finite element method (XFEM), this study modeled cracks in rail profiles with different orientations: parallel, perpendicular, and oblique to the rail axis. finite element analysis was used to obtain stress distribution results, highlighting the impact of crack presence, and orientation on maximum contact stresses. Subsequently, fatigue analysis was performed using FE-safe software, wherein the FEA results were imported to estimate fatigue life and damage evolution. The study revealed that the presence of a crack significantly influences contact stress, fatigue life, and damage accumulation. The results further demonstrated that crack orientation has an impact on the severity of those effects. Oblique cracks exhibited higher impact compared to lateral and longitudinal cracks. The study provides valuable insights into rolling contact fatigue-related failures, aiding in better understanding and mitigation of such issues, thereby contributing to improved rail maintenance practices and system safety. [ABSTRACT FROM AUTHOR]

Surface initiated rolling contact fatigue (RCF) of gears and rolling bearings can lead to premature failure in mechanical transmission systems. The orientation of surface crack initiation closely depends on surface tractive force, while the mechanism leading to this dependence is still obscure. In this work, a numerical model is proposed to investigate the effect of friction on surface crack initiation in RCF. An inhomogeneous contact solver based on semi‐analytical method (SAM) is developed by combining the damaged‐coupled constitutive relation and the Eshelby's equivalent inclusion method. The damage accumulation and concurrent degradation of material properties are modeled with continuum damage mechanics (CDM). The effect of surface tractive force on the orientation of surface crack initiation is simulated and analyzed. Results indicate that the progressive evolution of damage under the cyclic loading is accompanied by the stress variation around the damaged area. The damaged area increases, and the crack initiation life decreases with an increasing coefficient of friction. Highlights: A new damage evolution model incorporating an inhomogeneous contact solver is developed.The possible causes of the orientation of surface crack affected by friction traction are analyzed.The simulated results of damage evolution and stress variation agree well with open literatures. [ABSTRACT FROM AUTHOR]

The prediction of wheel/rail rolling contact fatigue (RCF) crack initiation during railway operations is an important task. Since RCF crack evolution is influenced by many factors, its prediction process is complex. This paper reviews the existing approaches to predict RCF crack initiation. The crack initiation region is predicted by the shakedown map. By combining the shakedown map with various initiation criteria and the critical plane method, the crack initiation life is calculated. The classification, methodologies, theories and applications of these approaches are included in this paper. The advantages and limitations of these methods are analyzed to provide recommendation for RCF crack initiation prediction. This review highlights that wheel/rail dynamic characteristic, complex working conditions, surface defects and wear all affect the RCF crack initiation. The optimal selection of criteria is essential in the crack initiation prediction. Based on the research gap regarding the challenging process of crack initiation prediction detailed in this review, a proposed prediction process of RCF crack initiation is proposed to achieve a more accurate result. [ABSTRACT FROM AUTHOR]

Copyright of China Mechanical Engineering is the property of Editorial Board of China Mechanical Engineering and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

The damage mode of U75V rail steel in application is determined by its rolling wear behavior. In this paper, the pearlite microstructure of U75V steel is characterized to investigate the relationship between wear and fatigue behavior. The results show that, with decreasing of pearlite lamellar spacing, the wear resistance of the steel increases and the contact fatigue resistance decreases. The spacing decreasing causes the change of the wear mechanism from abrasive wear to adhesive wear, as well as the damage mode from wear damage to fatigue damage. The smaller the pearlite lamellar spacing is, the stronger the deformation of the cementite lamellar is. The thin cementite lamellar is hardly broken in the rolling friction to pile up a large number of dislocations in the ferrite matrix and the work hardening degree was improved. So, the plastic deformation layer is difficult to remove, and fatigue cracks are easy to initiate and extend to the interior of the material. [ABSTRACT FROM AUTHOR]

Copyright of China Mechanical Engineering is the property of Editorial Board of China Mechanical Engineering and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

