Search

Lyocell fabrics are widely applied in textiles, however, its high flammability increases the risk of fire. Therefore, to resolve the issue, a novel biomass-based flame retardant with phosphorus and nitrogen elements was designed and synthesized by the reaction of arginine with phosphoric acid and urea. It was then grafted onto the lyocell fabric by a dip-dry-cure technique to prepare durable flame-retardant lyocell fabric (FR-lyocell). X-ray photoelectron spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FTIR) analysis demonstrated that the flame retardant was successfully introduced into the lyocell sample. Thermogravimetric (TG) and Raman analyses confirmed that the modified lyocell fabric featured excellent thermal stability and significantly increased char residue. Vertical combustion results indicated that FR-lyocell before and after washing formed a complete and dense char layer. Thermogravimetric Fourier-transform infrared (TG-FTIR) analysis suggested that incombustible substances (such as H2O and CO2) were produced and played a significant fire retarding role in the gas phase. The cone calorimeter test corroborated that the peak of heat release rate (PHRR) and total heat release (THR) declined by 89.4% and 56.4%, respectively. These results indicated that the flame retardancy of the lyocell fabric was observably ameliorated.

Nowadays, increasing attention is devoted to the search for polymeric composite materials that are characterized by reduced flammability. In this work, the layer-by-layer (LbL) technique was applied to form multilayered protective coatings for polyamide 6/montmorillonite (PA6/MMT) hybrid nanocomposites. This time, the double layers LbL deposition was used in order to improve the thermal properties or flammability of PA6 materials. Our goal was to check how five, 10, and 15 triple-layer deposition onto the surface of PA6 and PA6/MMT composites influenced these relevant properties. For this reason, disodium H-phosphonate, sodium montmorillonite, and iodo-bis(triphenylphosphino)copper were used for polyelectrolyte solution preparation. It was found that the LbL method could be successfully used to improve the flammability characteristics of polyamide 6-based composites. Nevertheless, the deposition of the copper complex should be combined with other flame retardants&mdash, preferentially containing phosphorus&mdash, which enable synergistic effects to occur. Moreover, microscopic observations confirmed that the surfaces on which the formation of interwoven fibrous crystal structures was observed had a tendency to protect the entire material against the destructive effects of heat, contributing, among other things, to reduce the maximum point of heat release rate (PHRR).

Phosphorus-containing polyol applications in polyurethane synthesis can prevent volatilization of flame retardants and their migration on the surface of a material. In this work, novel cast polyurethanes were prepared by a one-step method with the use of different amounts of phosphorus-containing polyol, 4,4′–diphenylmethane diisocyanate and 1,4-butanediol. The chemical structure, thermal, physicochemical and mechanical properties and flame resistance of the prepared materials were investigated. The results obtained for cast flame-retarded polyurethanes were compared with cast polyurethane synthesized with commonly known polyether polyol. It has been shown that with an increasing amount of phosphorus content to polyurethane’s chemical structure, an increased flame resistance and char yield were found during combustion tests. Phosphorus polyol worked in both the condensed (reduced heat and mass exchange) and gas phase (inhibition of flame propagation during burning). The obtained materials contained phosphorus polyol, indicating higher thermal stability in an oxidative environment than an inert atmosphere.