Search

The sulfur curing system, peroxide curing system and their combinations were applied for the cross-linking of unfilled and carbon black-filled rubber formulations based on ethylene-propylenediene-monomer rubber. The results demonstrated that the type of curing system influenced the course and shape of curing isotherms. This resulted in the change of curing kinetics of rubber compounds. The cross-link density of materials cured with combined vulcanization systems was lower than that for vulcanizates cured with the peroxide or sulfur system. Good correlation between the cross-link density as well as the structure of the formed cross-links and physical–mechanical characteristics of the cured materials was established. Both filled and unfilled vulcanizates cured with combined vulcanization systems exhibited a higher tensile strength and elongation at break when compared to their equivalents vulcanized in the presence of the peroxide or sulfur curing system. It can be stated that by proper combination of vulcanization systems, it is possible to modify the tensile behavior of vulcanizates in a targeted manner. On the other side, dynamical–mechanical properties were found not be significantly influenced by the curing system composition. [ABSTRACT FROM AUTHOR]

Calcium lignosulfonate in the amount 30 phr was incorporated into rubber compounds based on pure NBR and an NBR carbon black batch, in which the content of carbon black was 25 phr. Glycerine, as a cheap and environmentally friendly plasticizer, was applied into both types of rubber formulations in a concentration scale ranging from 5 to 20 phr. For the cross-linking of rubber compounds, a sulfur-based curing system was used. The work was aimed at the investigation of glycerine content on the curing process and rheological properties of rubber compounds, cross-link density, morphology and physical–mechanical properties of vulcanizates. The results show that glycerine influences the shapes of curing isotherms and results in a significant decrease between the maximum and minimum torque. This points to the strong plasticizing effect of glycerine on rubber compounds, which was also confirmed from rheological measurements. The application of glycerine resulted in better homogeneity of the rubber compounds and in the better dispersion and distribution of lignosulfonate within the rubber matrix, which was subsequently reflected in the significant improvement of tensile characteristics of vulcanizates. A higher cross-link density as well as better physical–mechanical properties were exhibited by the vulcanizates based on the carbon black batch due to the presence of a reinforcing filler. [ABSTRACT FROM AUTHOR]

In this work, dicumyl peroxide (DCP), di-tert-butyl peroxide (DTBP), di(tert-butylperoxyisopropyl)benzene (DTBPIB), and 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane (DDTBPH) were used for cross-linking of rubber matrix based on Ethylene-propylene-diene monomer rubber (EPDM). The aim was to investigate the influence of curing temperature and the type and content of peroxide on curing process of rubber compounds, cross-link density, and physical-mechanical properties of vulcanizates. The results revealed that higher curing temperatures promote faster decomposition of organic peroxides, leading to the faster reactions of peroxide radicals with rubber chains. The increase in temperature resulted also in the increase of cross-linking degree. Although, side reactions as chain scission take over the main cross-linking reactions at very high temperatures resulting in the decrease of cross-link density. The increasing content of peroxides resulted in the acceleration of curing reactions and to increase of cross-link density. The fastest curing kinetics exhibited rubber compounds cured with DCP. However, vulcanizates cured with DCP were found to have the lowest cross-link density. In generally, the dependences of modulus, hardness, and elongation at break of vulcanizates were in line with the dependences of the cross-link densities, while higher tensile strength were found to have vulcanizates cured at higher temperatures and lower peroxides content. [ABSTRACT FROM AUTHOR]

Calcium lignosulfonate in different loadings was applied to the rubber matrix based on EPDM. A sulfur curing system, organic peroxide, and a combination of organic peroxide with two coagent types were used for cross-linking of rubber compounds. The work was focused on the investigation of filler content and curing system composition in the curing process, cross-link density, morphology, and physical–mechanical properties of composites. The achieved results demonstrated that the curing parameters of rubber compounds cured with the sulfur system were significantly different from those cured with peroxide systems. There was also an observed different influence of curing systems composition on cross link density, though in all cases, the degree of cross-linking showed a decreasing trend with increasing content of lignosulfonate. The tensile strength of the composites cured with sulfur system and organic peroxide was comparable, regardless of lignosulfonate loading. This points to the application of both curing systems in cross-linking of rubber compounds with biopolymer filler. However, the introduction of coagents in peroxide vulcanization led to the improvement of adhesion and compatibility between the rubber and the filler on the filler–rubber interface. This subsequently resulted in the improvement of the tensile characteristics of composites. The introduction of organic peroxide in combination with coagent seems to be a very simple and efficient way for the preparation of biopolymer-filled composites with applicable physical–mechanical properties. [ABSTRACT FROM AUTHOR]