• Three dynamic indicators for predicting plastic flow in railway systems based on the mechanics of wheel-rail contact, Tresca's yielding criterion and shakedown theory. • A dynamic method that is simple to model and fast to compute for predicting plastic flow in railway systems. • Key parameters affecting plastic flow and rolling contact fatigue. • A dynamic approach for the impact of plastic flow on rolling contact fatigue damage. • Effect of different degrees of plastic flow on rolling contact fatigue. To analyze the plastic flow of wheels and its impact on rolling contact fatigue (RCF), this article proposes a multibody dynamics approach that is simple to model and fast to compute, based on the mechanics of wheel-rail contact and Tresca yield criterion. This method is used to study the plastic flow of the wheels and is validated by comparing it with plastic flow analysis based on the shakedown theory. The study shows that the dynamics indicators of maximum shear stress, adhesion saturation and stress ratio effectively reflect the plastic deformation of the wheel. Additionally, increasing wheel speed and curve radius, and decreasing wheel-rail friction coefficient, can effectively reduce the area and severity of plastic deformation in the wheel. Ignoring the impact of temperature effects on RCF, it is found that the more severe the plastic flow, the greater the likelihood of RCF. That is, alleviating the plastic flow of the wheel can reduce RCF damage in wheels. This approach to managing the health of wheels provides a comprehensive understanding of the interplay between operational parameters and the mechanical behavior of wheel materials, guiding maintenance strategies and operational decisions to enhance safety and extend the lifespan of railway components. [ABSTRACT FROM AUTHOR]

Aiming at early detection of subsurface cracks induced by contact fatigue in rotating machinery, the knowledge-based data analysis algorithm is proposed for health condition monitoring through the analysis of acoustic emission (AE) time series. A robust fault detector is proposed, and its effectiveness was demonstrated for the long-term durability test of a roller made of case-hardened steel. The reliability of subsurface crack detection was proven using independent ultrasonic inspections carried out periodically during the test. Subsurface cracks as small as 0.5 mm were identified, and their steady growth was tracked by the proposed AE technique. Challenges and perspectives of the proposed methodology are unveiled and discussed. [ABSTRACT FROM AUTHOR]

An investigation on the White Etching Crack (WEC) phenomenon as a severe damage mode in bearing applications led to the observation that in a latent pre-damage state period, visible alterations appear on the surface of the raceway. A detailed inspection of the microstructure underneath the alterations reveals the existence of plenty of nano-sized pores in a depth range of 80 µm to 200 µm. The depth of the maximum Hertzian stress is calculated to be at 127 µm subsurface. The present study investigates the effect of these nanopores on the fatigue crack initiation in SAE 52100 martensitic hardened bearing steel. In this sense, two micro-models by means of the Finite Element Method (FEM) are developed for both a sample with and a sample without pores. The number of cycles required for the crack initiation for both samples is calculated, using the physical-based Tanaka–Mura model. It is shown that pores reduce the number of cycles in bearing application to come to an earlier transition from microstructural short cracks (MSC) to long crack (LC) propagation significantly. [ABSTRACT FROM AUTHOR]

To serve in a corrosive environment, a corrosion-resistant rail steel U68CuCr has been developed in China. In the present study, the wear behavior of U68CuCr was investigated and compared with the commonly used rail steel U71MnG by rolling contact friction tests. The results indicate that the mass loss and wear rate of U68CuCr are smaller than those of U71MnG. The wear rates under the dry condition are smaller than those under the water–oil condition. In addition, the formation of oxide and spalling finally achieves the dynamic equilibrium on the surface of two types of rail steels. However, the duration of the lubricative and protective wear debris layer is longer for U68CuCr. Moreover, the worn surface of U68CuCr is relatively flat, while the wear regime of U71MnG is more severe. The amount and volume of the spalling pits of U68CuCr are smaller. Furthermore, the plastic deformation layers are shallower, and the rolling contact fatigue cracks are shorter for U68CuCr because of the finer pearlitic microstructure. The results prove that the U68CuCr rail steel shows good wear-resistant ability, suggesting its superior suitability for application in high-speed railways in a marine environment. [ABSTRACT FROM AUTHOR]

