Search

This research studies natural rubber (NR) composite blends prepared with recycled polyethylene (PE), polyurethane waste (PU), silica (SiO2), and aluminum trihydroxide (ATH) under the proper mixing conditions using an internal mixer and a two-roll mill. The mechanical, impact, dynamic mechanical, and thermal properties, together with flammability, were investigated. NR/PU composites filled with a specific SiO2/ATH concentration resulted in excellent flame-retardant properties without using PE. Adding PE causes poor flammability, while using PU and SiO2 prevents flame extensibility of the composites. In addition, SiO2 and ATH synergistically improved both mechanical and dynamical mechanical properties. This is attributed to the reinforcement of SiO2 particles inside the matrix, whereas the ATH releases water as a flame retardant. The V-0 composites tested with UL-94 showed acceptable heat resistance, strength, and durability, making them suitable for interior and exterior applications in buildings without the lightweight requirement. [ABSTRACT FROM AUTHOR]

This study focuses on examining the influence of bast fibers on the flammability and thermal properties of the polylactide matrix (PLA). For this purpose, Urtica dioica and Vitis vinifera fibers were subjected to two types of modifications: mercerization in NaOH solution (M1 route) and encapsulation in an organic PLA solution (M2 route). In a further step, PLA composites containing 5, 10, and 15 wt% of unmodified and chemically treated fibers were obtained. The results of the tests show that only biocomposites containing mercerized fibers had a nearly 20% reduced flammability compared to that of PLA. Moreover, the biofiller obtained in this way belongs to the group of flame retardants that generate char residue during combustion, which was also confirmed by TGA tests. The M2 modification route allowed to achieve higher mass viscosity than the addition of unmodified and M1-modified fibers. The reason is that fibers additionally encapsulated in a polymer layer impede the mobility of the chain segments. The inferior homogenization of the M2-modified fibers in the PLA matrix translated into a longer combustion time and only a 15% reduction in flammability. [ABSTRACT FROM AUTHOR]

Despite a recent sustained preoccupation for developing biobased epoxies with enhanced applicability, such products have not been widely accepted for industry because of their inferior characteristics compared to classic petroleum-based epoxy thermosets. Therefore, significant effort is being made to improve the flame retardance of the most commonly used epoxies, such as diglycidyl ether-based bisphenol A (DGEBA), bisphenol F (DGEBF), novalac epoxy, and others, while continuously avoiding the use of hazardous halogen-containing flame retardants. Herein, a phosphorus-containing bisphenol, bis(4-(((4-hydroxyphenyl)amino)(6-oxido-6H-dibenzo[c,e][1,2]oxaphosphinin-6-yl)methyl)phenyl) phenylphosphonate (BPH), was synthesized by reacting bis(4-formylphenyl)phenylphosphonate with 4-hydroxybenzaldehyde followed by the addition of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) to the resulting azomethine groups. Environmentally friendly epoxy-based polymer thermosets were prepared by using epoxy resin as polymer matrix and a mixture of BPH and 4,4′-diaminodiphenylsulfone (DDS) as hardeners. A hyperbranched phthalocyanine polymer (HPc) and BaTiO3 nanoparticles were incorporated into epoxy resin to improve the characteristics of the final products. The structure and morphology of epoxy thermosets were evaluated by infrared spectroscopy and scanning electron microscopy (SEM), while the flammability characteristics were evaluated by microscale combustion calorimetry. Thermal properties were determined by thermogravimetric analysis and differential scanning calorimetry. The surface morphology of the char residues obtained by pyrolysis was studied by SEM analysis. [ABSTRACT FROM AUTHOR]

