Search

The fiber-filled polymer composite is one of the best materials which provides a symmetrical superior strength and stiffness to structures. With the strengthening of people's environmental protection and resource reuse consciousness, the development of renewable materials, especially natural fiber-filled polymer composites, is receiving great attention. This study investigated the mechanical properties of polymer composites incorporating waste materials from the food processing industry and agricultural sources. Waste vegetal fiber-filled polymer biocomposites (WVFFPBs) with varying fiber types and 3D printing orientations were systematically fabricated. Subsequently, the tensile tests were executed to comprehensively assess the anisotropic mechanical behaviors of the WVFFPBs. The results demonstrated that WVFFPBs performed excellent anisotropic mechanical properties compared to pristine matrix samples as print orientation changed. As the printing angle increased from 0° to 90°, the tensile mechanical properties of the WVFFPBs displayed a decreasing trend. Moreover, the print orientation–anisotropic mechanical behavior relationship of 3D-printed WVFFPBs was revealed through the analysis of the material manufacturing characteristics and damage features. [ABSTRACT FROM AUTHOR]

Disposable surgical gowns are usually made from petroleum-based synthetic fibers that do not naturally decompose, impacting the environment. A promising approach to diminish the environmental impact of disposable gowns involves utilizing natural fibers and/or bio-based synthetic fibers. In this study, composite webs from polylactic acid (PLA) bicomponent fiber and natural fibers, cattail and kapok fibers, were prepared using the hot press method. Only the sheath region of the PLA bicomponent fiber melted, acting as an adhesive that enhanced the strength and reduced the thickness of the composite web compared with its state before hot pressing. The mechanical and physical properties of these composite webs were evaluated. Composite webs created from kapok fibers displayed a creamy yellowish-white color, while those made from cattail fibers showed a light yellowish-brown color. Additionally, the addition of natural fibers endowed the composite webs with hydrophobic properties. The maximum natural fiber content, at a ratio of 30:70 (natural fiber to PLA fiber), can be incorporated while maintaining proper water vapor permeability and mechanical properties. This nonwoven material presents an alternative with the potential to replace petroleum-based surgical gowns. [ABSTRACT FROM AUTHOR]

In this study, we utilized a hybridization approach for two different fibers to overcome the drawbacks of single-fiber-reinforced PLA composites. Coir fiber and bamboo leaf fiber were used as reinforcing natural fibers as their properties complement one another. Additionally, we combined thermal annealing with hybridization techniques to further improve the overall properties of the composites. The results showed that the hybridization of BF: CF with a ratio of 1:2 gave PLA-based hybrid composites optimal mechanical and thermal properties. Furthermore, the improvement in the thermal stability of hybrid composites, attributable to an increase in crystallinity, was a result of thermal annealing. The improvement in HDT in annealed 1BF:2CF hybrid composite was about 13.76% higher than that of the neat PLA. Annealing of the composites led to increased crystallinity, which was confirmed using differential scanning calorimetry (DSC). The synergistic effect of hybridization and annealing, leading to the improvement in the thermal properties, opened up the possibilities for the use of PLA-based composites. In this study, we demonstrated that a combined technique can be utilized as a strategy for improving the properties of 100% biocomposites and help overcome some limitations of the use of PLA in many applications. [ABSTRACT FROM AUTHOR]

A series of eco-friendly biocomposites with improved mechanical properties and interfacial interaction were prepared by melt-mixing natural fibers using a cellulose acetate derivative as a polymer matrix and used to evaluate their mechanical, thermal, and morphological properties. The natural fiber used as a biofiller was pre-surface-treated by a refining process using alkali and natural enzymes to improve compatibility and increase interfacial bonding with biopolymer substrate. To increase the processability of the cellulose material, the raw material was plasticized and the composition prepared in the form of pellets in a twin-screw extruder by mixing with an additive before being molded through an injection process. For each composition, the interfacial bonding force between different materials was confirmed through morphology analysis and evaluation of mechanical and thermal properties. When biofillers and a viscosity modifier were used at the same time, the fabricated biocomposites had controllable crystallinity, stiffness, and elasticity and showed improved mechanical strength, such as tensile strength and flexural strength. These results indicated that interfacial properties could be increased through interfacial interactions between two different components due to appropriate surface treatment. In addition, it was confirmed that a composition having interfacial interaction, not a simple mixture, could be prepared by lowering both glass transition and melting temperature. The lowering of glass transition temperature increased the elasticity of the biocomposites, which have the potential advantage of easier melt processing when applied to various injection parts. [ABSTRACT FROM AUTHOR]

