A melt-assisted solid flame synthesis approach was applied to synthesize boron nanoparticles in argon gas and air atmospheres. For this purpose, we investigated the characteristics of a thermally induced combustion wave in B 2 O 3 + α Mg mixtures ( α = 1.0–1.5 mol) in argon and air atmospheres. Utilizing stoichiometrically insufficient amounts of magnesium ensured that a large portion of molten B 2 O 3 remained in the sample, which reduced the combustion parameters and favored the formation of boron nanoparticles. Under these conditions the combustion temperature and burning velocity were controlled in the range of 1300–1580 °C and 0.065–0.18 cm/s, respectively, and boron nanoparticles in a ∼20–200 nm size range were obtained. The characteristics of boron nanoparticles (morphology, purity, specific surface area, oxidation activity, etc.) were analyzed and a reaction pathway leading to boron nanoparticles synthesis was proposed. [ABSTRACT FROM AUTHOR]

The synthesis of AlN nanoparticles in non-isothermal high-temperature conditions was developed. The process involved Al 2 O 3 –Mg–NH 4 Cl mixtures preparation and combustion in nitrogen atmosphere. Temperature profiles in the combustion waves were recorded by thermocouples, and the values of combustion temperature and wave velocity were determined from the recorded profiles. The existence of two independed combustion regimes with maximum temperatures of about 850 °C and 1400–1600 °C were revealed based on concentrations of NH 4 Cl. AlN nanocrystals were obtained and investigated by X-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy, and Brunauer–Emmett–Teller surface area. AlN nanocrystals prepared under non-isothermal combustion process were comprised well distributed multi-faceted particles with an average size of 50–200 nm. The chemical reactions in the combustion wave were discussed and a possible thermochemical pathway for the synthesis of AlN nanoparticles was proposed. [ABSTRACT FROM AUTHOR]