Search

This paper aims to investigate the mechanical and rheological properties of magnetorheological elastomer (MRE) in marine ecosystems. The prepared samples comprised silicone rubber (SR) and 70 wt% micron-sized carbonyl iron particles (CIPs), immersed in an artificial marine ecosystem using salt water (Natrium Chloride) for 30 days. The mechanical properties of MRE samples were evaluated using hardness and quasi-static tensile tests. While the rheometer was used to investigate the rheological properties of their storage modulus condition with magnetic field stimulation. Further analysis of the defects and damages caused by salt water ageing was done through morphological observation using scanning electron microscope (SEM) technology. The results showed that the hardness and tensile strength of MRE samples that were soaked in salt water were affected over time. Lower values of hardness and tensile strength were obtained after 30 days due to the presence of Na + and Cl - , which acted as an accelerator to the hydrolyzation process of the MRE. The process then, enhanced the water ingress capability into the matrix to cause the molecular changes. Interestingly, for rheological properties, 30 days of salt water ageing allowed the water molecules to move the MRE matrix molecular chains apart, a process known as plasticization and thus increasing the MR effect. Furthermore, morphological evidence was established to determine the MRE changes during salt water ageing. The research findings should greatly contribute to a better understanding of the effect of salt water on the performance of MRE., (© 2023. The Author(s).)

Magnetorheological elastomer (MRE) materials have the potential to be used in a wide range of applications that require long-term service in hostile environments. These widespread applications will result in the emergence of MRE-specific durability issues, where durability refers to performance under in-service environmental conditions. In response, the outdoor tropical climatic environment, combined with the effects of weathering, will be the primary focus of this paper, specifically the photodegradation of the MRE. In this study, MRE made of silicone rubber (SR) and 70 wt% micron-sized carbonyl iron particles (CIP) were prepared and subjected to mechanical and rheological testing to evaluate the effects under natural weathering. Magnetorheological elastomer samples were exposed to the natural weathering conditions of a tropical climate in Kuala Lumpur, Malaysia, for 30 days. To obtain a comprehensive view of MRE degradation during natural weathering, mechanical testing, rheology, and morphological evaluation were all performed. The mechanical and rheological properties test results revealed that after 30 days of exposure and known meteorological parameters, Young's modulus and storage modulus increased, while elongation at break decreased. The degradation processes of MRE during weathering, which are responsible for their undesirable change, were given special attention. With the help of morphological evidence, the relationship between these phenomena and the viscoelastic properties of MRE was comprehensively defined and discussed.

In this study, magnetorheological elastomer (MRE) was fabricated using an electromagnetic device with a new configuration mold at the orientation of 0°, 45° and 90°. This new curing concept enhanced the alignment of carbonyl iron particles (CIPs) within the silicone matrix in the presence of silicone oil (SO) during solidifying, by eliminating air gaps to prevent magnetic flux losses. Using a mold made of steel, which is a magnetic material, the mold functions as a guide for concentrated magnetic flux of 0.315 T to pass through the MRE sample. Scanning electron microscopy (SEM) was used to observe the surface morphology of the fabricated MRE samples particularly the alignment of the CIPs. The field-dependent dynamic properties of the MREs were measured using a rheometer. The analysis implied that the effectiveness of the MRE operating under shear deformation with this curing concept provided the highest magneto-induced modulus of 1.01 MPa when a 45° orientation mold is used, with relative magnetorheological (MR) effect value up to 918%, followed by 0° mold orientation with 0.79 MPa magneto-induced modulus and 646% relative MR effect. The high modulus properties offered by this MRE are believed to be potentially useful in industrial applications where a high range of stiffness is required particularly in the shear direction.

Chemically crosslinked hydrogel magnetorheological (MR) plastomer (MRP) embedded with carbonyl iron particles (CIPs) exhibits excellent magnetic performance (MR effect) in the presence of external stimuli especially magnetic field. However, oxidation and desiccation in hydrogel MRP due to a large amount of water content as a dispersing phase would limit its usage for long-term applications, especially in industrial engineering. In this study, different solvents such as dimethyl sulfoxide (DMSO) are also used to prepare polyvinyl alcohol (PVA) hydrogel MRP. Thus, to understand the dynamic viscoelastic properties of hydrogel MRP, three different samples with different solvents: water, DMSO, and their binary mixtures (DMSO/water) were prepared and systematically carried out using the oscillatory shear. The outcomes demonstrate that the PVA hydrogel MRP prepared from precursor gel with water shows the highest MR effect of 15,544% among the PVA hydrogel MRPs. However, the samples exhibit less stability and tend to oxidise after a month. Meanwhile, the samples with binary mixtures (DMSO/water) show an acceptable MR effect of 11,024% with good stability and no CIPs oxidation. Otherwise, the sample with DMSO has the lowest MR effect of 7049% and less stable compared to the binary solvent samples. This confirms that the utilisation of DMSO as a new solvent affects the rheological properties and stability of the samples.