Search

The purpose of this study was to investigate the protective effect of a glass ionomer cement (GIC) consisting of fluoro-zinc-silicate glass on the demineralization of bovine dentin using the ultrasonic pulse-echo method. The findings were compared with those obtained using a conventional GIC. Slabs of dentin from bovine teeth were sliced, shaped into a rectangular form, and immersed in 0.5 M ethylenediaminetetraacetic acid solution at 25ºC for 6 days, followed by storage in distilled water for 3 days. After demineralization, they were immersed in artificial saliva with and without the GIC specimens. The propagation times of the longitudinal ultrasonic waves in the samples were measured. The ultrasonic velocities of the fluoro-zinc-silicate glass-containing GICs were significantly increased 2-3 days after the start of the experiment and showed an upward trend thereafter. These findings indicate that the GICs containing fluoro-zinc-silicate glass might exhibit the potential to promote remineralization in the dentin. [ABSTRACT FROM AUTHOR]

Objective: To examine the effect of filler contentTo examine the effect of filler content on structural coloration of experimental flowable resin composites. Overview: Experimental composites containing spherical fillers and different filler contents (30, 40, 50, 60 and 70 wt%), a structural colored resin composite (Omnichroma), and a nanohybrid flowable resin composite (Gracefil LoFlo) were used. The optical characteristics of the specimens were measured on standard black and white backgrounds using a spectrophotometer under CIE D65 illuminant and the L*a*b* values were determined. The color matching abilities to artificial teeth were evaluated using the ΔE*ab and ΔE00 color difference formulas. One‐way analysis of variance and Tukey's post hoc test were used. The spectral reflectance of experimental composites showed different trends in different backgrounds, plate thickness, and filler contents. In particular, higher spectral reflectance was observed on the white background at wavelengths ranging from 450 to 700 nm in both 1.5 and 3.0 mm plates when compared to the black background. The percent reflectivity tended to decrease with a decrease of the filler contents. The color matching abilities of the experimental composites improved with the increase in the filler contents. Conclusions: Structural coloration of the flowable resin composites were affected by the filler contents. Clinical significance: Clinical Significance: Higher filler contents might be needed to achieve the optimal color properties of structural colored flowable resin composites, thereby improving the restoration esthetics. [ABSTRACT FROM AUTHOR]

Objectives: This study evaluates the effect of self-assembling peptide P11-4 (Curodont Repair, CDR) on bovine enamel remineralization by measuring changes in ultrasonic propagation velocity.Methods: Six specimens per group were prepared by sectioning bovine teeth into enamel blocks. These blocks were then immersed in lactic acid buffer solution (pH = 4.75) for 10 min twice a day and stored in artificial saliva. Other specimens were first treated with CDR, followed by a 10-min immersion in the lactic acid buffer solution twice a day, before storage in artificial saliva. The propagation time of longitudinal ultrasonic waves was measured using a pulser/receiver. Six specimens were used for each treatment protocol. The obtained data were statistically analyzed using ANOVA followed by Tukey's honestly significant difference tests (α = 0.05). Specimens were observed using laser scanning microscopy and scanning electron microscopy.Results: Sonic velocity was found to decrease with time for specimens stored in the demineralizing solution. On the other hand, increases in sonic velocity were found for specimens treated with CDR. These specimens also exhibited signs of mineral deposition.Conclusions: By measuring the ultrasonic propagation velocity, it can be concluded that CDR application has an ability to promote bovine enamel remineralization. [ABSTRACT FROM AUTHOR]

Objective Materials and Methods Results Conclusions The color matching of single‐shade resin composites after in‐office whitening was investigated.Four single‐shade resin composites were used. A total of 35% hydrogen peroxide was used as the whitening agent. The resin composite was placed in a cavity of an artificially discolored bovine tooth. The color differences between the restoration and surrounding enamel before and after whitening were determined based on ΔE*ab, ΔE00, and ΔWID. The color stability, surface roughness (Sa), and surface gloss (GU) of the resin composite alone were also evaluated. Statistical analyses were performed using repeated‐measures analysis of variance with the Tukey–Kramer test.Based on the 50:50% of perceptibility and acceptability thresholds of ΔE*ab and ΔE00, none of the resin composite restorations were clinically acceptable before or after whitening. Regarding ΔWID, although all resin composites showed “acceptable match” in the baseline, they showed “mismatch” after the third session of whitening. Most of the resin composites alone were stable in color against whitening.Although the single‐shade resin composites failed to achieve the expected color matching on discolored teeth either before or after the whitening, the impact of the whitening on the color of the resin composite alone may be negligible. [ABSTRACT FROM AUTHOR]