In the present work, barium ferrite in constant loading was dosed to the rubber matrices based on NR, SBR and NBR. Sulfur, peroxide and mixed sulfur and peroxide curing systems were applied for cross-linking of rubber magnetic composites. The application of sulfur or peroxide curing system leads to the formation of different types of linkages between rubber chain segments. As the structure of the formed cross-links plays a significant role in determining the final properties of rubber articles, the main aim of the work was to use the combination of curing systems in order to suppress the disadvantages of both systems and possibly to highlight their benefits. The results showed that composition of curing system has considerable influence on cross-link density of composites, which was subsequently reflected in typical change of physical-mechanical properties and glass transition temperature. The tensile strength was improved with increasing amount of peroxide curing system. The reason can be attributed to the presence of co-agent zinc methacrylate, which exhibits strong adhesion to magnetic filler and thus it contributes to the improvement of compatibility and homogeneity on the interphase filler–rubber. On the hand, there was observed no influence of curing system composition or type of rubber matrix on magnetic characteristics of composites. [ABSTRACT FROM AUTHOR]

Strontium ferrite in constant loading is incorporated into acrylonitrile butadiene rubber in order to prepare rubber magnetic composites. Sulfur, peroxide and combined sulfur/peroxide curing systems are applied for cross‐linking of rubber composites. The work is focused on the investigation of curing system composition and thermo‐oxidative ageing on cross‐link density, physical‐mechanical and magnetic properties of rubber magnets. The results revealed that the cross‐link density and the structure of the formed cross‐links within the rubber matrices affect the property spectrum of vulcanizates. [ABSTRACT FROM AUTHOR]

Rubber magnetic composites were prepared by incorporation of barium ferrite in constant amount—50 phr into acrylonitrile-butadiene rubber. Dicumyl peroxide as the curing agent was used for cross-linking of rubber magnets alone, or in combination with four different types of co-agents. The main aim was to examine the influence of curing system composition on magnetic and physical-mechanical properties of composites. The cross-link density and the structure of the formed cross-links were investigated too. The results demonstrated that the type and amount of the co-agent had significant influence on cross-link density, which was reflected in typical change of physical-mechanical properties. The tensile strength increased with increasing amount of co-agents, which can be attributed to the improvement of adhesion and compatibility on the interphase filler-rubber due to the presence of co-agents. Magnetic characteristics were found not to be influenced by the curing system composition. The application of peroxide curing systems consisting of organic peroxide and co-agents leads to the preparation of rubber magnets with not only good magnetic properties but also with improved physical-mechanical properties, which could broaden the sphere of their application uses. [ABSTRACT FROM AUTHOR]

Rubber magnetic composites were prepared by incorporation of strontium ferrite into natural rubber-based continuous matrix. The prepared rubber compounds have model character and besides the rubber and the filler, they contained only ingredients of peroxide curing system, dicumyl peroxide as curing agent, and ethylene glycol dimethacrylate as co-agent. The work was focused on the evaluation of curing system composition and magnetic filler content on curing process, cross-link density, physical–mechanical and magnetic properties of tested materials. The achieved results revealed that the evaluated properties are dependent on the composition of curing system and on the content of ferrite too. Ferrite incorporated in the rubber matrix imparts magnetic properties to the composites considerably. In addition, the improvement of physical–mechanical properties with doping content of ferrite was observed. [ABSTRACT FROM AUTHOR]

Rubber magnetic composites were prepared by incorporation of strontium ferrites in natural rubber-based elastomer matrix. The work was aimed at the evaluation of magnetic filler influence on physical-mechanical, magnetic and thermal properties of prepared composites. The study was also dedicated to the investigation of microstructure and evaluation of interactions between strontium ferrites and natural rubber. The observed parameters are dependent on the type of ferrite and on the content of applied ferrite, too. Surface modification of ferrite leads to the improvement of interfacial conditions and adhesion between the rubber matrix and the magnetic filler. [ABSTRACT FROM AUTHOR]