Search

This research aims to develop fiber-reinforced composites (FRC) with enhanced fire resistance, which can be particularly useful for the transport industry (e.g., aviation, automotive, and train production). The fire retardation was achieved through epoxy matrix modification with hexachlorocyclotriphosphazene (HCTP). First, the fire-resistant and mechanical properties of the epoxy matrix filled with different HCTP contents (4.8, 7.2, and 9.5 wt.%) were studied to select the most effective HCTP content for the impregnation of FRC. Then, glass, basalt, and carbon fiber fabrics were impregnated with epoxy filled with 7.2 wt.% of HCTP, and the fire resistance, flexural, and interlaminar fracture properties were studied to select the most effective HCTP-modified type of fiber reinforcement based on the test results. It was concluded that basalt fiber impregnated with epoxy filled with HCTP could be selected as the most effective reinforcement type, allowing excellent mechanical and flame-retardant properties. [ABSTRACT FROM AUTHOR]

Highlights S2‐glass fiber reinforced plastics (S2‐GFRP) and basalt fiber reinforced plastics (BFRP) have emerged as crucial materials due to their exceptional mechanical properties, and milling of composite materials plays an important role in achieving desired properties. However, they have proven challenges due to relative inhomogeneity compared with metals, resulting unpredictability in quality of milling operations. The objective of this work is to investigate the effect of cutting parameters, tool geometry and tool surface materials on the surface quality of composites using burrs as a metric. S2‐GFRP and BFRP composites were produced by the vacuum infusion method. Helical and straight flute end mills were manufactured from high‐speed steel (HSS) and carbide rounds, and half of them were coated with titanium nitride using reactive magnetron sputtering technique. Taguchi L18 orthogonal array is used to determine the effect of tool material, tool angle, coating, cutting direction, spindle speed, and feed rate on the machining quality of S2‐GFRPs and BFRPs with respect to burr formations. Milling experiments were conducted under dry conditions and then the burrs were imaged to calculate the total area and length. Statistical analysis was also performed to optimize the machining parameters and tool type for ensuring the structural integrity and performance of the final composite parts. The results showed that the selection of tool material has the most significant impact on the burr area and length of the machined surface. The novel image analysis allows to analyze the extent of the burr size with a desirable operation speed for industrial applications. Aerospace grade S2‐Glass (S2‐GFRP) and basalt fiber reinforced plastics (BFRP) were manufactured. Carbide and HSS end mills were fabricated and coated with titanium nitride protective layer. FRPs were machined at various process parameters designed by Taguchi method. Distinctive image processing was firstly used to compute milling induced Burr area and length. Statistical analysis was performed to quantify the contribution of parameters and optimize milling. [ABSTRACT FROM AUTHOR]

This paper presents a study regarding the obtaining, characterizing and mechanically testing a new laminar composite material, consisting of epoxy resin reinforced with basalt plain fabric. The composites were obtained by manual lay-up, cross-link stage being developed by pressure molding in a hydraulic press. Rectangular plates were obtained and cut into samples with specific shapes, for the mechanical tests (tensile, three-point bending and compression). After testing, the fracture zone was analyzed using optical microscopy to observe the behavior of the composite following the mechanical stresses applied (fracture mechanism, voids presence and fiber delamination identification). Due to the low costs and non-hazardous nature, basalt fibers can be a serious competitor in the production of laminar composites that could successfully replace ordinary glass fiber composites. The mechanical properties in tensile, three-point bending, and compression of epoxy-resin-impregnated basalt fiber composites are comparable and even exceed those of widely used epoxy-resin-impregnated fiberglass composites. [ABSTRACT FROM AUTHOR]