This work conducted an exploring study to minimize porosity cavities in a 300 mm × 2000 mm slab by mechanical heavy reduction when it has solidified. Real density measurements of slab samples indicated that, with a heavy reduction of 20 mm to slab after behind its solidification end, slab center was much denser and much more consistent. Porosity volumes at 1/4 and 1/2 width regions of slab were minimized from 5.19 × 10−4 cm3/g to 1.29 × 10−4 cm3/g and from 2.27 × 10−4 cm3/g to 1.05 × 10−4 cm3/g, respectively. Original Position Statistical-Distribution Analysis (OPA) of larger sampled slabs indicated that the heavy reduction was efficiently penetrated from slab surface into center to heal porosity cavities. Obtained results indicated positive influences of heavy reduction in healing porosity holes in slab even after solidification, when the temperature gradient of slab surface and center was about 280 °C. [ABSTRACT FROM AUTHOR]

To improve the phenomenon of serious power consumption of a ladle furnace, the impact of argon flow rate on power consumption in the refining process is investigated through theoretical calculations based on the principle of alternating current measurement using Rogowski coil and integrator circuit. The study divides the power supply phase into four distinct flow rate regions in a single furnace of DH36 steel, a low‐alloy, high‐strength ship plate steel commonly used in shipbuilding and offshore platforms. The analysis of active power, current, and voltage trends, along with average power consumption per second at each flow rate region, reveals a potential for efficient reduction in power consumption. Additionally, experiments with different argon flow rates (300, 400, and 500 NL min−1) during the power supply stages of multifurnace argon tests of AB/A steel show improvements in desulfurization rate, heating rate, processing time, and power consumption per ton of steel heated by 1 °C and power consumption per ton of steel per second. [ABSTRACT FROM AUTHOR]