Search

There have been numerous studies on shotcrete based on strength and durability. However, few studies have been conducted on rheological characteristics, which are very important parameters for evaluating the pumpability and shootability of shotcrete. In those studies, silica fume has been generally used as a mineral admixture to simultaneously enhance the strength, durability, pumpability, and shootability of shotcrete. Silica fume is well-known to significantly increase the viscosity of a mixture and to prevent material sliding at the receiving surface when used in shotcrete mixtures. However, the use of silica fume in shotcrete increases the possibility of plastic shrinkage cracking owing to its very high fineness, and further, silica fume increases the cost of manufacturing the shotcrete mixture because of its cost and handling. Colloidal silica is a new material in which nano-silica is dispersed in water, and it could solve the above-mentioned problems. The purpose of this research is to develop high-performance shotcrete with appropriate levels of strength and workability as well as use colloidal silica for normal structures without a tunnel structure. Thereafter, the workability of shotcrete with colloidal silica (2, 3, and 4%) was evaluated with a particle size of 10 nm and silica fume replacement (4 and 7%) of cement. In this study, an air-entraining agent for producing high-performance shotcrete was also used. The rheological properties of fresh shotcrete mixtures were estimated using an ICAR rheometer and the measured rheological parameters such as flow resistance and torque viscosity were correlated with the workability and shootability. More appropriate results will be focusing on the Bingham model properties such that the main focus here is to compare all data using the Bingham model and its performance. The pumpability, shootability, and build-up thickness characteristics were also evaluated for the performance of the shotcrete. This research mainly focuses on the Bingham model for absolute value because it creates an exact linear line in a graphical analysis, which provides more appropriate results for measuring the shotcrete performance rather than ICAR rheometer relative data.

BACKGROUND/AIMS Aberrant DNA methylation has a specific role in field cancerization. Certain molecular markers, including secreted frizzled-related protein 2 (SFRP2), tissue factor pathway inhibitor 2 (TFPI2 ), N-Myc downstream-regulated gene 4 (NDRG4) and bone morphogenic protein 3 (BMP3), have previously been shown to be hypermethylated in colorectal cancer (CRC). We aim to examine field cancerization in CRC based on the presence of aberrant DNA methylation in normal-appearing tissue from CRC patients. METHODS We investigated promoter methylation in 34 CRC patients and five individuals with normal colonoscopy results. CRC patients were divided into three tissue groups: tumor tissue, adjacent and nonadjacent normal-appearing tissue. The methylation status (positive: methylation level >20%) of SFRP2 , TFPI2 , NDRG4 , and BMP3 promoters was investigated using methylation-specific PCR. RESULTS The methylation frequencies of the SFRP2 , TFPI2 , NDRG4 and BMP3 promoters in tumor/adjacent/nonadjacent normal-appearing tissue were 79.4%/63.0%/70.4%, 82.4%/53.6%/60.7%, 76.5%/61.5%/69.2%, 41.2%/35.7%/50.0%, respectively. The methylation levels of the SFRP, TFPI2, NDRG4 and BMP3 promoters in tumor tissues were significantly higher than those in normal-appearing tissue (SFRP2, p=0.013; TFPI2, p

Recently, there have been reports of severe symptoms of wear in bearings due to foreign substances mixed in lubricants. Therefore, studying the effects of foreign substances (such as combustion products and metallic debris) on the wear characteristics of journal bearings and proposing appropriate management standards for lubricant cleanliness have become necessary. Studies on the effect of particle size and concentration of foreign substances on surface damage have actively progressed in the recent times. These studies indicate the possibility of foreign sub- stances causing direct wear of bearing surfaces. However, experiments conducted until now involve only basic tests such as the Pin-on-Disk test instead of those involving real bearing systems. This study experimentally examines the damage to the surface of a journal bearing due to foreign substances (combustion products and alumina) mixed with the lubricant, as well as the effect of the type and size of particles on its wear characteristics. The study uses an exper- imental journal bearing similar to a real bearing system for conducting the lubrication test. Hydrodynamic Lubrication (HL) numerical analysis, experiment results, and film parameters are used for calculating the operating conditions required for achieving the desired film thickness, and the results of the analysis are modified for considering the sur- face roughness. The run-time of the experiment is 10 min including the stabilization process. The experiment results show that alumina particles larger than the minimum film thickness cause significant surface damage. Keywordsabrasive wear(연삭마멸), combustion products(연소산화물), damage(손상), journal bearing(저널 베어링), metallic debris(금속성 이물질)