Search

• Tannic acid is neither a good flame retardant nor a highly swelling material. • TA combined with CLS reduces flammability of biocomposite by 30 % compared to PLA. • Mixing of TA with CLS in melt doesn't allow for PHRR reduction of more than 20 %. The purpose of this study was to determine the quantitative and qualitative effects of the form of natural phenolic compounds (NPCs) on the decomposition of polylactide (PLA) under different measurement conditions. For this purpose, thermogravimetry analysis (TGA), differential scanning calorimetry (DSC), and pyrolysis-combustion flow calorimetry (PCFC) analyses were carried out not only on individual raw materials like calcium lignosulfonate (BX), tannic acid (TA), BX chemically modified with TA (BMT), but also on PLA/BX, PLA/TA, and PLA/BMT composites with 3, 6, and 9 wt.% of filler. Moreover, the work checked whether to obtain satisfactory results it is necessary to carry out chemical modification lasting many hours, or whether simple physical mixing of ingredients (TABX) is enough, e.g. in proportions 1:2, 2:4, 3:6. The results of these analyses showed that TA is neither a good flame retardant nor a highly swelling material, but when combined with BX physically or chemically, it can produce an interesting synergistic effect. This work proves that chemically obtained BMT hybrid material allows to reduce flammability by 30 % compared to PLA which cannot be achieved by physically mixing these components in a polymer melt. On the other hand, the addition of TABX is sufficient to achieve a good thermal stabilization effect under processing conditions. [Display omitted] [ABSTRACT FROM AUTHOR]

This paper presents research findings on the influence of alkaline deacetylation on the thermal stability and fire reaction properties of non-pathogenic Basidiomycota fungi (mycelium) grown in molasses. The relationship between deacetylation conditions, such as incubation time and NaOH concentration, and the thermal and fire reaction properties of mycelium was investigated. The degree of deacetylation was also examined for its influence on the high-temperature thermal stability of mycelium, such as char formation. The findings indicated that the high-temperature thermal stability increased as the degree of deacetylation increased due to the conversion of chitin into chitosan as well as the presence of char-promoting hydroxyl‑terminated polysaccharide moieties. The study further investigated the influence of hollow glass microspheres on the thermal properties and microscale combustion behaviour of unmodified and deacetylated mycelium. This study provides an in-depth analysis of the thermal degradation mechanisms that govern the thermal stability and char-forming ability of unmodified and deacetylated mycelium. Additionally, the link between the thermal stability and fire reaction properties of mycelium and its deacetylated derivatives was established. Finally, the effectiveness of unmodified and deacetylated mycelium mats for fireproofing flammable glass fibre-reinforced epoxy laminates exposed to a simulated moderate-intensity fire was evaluated. [Display omitted] [ABSTRACT FROM AUTHOR]

[Display omitted] • A novel phosphorus-containing tertiary amine hardener (DCM) is synthesized. • DCM endows epoxy resin with desired heat resistance and char-forming capacity. • DCM improves the mechanical stiffness, robustness and toughness of epoxy resin. • DCM imparts superior flame retardancy and smoke suppression to epoxy resin. Although current phosphorus (P)-based hardeners endowed epoxy resins (EPs) with intrinsic flame retardancy, their addition usually reduced thermal and mechanical properties. In this work, a novel phosphorus-containing tertiary amine hardener (DCM) was synthesized using diphenylphosphinic chloride and 2,4,6-tris(dimethylaminomethyl)phenol (DMP-30), and applied to fabricate high-performance EP/DCM. Introducing P-containing group reduced the reactivity of tertiary amine of DCM, but EP/DCM gelled at 100 °C within 11.3 min, showing modest-temperature curing character. EP/DCM exhibited higher glass-transition temperature (T g) and char yield than virgin EP/DMP-30. Moreover, EP/DCM featured superior mechanical properties, of which the tensile strength, elongation at break and impact strength increased by 61.2%, 72.0% and 198.5%, respectively, relative to those of EP/DMP-30. DCM endowed EP thermosets with remarkable flame retardancy and smoke suppression. The limiting oxygen index (LOI) and UL-94 rating of EP/DCM reached 35.7% and V-0, respectively, with 36.2% and 22.6% reductions in peak heat release rate (PHRR) and peak smoke production rate (PSPR) compared with those of EP/DMP-30. This work pioneers an innovative strategy for creating high-performance EPs with satisfactory heat resistance, fire safety, and mechanical properties by curing with P-containing tertiary amine hardeners. [ABSTRACT FROM AUTHOR]

