Search

Thermally modified wood is becoming an increasingly popular material for different applications in buildings. Laboratory tests indicated a positive effect of thermal modification on durability, dimensional stability and thermal conductivity of wood. Therefore, windows and facade elements made of thermally modified Norway spruce and non-modified Norway spruce were tested in the field and installed in different test objects which were exposed at five locations in Europe (Slovenia, Germany, Sweden, and Spain). Results from monitoring showed that elements and windows made of thermally modified spruce (TMS) had considerably lower wood moisture content compared to the ones made of non-modified spruce and that wax further positively influenced moisture performance. Colour changes of TMS were more intensive compared to non-modified spruce but were successfully retarded by adding pigments to the wax. Mould and stain growth was largely dependent on the location, amount of precipitation and relative humidity. [ABSTRACT FROM AUTHOR]

Thermal modification is the most important commercial modification procedure. Thermally modified (TM) wood has improved durability, but its performance does not meet expectations predominately under moist conditions. To reduce water uptake of TM wood, Norway spruce specimens were treated with suspensions of a natural wax by dipping impregnation (DipI) or by vacuum-pressure impregnation (VPI). Wax-treated specimens were subsequently TM at 185, 200, 215, and 230°C. Control specimens were heated up to 100°C only. Contact angle (CA), short-term and long-term water uptake, bending strength, and performance against wood decay fungi of the resulting material were determined. The results show that a combination of wax treatment and thermal modification have a synergistic effect that considerably improves hydrophobicity, reduces liquid water uptake, slows down water vapor uptake, and improves the resistance against fungal decay of the treated material. [ABSTRACT FROM AUTHOR]

This paper is an overview of our recent investigations of liquefied wood (LW) for preparation and application of wood adhesives and wood surface finishes. For the purpose of wood bonding, poplar wood (Populus nigra L.) was liquefied with ethylene glycol (EG) and sulphuric acid. The process of the curing of LW at different conditions was characterized using differential scanning calorimetry (DSC). The effect of the press temperature and the pressing time on the shear strength of bonds was monitored after the bonding of 5mm thick beech (Fagus sylvatica L.) lamellas. According to the results of DSC measurements, the curing process of the LW took place in two phases. In the initial physical phase the removal of water and EG from the LW occurred. This phase was followed by an exothermic chemical reaction. It was found that the optimum conditions for bonding beech lamellas were: a ratio between poplar and EG of 1:1, a press temperature of 180°C, and a pressing time of 12 minutes. Using such conditions it was possible to obtain bonds with a dry shear strength of about 7N/mm². For preparation of polyurethane wood coatings, poplar wood was liquefied with diethylene glycol (DEG) and the excessive DEG was removed from the reaction mixture prior to curing with isocyanate type hardener. For the purpose of preparation of light-coloured polyurethane coatings from bleached liquefied wood, liquefaction of wood was conducted with a mixture of polyethylene glycol (PEG) and glycerol (GLY) at a 9:1 ratio. Both LW based PU coatings and bleached LW based PU finishes were in the most relevant properties comparable to commercial polyurethane wood coatings. [ABSTRACT FROM AUTHOR]