Search

It is well known that the development of lightweight alloys with improved comprehensive performance and application value are the future development directions for the ultra-high-strength 7xxx series Al-Zn-Mg-Cu alloys used in the aircraft field. As the lightest metal element in nature, lithium (Li) has outstanding advantages in reducing the density and increasing the elastic modulus in aluminum alloys, so Al-Zn-Mg-Cu alloys containing Li have gained widespread attention. Furthermore, since the Al-Zn-Mg-Cu alloy is usually strengthened by aging treatment, it is crucial to understand how Li addition affects its aging precipitation process. As such, in this article, the effects and mechanism of Li on the aging precipitation behavior and the impact of Li content on the aging precipitation phase of Al-Zn-Mg-Cu alloys are briefly reviewed, and the influence of Li on the service properties, including mechanical properties, wear resistance, and fatigue resistance, of Al-Zn-Mg-Cu alloys are explained. In addition, the corresponding development prospects and challenges of the Al-Zn-Mg-Cu-Li alloy are also proposed. This review is helpful to further understand the role of Li in Al-Zn-Mg-Cu alloys and provides a reference for the development of high-strength aluminum alloys containing Li with good comprehensive properties. [ABSTRACT FROM AUTHOR]

Adding alloying elements to increase precipitation is a common method to strengthen aluminum (Al) alloys, but an excessively high alloying element content causes segregation and a reduction in plasticity. In this work, the tradeoff between alloying element content and segregation was explored along with the simultaneous increase in precipitation and dislocation density under the action of trace TiB 2 +TiC particles with the aim of giving a full play to the strengthening effect of dislocation and precipitation and maximizing the strength and toughness of the alloy. The cast Al–Zn–Mg–Cu alloys contained various alloying elements (Zn, Mg), and the alloys were reinforced with 0.5 wt% TiB 2 +TiC particles via in-situ reaction in the Al melt. The TiB 2 +TiC particles blocked the diffusion of the alloying elements and inhibited segregation, promoting solution of alloying elements and yielding dispersed and finer precipitates after solution and aging. Meanwhile, owing to the difference in the thermal expansion coefficients of the matrix and particles, the dislocation density of the alloy doubled. Therefore, the yield strength, elongation, and the product of the tensile strength and elongation of the Al-6.60Zn-3.15Mg-1.60Cu alloy with particles reinforcement were 562 MPa, 4.5%, and 3163 MPa·%, respectively, representing increases of 31.6%, 108.9%, and 186.0%, respectively, compared with the cast 7075 alloy. This study is significant for the successful preparation of high-strength and high-toughness cast aluminum alloys with high alloying-element content. [ABSTRACT FROM AUTHOR]

It is challenging to concurrently control the microstructure evolutions after undergoing casting, sheet forming and welding. This study successfully addressed this challenge via trace TiC–TiB 2 nanoparticles in the amelioration of solidification-rolling-welding microstructural evolution. Nanoparticles refined the solidified microstructures and significantly increased the net driving force for recrystallization, promoting the precipitation of nanoscale Guinier–Preston zones and β'' phases. The coarsening of the fusion and heat-affected zones was also effectively suppressed. The yield strength (YS) and ultimate tensile strength (UTS) of the rolled plates were enhanced by 31.3% and 16.3%, respectively, without significantly sacrificing ductility. Additionally, the YS and UTS of the as-welded welding joints were enhanced by 30.2% and 7.8%, respectively. The amelioration mechanism of TiC–TiB 2 throughout the microstructural evolution and strengthening process was systematically investigated. This study provides a typical model for the complete amelioration of microstructural evolution in aluminum alloys under multiple processing conditions. • The nucleation of solidified phases is promoted, and their growth is hindered. • Recrystallization and formation of coherent nanoscale precipitates are promoted. • Coarsening of fusion zone and heat affected zone is suppressed. • Building better microstructure configuration for improved properties. [ABSTRACT FROM AUTHOR]