Search

[Display omitted] • A simple but powerful solution to overcome the chronic bottleneck of the nanocatalyst delivery on oxide support: the carbothermal shock driven nanocatalyst formation on carbon nanofibers (CNFs) with small sizes and fine distribution can be delivered to oxide structures of choice while retaining high uniformity. • Fabrication of catalyst delivered porous oxide structures: the asymmetric sputtering of oxide on CNFs can induce the formation of openly porous hemi-tubular structures with tunable porosity and thickness. A simple subsequent calcination results in the transfer of catalysts from the CNF template to the porous oxide structures. • Superior hydrogen sulfide sensing properties: Uniform distribution of Pt nanoparticles on SnO 2 hemitubes showed superior H 2 S sensing performances (Response Rair/Rgas > 1500 at 5 ppm H 2 S) compared to state-of-the-art H 2 S sensors. To achieve powerful gas sensors oxide semiconductor chemiresistors, the uniform functionalization of nanocatalysts on the desired metal oxides is considered as a key strategy. However, still, it is challenging to achieve the nanocatalysts decoration on desired oxides without deterioration of target materials. In this study, thermal-shock (rapid joule-heating method) was applied to uniformly decorate Pt nanoparticles (NPs) on the surface of carbon nanofibers (CNFs) to achieve the uniform distribution of Pt NPs on one-dimensional structures. And then, SnO 2 was physically deposited on the Pt NPs loaded CNFs and continuous heat-treatment was conducted to transfer the Pt NPs to desired SnO 2 porous hemitubes. Thanks to the well-distributed Pt NPs on porous SnO 2 hollow structures, the Pt laoded SnO 2 hemitubes showed an exceptional sensitivity (R air /R gas = 1500 at 5 ppm) in H 2 S. Also, it showed high selectivity for H 2 S and high stability even under continuous gas exposure, confirming its potential as an effective H 2 S sensor. [ABSTRACT FROM AUTHOR]

• The non-noble metals are introduced on graphene-based fiber as a sensitizer for the high-performance chemiresistor. • Metal oxides on graphene fibers naturally are converted into metals at a relatively low temperature annealing (under 700 °C) due to catalytic effect of graphene. • The graphene fiber acts as a flexible conductive support as well as a catalyst for the deoxidation of metal oxide. • The metal/metal oxide/graphene fibers exhibited a 16 times higher response to NO 2 gas and recovery than metal oxide/graphene fiber without metal. • The proposed strategy opens a new avenue for the realization of high-performance devices, such as chemical catalysts, photoactive devices. [Display omitted] Noble metal/metal-oxide-based hybrid gas sensors exhibit a low operating temperature, remarkable sensitivity, and fast recovery. As additives, noble metals induce a catalytic sensitization effect, which promotes charge transfer from the metal oxide to the analyte molecules, the so-called spillover mechanism. This suggests that metal catalysts can improve gas sensing performance. Herein, for the first time, non-noble metals are introduced on hybrid metal oxide/graphene fibers as sensitizers to fabricate high-performance chemiresistive sensors. The formation of metal components can be effectively controlled by annealing the metal oxide on graphene. Remarkably, compared with the corresponding metal oxide/graphene fiber sensors without metal components, the metal/metal oxide/graphene fiber sensors exhibit over a 16-fold higher response to NO 2 gas as well as effective recovery characteristics. Specifically, the Cu/Cu 2 O/graphene and Ni/NiO/graphene fiber sensors operating at 150 °C exhibit sensitivities of 18.90 % and 0.82 %, respectively, for 5 ppm NO 2 gas. The proposed strategy to achieve flexible graphene fiber chemiresistors by decorating them with non-noble metal and metal oxide nanoparticles opens a new avenue for realizing high-performance devices, such as photovoltaic devices, photocatalysts, and chemical catalysts. [ABSTRACT FROM AUTHOR]