Search

Aqueous Zn-ion hybrid supercapacitors (AZHSCs) combining the advantages of high‐energy batteries and high‐power supercapacitors see a bright future, but they still suffer from the poor capacity of carbonic cathodes. Herein, a functionalized porous carbon cloth (denoted as FPCC) electrode is demonstrated based on commercial carbon cloth (denoted as CC) tuning by structural and surface engineering. The constructed exfoliated porous carbon layer and the negatively charged functionalized interface not only increase the electrical double layer capacitance but also favor the chemical adsorption of Zn2+ to obtain additional pseudocapacitance. Consequently, the FPCC electrode delivers a high capacity of 0.16 mAh cm−2 at 4 mA cm−2, which is 923.8 times higher than CC, and a long cycle life (85.0% capacity retention after 30 000 cycles). More importantly, the Zn//FPCC AZHSC possesses an impressive energy density (3.3 mWh cm−3) and power density (240 mW cm−3), superior to many advanced batteries and supercapacitors. The quasi-solid-state device is also assembled as a demo. This modification strategy may provide new opportunities for high-performance AZHSCs. [ABSTRACT FROM AUTHOR]

Aqueous zinc‐ion batteries (AZIBs) are emerging as one of the most reliable energy storage technologies for scale‐up applications, but still suffer from the instability of Zn anode, which is mainly caused by the undesirable dendrite growth and side reactions. To tackle these issues, we formulate a new aqueous electrolyte with weak solvation effect by introducing low‐dielectric‐constant acetone to achieve H2O‐poor solvation structure of Zn2+. Experimental and theoretical calculation studies concurrently reveal that such solvation structure can: i) relieve the solvated H2O related side reactions, ii) suppress the dendrite growth by boosting the desolvation kinetics of Zn2+ and iii) in situ form solid electrolyte interface (SEI) to synergistically inhibit the side reaction and dendrite growth. The synergy of these three factors prolongs the cycling life of Cu/Zn asymmetric cell from 30 h to more than 800 h at 1 mA cm−2/1 mAh cm−2, and can work at more harsh condition of 5 mA cm−2/5 mAh cm−2. More encouragingly, Zn/V2O5 ⋅ nH2O full cell also shows enhanced cycling stability of 95.9 % capacity retention after 1000 cycles, much better than that with baseline electrolyte (failing at ≈700th cycle). [ABSTRACT FROM AUTHOR]

The inferior capacity and cyclic durability of V2O5 caused by inadequate active sites and sluggish kinetics are the main problems to encumber the widespread industrial applications of vanadium‐zinc batteries (VZBs). Herein, a cooperative redox chemistry (CRC) as "electron carrier" is proposed to facilitate the electron‐transfer by capturing/providing electrons for the redox of V2O5. The increased oxygen vacancies in V2O5 provoked in situ by CRC offers numerous Zn2+ storage sites and ion‐diffusion paths and reduces the electrostatic interactions between vanadium‐based cathode and intercalated Zn2+, which enhance Zn2+ storage capability and structural stability. The feasibility of this strategy is fully verified by some CRCs. Noticeably, VZB with [Fe(CN)6]3−/[Fe(CN)6]4− as CRC displays conspicuous specific capacity (433.3 mAh g−1), ≈100% coulombic efficiency and superb cyclability (≈3500 cycles without capacity attenuation). Also, the mechanism and selection criteria of CRC are specifically unraveled in this work, which provides insightful perspectives for the development of high‐efficiency energy‐storage devices. [ABSTRACT FROM AUTHOR]

With the merits of low cost, environmental friendliness and rich resources, manganese dioxide is considered to be a promising cathode material for aqueous zinc-ion batteries (AZIBs). However, its low ion diffusion and structural instability greatly limit its practical application. Hence, we developed an ion pre-intercalation strategy based on a simple water bath method to grow in situ δ-MnO2 nanosheets on flexible carbon cloth substrate (MnO2), while pre-intercalated Na+ in the interlayer of δ-MnO2 nanosheets (Na-MnO2), which effectively enlarges the layer spacing and enhances the conductivity of Na-MnO2. The prepared Na-MnO2//Zn battery obtained a fairly high capacity of 251 mAh g−1 at a current density of 2 A g−1, a satisfactory cycle life (62.5% of its initial capacity after 500 cycles) and favorable rate capability (96 mAh g−1 at 8 A g−1). Furthermore, this study revealed that the pre-intercalation engineering of alkaline cations is an effective method to boost the properties of δ-MnO2 zinc storage and provides new insights into the construction of high energy density flexible electrodes. [ABSTRACT FROM AUTHOR]

Transition metal organic framework materials and their selenides are considered to be one of the most promising cathode materials for nickel-zinc (denoted as Ni-Zn) batteries due to their low cost, environmental friendliness, and controllable microstructure. Yet, their low capacity and poor cycling performance severely restricts their further development. Herein, we developed a simple one-pot hydrothermal process to directly synthesize NiSe2 (denotes as NiSe2-X based on the molar amount of SeO2 added) stacked layered sheets. Benefiting from the peculiar architectures, the fabricated NiSe2−1//Zn battery based on NiSe2 and the Zn plate exhibits a high specific capacity of 231.6 mAh g−1 at 1 A g−1, and excellent rate performance (162.8 mAh g−1 at 10 A g−1). In addition, the NiSe2//Zn battery also presents a satisfactory cycle life at the high current density of 8 A g−1 (almost no decay compared to the initial specific capacity after 1000 cycles). Additionally, the battery device also exhibits a satisfactory energy density of 343.2 Wh kg−1 and a peak power density of 11.7 kW kg−1. This work provides a simple attempt to design a high-performance layered cathode material for aqueous Ni-Zn batteries. [ABSTRACT FROM AUTHOR]

The rational design of cathodes with high capacity, rate capability and stability is intriguing but challenging to achieve state-of-the-art aqueous Zn-based batteries. Co3O4 has aroused intense interest as cathodes of Zn-based batteries based on its attractive merits of high theoretical capacity in alkaline electrolytes and good thermodynamic stability. Unfortunately, the poor electric conductivity and insufficient active sites of Co3O4 materials impede their more extensive applications. Herein, a facile solvothermal reduction strategy is demonstrated to introduce oxygen defects into the ultrathin Co3O4 nanosheets (R–Co3O4), which function as an advanced cathode for Zn//Co batteries. In comparison with pristine Co3O4, the solvothermal reduction process can endow the R–Co3O4 sample with improved electric conductivity, enhanced specific surface area and enriched active sites. As a result, the alkaline Zn//Co battery with the R–Co3O4 cathode presents a considerable capacity (240.8 mA h g−1), good rate performance and excellent stability. Furthermore, an admirable energy density of 295.5 W h kg−1 (14 mW h cm−3) is achieved by this Zn//Co battery, surpassing that of most reported aqueous rechargeable batteries. [ABSTRACT FROM AUTHOR]