• Typical factors affecting the wheel-rail dynamic response are comprehensively considered to reveal the short-term load characteristics of frog under complex conditions. Meanwhile, based on the ellipsoidal Gaussian extrapolation theory, long-term wheel-rail load characteristics are obtained. • Combined with the strain energy fatigue parameter theory, a prediction method for the fatigue life of nose rail under complex conditions based on load spectrum preparation was proposed. • The location between the 30 mm and 35 mm sections of the nose rail has the shortest rolling contact fatigue crack initiation life and should be focused on during damage inspection. The rail profile irregular variation and wheel-rail relationships complexity at the gap in the frog enhance the wheel-rail impact forces, frequently resulting in rolling fatigue damage under complex cyclic loads. Therefore, it is particularly important to study the transient rolling contact load characteristics of fixed frog and to compile load spectrum considering various complex conditions for analyzing the fatigue damage of frog and extending the service life of structure. In this paper, a 3D transient FE model of wheelset and fixed frog is established, revealing rolling contact behavior of wheel-rail in frog area from both macro and mesoscopic perspectives. In order to investigate long-term load characteristics of wheel and rail under complex service conditions, the changes of line conditions, load conditions, rail wear state and other influencing factors in actual operation are taken into account. Based on elliptic Gaussian kernel density theory, a method for compiling the load spectrum of fixed frog nose rail is proposed, and the FP method is used for fatigue crack initiation life prediction of nose rail in fixed frog. The results show that the force state is more severe when passing through the frog in straight reverse direction, and resonance is prone to occur in the third and fifth vertical bending modes of the frog, as well as the fourth and sixth vertical bending modes of the stock rail. The increase in factors such as speed, axle load, wheelset lateral displacement towards frog side and wing rail wear will exacerbate wheel-rail impact and shorten frog service life. Different factors have an impact on the overall amplitude, oscillation center range, and maximum frequency load of the wheel-rail force in the long-term load spectrum of the frog. The fatigue crack initiation area of nose rail is mainly in 30 mm–35 mm sections, which is consistent with the on-site flaw detection results, verifying the accuracy of the calculation method developed in this paper. [ABSTRACT FROM AUTHOR]

Track–vehicle severe interaction on track with small curve radius results in rail wear and corrugation, and wheel polygonization, which drain considerable resources for rail grinding and wheels re-profiling in metro lines. To reduce the damage caused by track-vehicle severe interaction, the paper analyzes the reasons leading to rail wear and then proposes an architecture of a metro vehicle with independently rotating wheels driven directly by permanent magnet synchronous motors. The architecture is axle guidance, offered by passive linkages, which ensures that all axles are oriented radially, while control strategy was kept as simple as possible, identifying only two basic traction conditions. The concept is first discussed and then validated through a comprehensive set of running dynamics simulation performed with a multibody software to evaluate rail wear and rolling contact fatigue in traction/braking, coasting with different cant deficiency/excess conditions. The multibody dynamics simulation shows that the proposed architecture is virtually capable of avoiding both wear and rolling contact fatigue damages, and achieves the highest possible track friendliness. The concept of the proposed architecture is a track-fiendly metro architecture and could be a good reference for reducing rail-track interaction damages and maintainace cost. [ABSTRACT FROM AUTHOR]

• First S-N curve of surface initiated damage under rolling contact fatigue. • Uniquely conservative mechanical fatigue failure definition used for surface damage. • RCF and torsional fatigue S-N curves have similar fatigue strength exponent. • Study unveils that torsion tests can predict RCF surface damage results 10x faster. • Different operating regimes identified based on RCF surface damage severity. This paper presents fundamental findings on equivalence of rolling contact fatigue (RCF) driven surface damage and torsional fatigue modes of failure. Fatigue experiments were conducted for both modes of failure using AISI 4130 case carburized steel specimens. A Thrust Bearing Surface Pitting Rig (TBSPR) was designed and developed to perform RCF tests on flat test specimens using thrust ball bearings. The experiments were conducted in boundary lubrication regime, simulating the contact conditions in tribological machine components. The current investigation presents a novel approach where the effect of contact pressure and number of fatigue cycles on the initiation of surface damage was characterized by surface profilometry of the wear track after each test to generate a stress-life (S-N) map. The S-N map provides unique insights to early detection of RCF driven fatigue damage. The S-N map was utilized to generate the surface damage S-N curve. Torsional fatigue experiments were conducted on the same material, and the S-N curves of both failure modes were compared. The comparison shows key similarities between the two S-N curves, as they differ by a simple scaling factor. This investigation demonstrates that RCF driven surface damage characteristics can be predicted by conducting much simpler, and faster, torsion fatigue tests. This paper also presents a novel methodology to determine contact pressures to avoid incipient micropitting/microdenting damage. [Display omitted] [ABSTRACT FROM AUTHOR]

[Display omitted] Material microstructure plays a key role in crack initiation under rolling contact fatigue. When studying microstructure with crystal plasticity finite element method (CPFE), mesh sensitivity study is of great importance, as the surface-near region is under high uniaxial stresses. In this paper, a new structured mesh strategy is purposed and compared with the classical unstructured mesh strategy. Modelling tests on a bi-grain and a polycrystal model show the calculation of geometrically necessary dislocation (GND) density, recently proposed as a suitable fatigue damage indicator, is highly dependent on mesh morphology, when GND hotspots tend to appear near distorted elements even in homogeneous materials. With uniform mesh size and shape, structured mesh elements can provide physically more acceptable GND calculations, which is particularly important in loading scenarios with complex stresses, such as rolling contact fatigue. Computational efficiency is also improved compared to unstructured models because a smaller number of elements are required in a structured mesh model and pre-processing of the mesh is not required. [ABSTRACT FROM AUTHOR]