This study investigates how the cavity depth of restorations influences the color adjustment potential of universal shade bulk-fill resin composites. Standard cavities, with diameters of 4 mm and depths of either 2 or 4 mm, were created at the center of artificial teeth occlusal surfaces. A structural-colored bulk-fill resin composite and two pigment-incorporated universal shade bulk-fill resin composites were used. Each resin composite was placed into the cavity to assess its color adjustment potential in relation to the artificial tooth color. Following application, the resin composites' surfaces were polished using diamond-impregnated silicone polishers. Color difference analysis revealed ΔE*ab values of 3.3-4.6 and 2.2-9.6 for structural-colored resin composites and pigment-incorporated universal shade resin composites, respectively, as well as ΔE 00 values of 2.7-3.4 and 1.7-5.8 for these resin composites, respectively. These findings suggest that the tested bulk-fill resin composites' color adjustment potential was influenced by restoration depth.

Purpose: To examine the effects of an ion-releasing filler-containing gel on the remineralization of dentin using optical coherence tomography (OCT)., Methods: Dentin slabs of bovine teeth were sliced and shaped into a rectangular form. Specimens were treated with undersaturated 0.1 M lactic acid buffer solution (pH 4.75) for 10 minutes and then placed in artificial saliva (pH 7.0). This procedure was repeated three times a day for 28 days. The dentin remineralization effects of a fluoride/S-PRG filler-containing gel (PRG) and a 38% SDF solution (SDF) on dentin slabs of bovine teeth were compared. After treatment, the dentin slabs were immersed in a 0.1 M lactic acid buffer solution and then placed in artificial saliva. This procedure was repeated three times a day for 28 days. OCT imaging was conducted on the selected location of the dentin surface. The peak intensity and width at 1/e² were recorded in each of the six areas on the sample and averaged. Each group had a sample size of 10. Knoop hardness number (KHN) measurements and scanning electron microscopy (SEM) observations were also conducted. The data for each group were subjected to a one-way repeated-measures ANOVA and Tukey tests (α= 0.05). The samples were also observed using SEM., Results: The peak signal intensities of SDF and PRG decreased on day 7 and then slightly increased during the experimental period for the one-off application groups and then decreased for frequent-time application groups. Although the width at 1/e² in the untreated specimens decreased over the test period, SDF and PRG for the one-off application groups exhibited an increase in widths on day 7 followed by a slight decrease, whereas it increased for the frequent-time application groups. The average KHN of the dentin samples exhibited the same tendency as the width at 1/e². Closure of the dentin tubules and crystal precipitation were detected on the surface of both SDF and PRG groups., Clinical Significance: S-PRG filler-containing gel might have the ability to prevent dentin demineralization and could be useful for the prevention of hard-to-access lesions. This material achieved remineralization of the demineralized root dentin and had the same remineralization ability as SDF in vitro., Competing Interests: The authors certify that they have no proprietary, financial, or other personal interest of any nature or kind in any product, service, and/or company that is presented in this article. This work was supported, in part, by Nakao Foundation, Grants-in-Aid for Scientific Research (C) 19K10158, 19K10159, from the Japan Society for the Promotion of Science. This project was also supported, in part, by the Sato Fund, Uemura Yasuo-Haruko Fund, and by a grant from the Dental Research Center of Nihon University School of Dentistry, Japan., (Copyright©American Journal of Dentistry.)

Purpose: To evaluate the ability of a pencil-type transducer connected to a pulser-receiver to measure remaining dentin thickness (RDT)., Methods: A total of 24 freshly extracted bovine incisors were used to prepare dentin disks with certain thicknesses (0.5, 1.0, 1.5 and 2.0 mm). The thicknesses of the specimens were measured with an ultrasonic technique using a pencil-type transducer, and the data obtained were compared with the direct measurement obtained using a micrometer. The Bland-Altman comparison method and paired t-test were performed at a 0.05 significance level., Results: The agreement between different measurement methods was analyzed to evaluate the inter-methodology variation. The Bland-Altman comparison method revealed a mean difference of 0.0098 ± 0.724 mm between the ultrasonic technique and the direct measurement, with the 95% Bland-Altman limits of agreement ranging from 0.1322 to 0.1517 mm., Clinical Significance: Ultrasonic measurement using the pencil-type transducer may be a promising method to evaluate remaining dentin thickness., Competing Interests: The authors declared no conflict of interest. This work was supported in part by Grants-in-Aid for Scientific Research, 19K10158 and 19K10159, from the Japan Society for the Promotion of Science. This project was also supported in part by the Sato Fund and by a grant from the Dental Research Center of the Nihon University School of Dentistry, Japan., (Copyright©American Journal of Dentistry.)