Codoping of gallium nitride for improved acceptor ionization has long been theorized; however, reduction to practice proves difficult via growth. Herein, implementation of codoping via ion implantation and symmetric multicycle rapid thermal annealing utilizing magnesium codoped with silicon or oxygen is demonstrated. Results show enhanced photoluminescence with both donor species but with an order of magnitude greater increase with concurrent p‐type hall for codoping with oxygen. Furthermore, the addition of nitrogen to balance stoichiometry suppresses defect photoluminescence signals. The incorporation of the donor and nitrogen demonstrates defect reduction beyond magnesium, only implants despite the additional implant dose and resultant damage with coimplantation. The enhanced hole concentrations evident with oxygen incorporation reveal important considerations for device design given unintentional doping during growth and future incorporation of ion implantation capabilities. [ABSTRACT FROM AUTHOR]

We report selective area n-type doping using ion implantation of Si into semi-insulating, C-doped GaN samples activated using both conventional rapid thermal annealing (RTA) and 30 atm N2 overpressure annealing. Implanted regions were tested for Si activation using Circular Transmission Line Measurements (CTLM), while linear and circular photoconductive switches (PCSS) in the unimplanted regions were used as a test vehicle to separate implanted Si dopant activation from leakage paths generated by N vacancy formation due to damage and decomposition during annealing. We observed that at an optimal temperature around 1060 °C, a low contact resistivity of $1\times 10^{-6}\,\,\Omega $ -cm2 was obtained while preserving the breakdown of the unimplanted regions. [ABSTRACT FROM AUTHOR]