• A first study of the effect of full creepage on RCF crack growth behaviour. • Predicted crack growth directions show a good agreement with field observation. • Lateral and spin creepages can significantly affect K II and K III evolutions. • Increase in spin creepage is more detrimental to RCF crack driving force. In heavy-haul railway systems, the experience of high traction force of rails in curved tracks significantly accelerates the rolling contact fatigue crack growth. The overall level of traction force and its detailed distribution within a contact patch can be determined by the extent of wheel slips in different directions, also referred to as creepage. However, few studies have focused on quantifying the influence of creepage on rolling contact fatigue crack growth behaviour. In this paper, a numerical method is proposed to investigate the non-proportional mixed-mode rolling contact fatigue crack growth behaviour in the presence of severe longitudinal, lateral and spin creepages. To partially validate the proposed numerical method, the predicted crack growth directions on the rail surface are compared with the cracking patterns obtained from field observations. A parametric study is also conducted to further quantify the influence of different creepage combinations on the evolution of stress intensity factors at the crack front. Results show that both lateral and spin creepages can significantly affect the phase and maximum magnitude of K II and K III during one complete loading cycle. Moreover, the increase of spin creepage is found to have a more detrimental effect on overall RCF crack driving force than the increase of the other two creepage components. [ABSTRACT FROM AUTHOR]

• A two-stage simulation strategy was proposed to investigate the mechanisms of RCF cracks on the rail, consisting of a dynamic FEM for wheel and rail interaction and a coupled static FEM/BEM for crack growth. • The critical wheel positions for crack propagation during wheel approaching to and departing from the crack were determined and correlated with the different cracking mechanisms. • The orientation of the crack in rail played an essential role in crack growth behaviors. Rolling contact fatigue (RCF) crack is one of dominating damages on the rail surface due to repeated wheel and rail contact. RCF defects, including squats and head checks, can potentially cause rail fracture failure if not treated in time. It is critical to accurately predict the pertinent damage for different operational conditions. A two-stage simulation strategy was proposed to investigate the mechanisms of RCF-induced cracks on the rail, consisting of a dynamic FEM for wheel and rail interaction and a coupled static FEM/BEM for crack growth. It was found that there are two critical wheel positions for crack propagation during wheel approaching to and departing from the pre-existed crack. The different cracking mechanisms at these two critical wheel positions are correlated with the local physical phenomena, i.e. , the traction at the wheel/rail interface, the relative distance between the contact patch and crack, and the sliding at crack faces. The twisting of the cracks from the transverse plane to the longitudinal plane at the railhead significantly reduces crack growth in mode I, enhances crack propagation in modes II and III, and shifts the dominant crack growth from the crack front center to the crack corners. The increased incline of the crack in the rolling direction promotes the crack to grow downward in opening mode I. [ABSTRACT FROM AUTHOR]

• FASTSIM algorithm implementation in Abaqus to consider slipping and adhesion zones of the wheel/rail contact patch. • XFEM rolling contact fatigue (RCF) analysis of a 60E1 rail profile considering creepages. • Validation of the developed rail model with data available in the literature. • Sensitivity analysis to determine the influence of contact conditions on the fatigue life of rails. In this work the influence of considering wheel-rail contact creepages on fatigue crack growth rates due to Rolling Contact Fatigue (RCF) is studied. For this purpose, the FASTSIM algorithm, which considers the moving complex pressure distribution with slipping and adhesion zones of the wheel-rail contact patch, has been implemented in Abaqus using FORTRAN code subroutines. The developed methodology has been validated with a 60E1 rail profile model which uses XFEM, by comparing the obtained Stress Intensity Factors (SIFs) and sub-surface shear stresses with numerical results available in the literature. Finally, the RCF crack propagation analysis of a 60E1 rail profile with different contact conditions has been performed using the XFEM. The obtained results justify the necessity of considering contact creepages on contact shear stresses for crack growth analysis. [ABSTRACT FROM AUTHOR]

