Search

Boronizing treatment has been considered as a promising strategy to enhance the surface hardness, self-lubrication and wear resistance of high entropy alloy (HEA), endowing the advancements of HEA in engineering applications. However, the anti-friction, anti-wear and corrosion resistance properties of the boronized HEA in sulfuric acid and seawater environments remain unclear. Here, the self-lubrication and corrosion resistance of the boronized CoCrFeNiMn HEA in these corrosive media were studied to assess the applicable environments. Firstly, a boronized layer with thickness of approximately 25 μm on the CoCrFeNiMn HEA surface was fabricated using the powder-pack boronizing treatment. Tribological assessments demonstrated exceptional self-lubricating properties of boronized HEA in various liquid conditions, with over 30 % reduced friction coefficients and over 80 % decreased wear rates. XPS analysis confirmed the formation of a boron-containing tribofilm, enhancing self-lubrication and reducing friction and wear in liquid environments. However, electrochemical tests indicated that the corrosion resistance of the boronized HEA was significantly affected by the liquid medium. The impedance value (|Z|) of boronized HEA decreased to 4.6 % of that of the original HEA in 3.5 wt% NaCl solution, revealing poor corrosion resistance. Conversely, an enhancement of corrosion resistance was observed in 0.05 M H 2 SO 4 solutions with the increase of the |Z| value by 8 times. Therefore, for applications requiring service safety, boronizing HEAs are more suitable for acidic environments, but not in seawater environments, offering valuable insights for the industrial application of CoCrFeNiMn HEA in reducing friction and wear. • The COF of boronized HEA is over 30 % lower than original HEA in liquid conditions. • The tribofilm (composed of H 3 BO 3 and B 2 O 3) significantly reduce friction and wear. • Boronized HEAs are more suitable for acidic environments, but not in seawater. [ABSTRACT FROM AUTHOR]

The CoCrNi medium-entropy alloy (MEA) exhibits an impressive ductility, but its low hardness (∼352 HV) and poor wear resistance limit its engineering applications. In this study, a significant increase of surface hardness and enhancement of self-lubrication were achieved for the CoCrNi MEA using powder-pack boronizing. Results indicate that dual reaction layers with a total thickness of about 50 μm were formed on the surface. These two strengthened layers are mainly consisted of silicide (Ni 2 Si) and borides (CoB, Cr 5 B 3). The hardness of the affected region reaches to 11–21 GPa dependence on the cross-sectional depth, being about 6 times higher than that of untreated MEA. In the deionized water condition, the friction and wear rate reductions of the boronizing treated specimen reach to about 25% and 63%, respectively. Energy Dispersive Spectrometer (EDS) and X-ray Photoelectron Spectroscopy (XPS) analysis on the wear scars showed that a silicon/boron-containing tribofilm was formed under the water environment, which reduces the friction coefficient and enhances the wear resistance. Our study demonstrates that powder-pack boronizing is a powerful way to enhance surface hardness and self-lubrication properties of CoCrNi MEA. • Double-strengthened layers were observed on the boronized CoCrNi alloy surface. • An obvious improvement of surface hardness was obtained. • The self-lubrication performance of boronized CoCrNi MEAs in the water is excellent. • The self-lubrication enhancement was due to the formation of silicon-boron based tribofilm. [ABSTRACT FROM AUTHOR]

In high-speed and heavy-load mechanical operations, gears are susceptible to pitting, adhesion, and wear, which resulting tooth breakage and wear failure. In this paper, failed gears are subjected to repair experiments through the integration of laser cladding and boriding, and the tribological performances and post-repair vibration characteristics are also systematically investigated. In comparison to the base material, the average hardness of the boride surface exhibited an increase of up to 8.37 times, while the wear resistance increased to 15.60 times. The wear resistance of the repaired gear is 2.62 times that of the normal gear, and its vibration parameters are commensurate with that of the normal gear, which offers empirical substantiation for the enhancement of gear repair and remanufacturing strategies. • The hardness and wear resistance were increased at least 8 times after situ-boriding laser cladding treatment. • After situ-boriding laser cladding, the vibration and impact of the repaired gear were weakened. • Compared with the normal gear, the wear resistance of the repaired gear increased by 2.62 times. [ABSTRACT FROM AUTHOR]