• A bio-based, phosphorus-phosphorus, hyperbranched oligomer (DIT) was synthesized. • DIT enabled EP to achieve durable fire safety. • DIT significantly improved mechanical robustness and toughness of EP. • DIT well maintained high transparency and thermal resistance of EP. The manufacture of transparent, durable fire-safe, strong yet tough epoxy resins (EPs) remains a great challenge. Herein, a novel hyperbranched, P-P synergetic, bio-based flame retardant (DIT) was synthesized, which was composed by 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO), bio-derived itaconic anhydride (ITA) and trihydroxymethylphosphine oxide (THPO) moieties. Adding 2 wt% DIT enabled the EP/2DIT sample to achieve a UL-94 V-0 rating and a limiting oxygen index (LOI) of 36.6%. The peak heat release rate and total smoke production of EP/4DIT sample with 4 wt% DIT were 23.8% and 19.9% lower than those of virgin EP sample. Notably, the EP/DIT sample featured durable flame retardancy because of the oligomeric structure of DIT. The high flame-retardant efficiency of DIT was mainly due to the synergism between DOPO and THPO. DIT simultaneously strengthened and toughened EP thermoset at a low addition (≤2 wt%), and 2 wt% of DIT increased the elongation at break, tensile strength, flexural strength and impact strength of EP/2DIT sample by 35.8%, 40.5%, 24.2% and 21.2%. Moreover, the glass transition temperature (T g) of EP/2DIT sample was equal to that of EP sample, and the high transparent was maintained. Hence, this work offers an all-rounded design for the creation of durable flame-retardant EPs with superior mechanical properties, thermal resistance and transparency by introducing hyperbranched, P-P, bio-based flame retardants, which shows huge potential and broad prospect. [Display omitted] [ABSTRACT FROM AUTHOR]

In this study, bamboo polymer composite (BPC) was prepared by blending of high-density polyethylene (HDPE) with boric acid - borax (Ba-Bx) pre-treated bamboo fibers as reinforcement material and by using maleic anhydride grafted polyethylene as coupling agent. BPCs were incorporated with conventional flame retardants (FRs) additives such as ammonium polyphosphate (APP) along with nano particles such as silicon dioxide (nano-SiO 2) and flame performance was investigated using cone calorimeter and limiting oxygen index analysis (LOI). The thermal behaviour of BPC was investigated under nitrogen atmosphere using thermogravimetric analyser (TGA). The maximum improvement in flammability was achieved with flame additive i.e., Ba-Bx 5%/APP15%. LOI value was found to be highest at Ba-Bx 5%/APP 13%/nano-SiO 2 2%. Mechanical properties of BPCs were analysed using flexural and tensile tests. While the flame and thermal properties of BPCs was improved significantly, the strength properties were marginally reduced due to application of FR additives. In general, APP as synergist with Ba-Bx improved thermal stability and flammability of BPCs. The effects of boron compounds (BCs) utilization as synergists with ammonium polyphosphate (APP) on the mechanical and fire retardant (FR) properties of wood polymer composites (WPCs) manufactured from wood flour, HDPE, MAPE is known through work by Kurt et al. (2012). BCs acts as synergist with APP, however, reduced mechanical properties of WPCs is an imminent result in this combination. Studies in the past have reported on reduced strength properties of wood or lignocellulosic biomass due to BCs treatment (Nagieb et al., 2011; Toker et al., 2009 etc). Further, additives with nano-scale, such as nanoclay, carbon nanotube, and nano-SiO2 are incorporated to polyethylene, polypropylene, and acrylic polymer for improving the tensile and flexural properties of the composites. Thermal stability, hardness, flame retardancy, and water resistance capacity were also found to enhance with addition of nano SiO 2. Pan et al. (2014) have investigated the synergistic effects of the combination of APP and nano-SiO2 on the flame retardant properties of WPCs, and APP/nano-SiO2 has significant improvement on heat release rate, total heat release, time to ignition, mass loss rate, and limited oxygen index. The most efficiency was appeared in APP 8%/nano-SiO2 6%. There is little or no information on synergistic effects of the combination of BCs, APP and nano-SiO2 on the flame retardancy, strength, thermal and recyclability properties of WPC. [ABSTRACT FROM AUTHOR]