In engineering applications, natural fiber composites must comply with fire requirements including the use of flame retardant. Furthermore, biocomposites are known to be water sensitive. Whether flame retardants affect the water sensitivity and whether water absorption affects the fire behavior and the mechanical performance of biocomposites are the two main topics addressed in this work. In this study, a flax fiber/epoxy composite flame retardant with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) or aluminum diethyl phosphinate (AlPi) was aged in humid atmosphere or by immersion in water. Water absorption kinetics revealed that DOPO induces an increase in equilibrium water content by approximately a factor of 2 due to its intrinsic hygroscopicity and/or its plasticizing effect on the epoxy matrix. In contrast, AlPi does not significantly change the water sensitivity of the biocomposite. Mechanical testing highlighted that, whatever the FR, the evolution of mechanical properties with ageing is governed by the moisture content. The drop of elastic modulus was attributed to a decrease in fiber rigidity due to plasticization, while the increase in tensile strength was assigned to an increase in fiber/matrix friction due to fiber swelling. As regards flame retardancy, only the highest water contents modified the fire behavior. For the AlPi containing biocomposite, the water release resulted in an increase by 50% of the time to ignition, while for the DOPO flame retardant biocomposite the water release was mainly postponed after ignition. [ABSTRACT FROM AUTHOR]

Natural fibre biopolymer composites with both fibres and matrix being derived from biomaterials are increasingly used in demanding applications, such as sensing, packaging, building, and transport, and require good electrical, thermal, and flame retardant properties. Herein, an investigation of the effectiveness of functionalising nonwoven cotton/poly(lactic acid) (PLA) fibre mats with graphene oxide nanosheets has been reported by using a facile dip-coating method followed by thermal reduction for enhancing the electric, thermal, and abrasion-resistance properties. The manufacturing processes for preparing biocomposites and introducing functionality are readily scalable. Experimental results reveal that with the addition of less than 0.5 wt% graphene nanoplatelets, the biocomposites showed significant improvements in abrasion resistance, electrical conductivity, thermal conductivity, and diffusivity. Furthermore, the composite shows excellent piezo-resistivity to act as strain sensors with a gauge factor of 2.59 at strains up to 1%. [ABSTRACT FROM AUTHOR]

Paunch is a fibrous solid residue consisting of partially digested feed from the stomachs of processed cattle. It is the largest untapped solid waste stream from animals at meat processing plants, and potentially a valuable source of fibres for the production of sustainable and potentially higher-value natural biocomposite materials. Paunch was obtained from the waste effluent of a red meat processing plant, and the fibre characteristics of the as-obtained material were studied and benchmarked against wood flour and ground buffel grass, with a view to evaluating the potential of paunch as a fibre for polymer composites. The ground paunch possessed a rough fibrous surface and fibre-like characteristics that were comparable to both wood flour and ground buffel grass, demonstrating their potential for use in composites. Without any pre-treatment or compatibilisation, composites of a representative biopolymer, poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and ground paunch were successfully produced for the first time via extrusion, with up to 50 wt% paunch content. Mechanical property analysis showed that, at 30 wt% content, PHBV/ground paunch composites yielded mechanical properties that were comparable to those of composites with ground buffel grass. [ABSTRACT FROM AUTHOR]

Natural fibers such as jute, cotton, and bamboo composites are becoming alternative materials to synthetic fiber composites, as their use raises awareness of environmental protection. Among natural fibers, jute and cotton fibers were used in this research to fabricate six-layered composites reinforced by spent tea leaves. Varying amounts (0, 5, 10, and 15 g) of spent tea leaf powder were incorporated as reinforcement with resin to improve and observe properties and determine usability. The prepared composites were investigated comparatively in terms of mechanical, microstructural, morphological, and thermal properties. As regards mechanical characterization, tensile, compression, and bending properties were tested in this research to compare the obtained data with the data available in the literature to show its practical application. The results indicated that significant improvements in mechanical properties were obtained from the composites up to a certain proportion of reinforcement. The addition of 10 g reinforcement of spent tea leaves improved tensile strength by 33.46% and compressive strength by 38.86%. In terms of microstructural, morphological, and thermal characterization, in-depth SEM, EDS, XRD, UV, FTIR, TGA, and DSC analyses were performed. The results revealed that advanced microstructural, morphological, and thermal properties were improved with a certain proportion of spent tea leaf reinforcement. [ABSTRACT FROM AUTHOR]