The present work proposes a novel efficient numerical approach for the simulation of three-dimensional propagation of non-planar frictional crack under Rolling Contact Fatigue (RCF). The developed model relies on a global–local strategy involving the Semi-Analytical Method (SAM), dedicated to the resolution of 3D contact problems, and the eXtended-Finite Element Method (X-FEM), dedicated to the solving of 3D crack problems. Similar to a submodeling technique, it consists in performing a local X-FEM analysis of the 3D RCF crack problem by means of boundary conditions extracted from a prior global SAM analysis which solves the contact problem between two semi-infinite bodies without considering the crack. A powerful procedure for the transfer of relevant mechanical quantities between the SAM and X-FEM models is developed. It allows the use of non-matching and non-conforming discretization scheme for the global SAM model and the local X-FEM model, particularly worthwhile for the pre-processing stage. An initial arbitrary stress profile can be considered to investigate the influence of residual stresses on crack behavior. The non-intrusive SAM/X-FEM coupling is integrated into a fully automatic crack propagation algorithm. This provides a powerful and user-friendly tool suitable for industrial applications, which easily handles 3D long non-planar frictional crack growth in the region of interest. After introducing some details concerning the implementation of the model, a validation of the innovative SAM/X-FEM coupling is performed by using results from the literature. Furthermore, a practical example demonstrates the great potential of this novel numerical technique to simulate in a fast, robust and accurate way the 3D complex behavior of fatigue crack under moving contact. • Simulation of the 3D frictional crack propagation under rolling contact conditions. • Non-intrusive global–local approach based on the coupling of SAM and X-FEM. • Field transfer procedure allowing independent meshes for the SAM and X-FEM models. • Fast, efficient and robust resolution coupled with a pre-processing time saving. • Influence of residual stresses on crack behavior highlighted. [ABSTRACT FROM AUTHOR]

This paper aims to propose a new and fast method to estimate the multiaxial non-proportional elastic–plastic stress and strain time histories developed in rails due to rolling contact and evaluate its accuracy for fatigue analysis. The method has the pseudo-elastic stress time history as input, which is obtained by a coupled analytical and numerical method. Therefore, a method originally proposed for notch-root elastic–plastic stress–strain analysis was extended to the Rolling Contact Problem (RCF). The problem is solved incrementally and is established considering a set of equations composed by constitutive and multiaxial notch correction equations. Additionally, a kinematic cyclic plasticity model was included. An equivalent model based on the Finite Element Method was used for comparison purposes. The comparison was made in terms of multiaxial fatigue damage parameters in critical planes, according to fatigue analysis models developed by Matake and Brown & Miller. The more relevant advantage of the method over the non-linear FEM analysis is the possibility to readily obtain long elastic–plastic stress and strain histories and to perform material parameter and load case studies. The method proposed agrees with the equivalent FEM and proved to be a powerful tool for fast wheel-rail failure analysis, especially in RCF problems. [ABSTRACT FROM AUTHOR]

• The wear performance of the defected rail materials under various slip ratios and contact stresses was investigated. • The surface damage of the defected rail materials under various slip ratios and contact stresses was studied. • The effect of slip ratio and contact stress on crack propagation mechanisms near the dent was discussed. The defects on rail surface may have negative effects on the rolling contact fatigue (RCF) performance of the rail materials. This investigation researched on the RCF behaviors of the defected rail materials under various slip ratios and contact stresses. The results show that both the wear loss and the average crack length increase if the slip ratio or the contact stress increases. Moreover, the surface damage characteristics change from simple adhesion spots to significant fatigue crack grouping when slip ratio and contact stress rise. Finally, the experimental results also highlight that the slip ratio provides the deformation area for crack initiation whereas the contact stress accelerates the crack propagation by emphasizing the geometric effects. [ABSTRACT FROM AUTHOR]

Wheel rail rolling contact fatigue is a very common form of damage, which can lead to uneven rail treads, railhead nuclear damage, etc. Therefore, ANSYS software was used to establish a three-dimensional wheel–rail contact model and analyze the effects of several main characteristics, such as the rail crack length and crack propagation angle, on the fatigue crack intensity factor during crack propagation. The main findings were as follows: (1) With the rail crack length increasing, the position where the crack propagated by mode I moved from the inner edge of the wheel–rail contact spot to the outer edge. When the crack propagated to 0.3–0.5 mm, it propagated to the rail surface, causing the rail material to peel or fall off and other damage. (2) When the crack propagation angle was less than 30°, the cracks were mainly mode II cracks. When the angle was between 30 and 70°, the cracks were mode I–II cracks. When the angle was more than 70°, the cracks were mainly mode I cracks. When the crack propagation angle was 60°, the equivalent stress intensity factor reached the maximum, and the rail cracks propagated the fastest. [ABSTRACT FROM AUTHOR]