Polybenzoxazine (PBa) composites based on phosphorous-containing bio-based furfurylamine type benzoxazines (D-fu) and bisphenol-A type benzoxazines (Ba) were developed for flame retardation. The structure of D-fu was analyzed by Fourier transform infrared (FTIR) spectroscopy and 1H-NMR spectroscopy. The curing temperature of Ba/D-fu mixtures was systematically studied by differential scanning calorimetry (DSC). Thermogravimetric analysis (TGA) demonstrated the excellent char formation ability of the PBa composites with the addition of phosphorous-containing D-fu. The flame retardancy of the PBa composite materials was tested by the limited oxygen index (LOI), vertical burning test (UL-94) and cone calorimeter (CONE). The LOI and UL-94 level of PBa/PD-fu-5% reached 34 and V0 rate, respectively. Notably, the incorporation of 5% D-fu into PBa led to a decrease of 21.9% at the peak of the heat-release rate and a mass-loss reduction of 8.0%. Moreover, the fire performance index increased, which demonstrated that the introduction of D-fu can diminish fire occurrence. The role of D-fu in the condensed and gas phases for the fire-resistant mechanism of the PBa matrix was supported by SEM-EDS and TGA/infrared spectrometry (TG-FTIR), respectively. Dynamic mechanical analysis (DMA) revealed that the Tg of PBa flame-retardant composites was around 230 °C. Therefore, PBa composites are promising fire-retardant polymers that can be applied as high-performance functional materials. [ABSTRACT FROM AUTHOR]

In transport sectors such as aviation, automotive and railway, materials combining a high lightweight potential with high flame retardant properties are in demand. Polymeric foams are suitable materials as they are lightweight, but often have high flammability. This study focuses on the influence of different flame retardants on the burning behavior of Novolac based epoxy foams using Isophorone Diamine carbamate (B-IPDA) as dual functional curing and blowing agent. The flame retardant properties and possible modifications of these foams are systematically investigated. Multiple flame retardants, representing different flame retardant mechanisms, are used and the effects on the burning behavior as well as mechanical and thermal properties are evaluated. Ammonium polyphosphate (APP), used with a filler degree of 20 wt.% or higher, functions as the best performing flame retardant in this study. [ABSTRACT FROM AUTHOR]

This work is devoted to the influence of phosphazene modifiers with different substituents on the curing process, thermal properties and flammability of benzoxazine resin. Novel catalysts with m-toluidine substituents were introduced. The catalytic activity of studied phosphazene compounds decreased in the row: hexachlorocyclotriphosphazene (HCP) > tetra m-toluidine substituted phosphazene PN-mt (4) > hexa m-toluidine substituted phosphazene PN-mt (6) > hexaphenoxycyclotriphosphazene (HPP), where HPP is totally inactive. Two types of catalysis: basic and acid were proposed. A brief study of resulting properties of polybenzoxazines was presented. The addition of any studied modifier caused the decrease of glass transition temperature and thermal stability of polymers. The morphology of cured compositions was characterized by matrix-dispersion phase structure. All phosphazene containing polybenzoxazines demonstrated the improved flame resistance. [ABSTRACT FROM AUTHOR]

Biocomposites comprising a combination of natural fibres and bio-based polymers are good alternatives to those produced from synthetic components in terms of sustainability and environmental issues. However, it is well known that water or aqueous chemical solutions affect natural polymers/fibres more than the respective synthetic components. In this study the effects of water, salt water, acidic and alkali solutions ageing on water uptake, mechanical properties and flammability of natural fibre-reinforced polypropylene (PP) and poly(lactic acid) (PLA) composites were compared. Jute, sisal and wool fibre- reinforced PP and PLA composites were prepared using a novel, patented nonwoven technology followed by the hot press method. The prepared composites were aged in water and chemical solutions for up to 3 week periods. Water absorption, flexural properties and the thermal and flammability performances of the composites were investigated before and after ageing each process. The effect of post-ageing drying on the retention of mechanical and flammability properties has also been studied. A linear relationship between irreversible flexural modulus reduction and water adsorption/desorption was observed. The aqueous chemical solutions caused further but minor effects in terms of moisture sorption and flexural modulus changes. PLA composites were affected more than the respective PP composites, because of their hydrolytic sensitivity. From thermal analytical results, these changes in PP composites could be attributed to ageing effects on fibres, whereas in PLA composite changes related to both those of fibres present and of the polymer. Ageing however, had no adverse effect on the flammability of the composites. [ABSTRACT FROM AUTHOR]