A type of hexagonal boron nitride-magnesium aluminosilicate composite ceramics was fabricated by hot-pressed sintering under different pressures. The relationships between sintering pressure, microstructure, and mechanical properties were investigated. The results indicate that sintering pressure has a great influence not only on the mechanical properties of composite ceramics, but also on crystallization of magnesium aluminosilicate (MAS) and structural order of hexagonal boron nitride. Under the given sintering pressure of 30 MPa, the fracture toughness of composites was greatly improved 66 % (from 2.49 to 4.12 MPa m, with similar densities). It also exhibits the highest bend strength of 245 ± 23 MPa. The fracture behavior of composites and the mechanism of sintering pressure which affect the crystallization of mullite in MAS were also discussed. [ABSTRACT FROM AUTHOR]

MWCNTs modified Si 2 BC 3 N ceramics were prepared through SPS sintering mechanically alloyed amorphous Si 2 BC 3 N powder and MWCNTs at 1900 °C in N 2 atmosphere. The phase evolutions, microstructures and mechanical properties of the prepared ceramic were characterized by XRD, SEM and TEM (SAED and HRTEM), as well as the properties testing. The results show that the Si 2 BC 3 N ceramics are mainly composed of β-SiC, α-SiC and BN(C) phases. The introduction of MWCNTs can stimulate the formation of β-SiC in comparison with the pure Si 2 BC 3 N ceramics. Meanwhile, the particle sizes of BN(C) and SiC are reduced with the introduction of MWCNTs. Furthermore, the MWCNTs are mainly embedded in the Si 2 BC 3 N matrixes, contributing to enhanced bonding. Judging from the interfacial characteristic, the strengthening and toughening mechanisms of MWCNTs in Si 2 BC 3 N ceramics can be classified as “crack bridging”, “pull-out” and “crack deflection”. Based on these effects, the 1 vol% MWCNTs incorporated Si 2 BC 3 N ceramics have much higher flexural strength and fracture toughness of 462.1 MPa and 5.54 MPa·m 1/2 , respectively. [ABSTRACT FROM AUTHOR]

Si-B-C-N ceramic monoliths with LaB 6 additive were prepared by mechanical alloying followed by spark plasma sintering. The microstructures and mechanical properties were investigated compared to LaB 6 -free Si-B-C-N counterparts. After sintered at 1900 °C/50 MPa, the La/Si-B-C-N monoliths provide well-developed BN(C) flakes (≤100 nm in thickness) and improved fracture toughness, while the BN(C) ones show no lamellar microstructures in Si-B-C-N systems. The solid-solution of La in BN(C) grains promotes ordered arrangement of BN(C) along the (0002) plane causing in situ growth of BN(C) thus leading to an increase in toughness by 40% (from 5.6 to 7.8 MPa m −1/2 ). [ABSTRACT FROM AUTHOR]