Search

The characterization of acid sites on solid catalysts is a key to understanding reaction mechanisms at the molecular level. This is generally done indirectly using a model probe molecule able to coordinate or be protonated on surface acid sites. For instance, Temperature Programmed Desorption (TPD) of the pyridine probe molecule followed by IR spectroscopy has become a standard method for the quantification and identification of Brønsted and Lewis acid sites found in zeolites. On the other hand, there is a lack of molecules able to be protonated on very weak Brønsted acid sites. In this work 2,6-ditert- butylpyridine is shown to be a suitable probe for characterizing weak Brønsted acidity. The proof of concept is performed on a series of Pt catalysts supported on a chlorinated alumina support (Pt--γ-Al2O3--Cl) generally used in the reforming process. In particular, we show that the area of the 1617 cm-1 vibration band is correlated to the concentration of Cl introduced into the catalyst. We also underline the relative insensitivity of pyridine as an IR probe molecule and the inadequacy of NH3 TPD for the characterization of acid sites of reforming catalysts, making 2,6-di-tert-butylpyridine a particularly important and specific probe molecule. [ABSTRACT FROM AUTHOR]

Highly crystalline hollow Y zeolite has been obtained by post-synthesis modification of conventional NaY crystals. The top-down transformation involves substantial dealumination of the zeolite framework by silicon tetrachloride followed by acid leaching and finally selective dissolution of the crystal core in the presence of protective aluminium species. The formation of internal cavities depends on the extent of dealumination of the zeolite as well as on the efficiency to remove extraframework Al species prior to realumination. Hollow Y zeolite crystals possess more or less regular internal cavities of ca. 0.8 μm diameter with external size and shape similar to those of the original NaY crystals. They differ from those recently reported in the literature by much higher Si/Al ratios, higher crystallinities and pure microporous shells of ca. 0.12 μm thickness. As a result of these differences, the family of hollow faujasites is significantly enlarged towards more siliceous and less defective materials. Their formation is most likely based on the presence of an Al-rich surface generated by NaAlO2 species during the last stage of the process, which protects the outer parts of the crystals from desilication. [ABSTRACT FROM AUTHOR]

This review article presents the fundamental and practical aspects of water adsorption in Metal-Organic Frameworks (MOFs). The state of the art of MOF stability in water, a crucial issue to many applications in which MOFs are promising candidates, is discussed here. Stability in both gaseous (such as humid gases) and aqueous media is considered. By considering a non-exhaustive yet representative set of MOFs, the different mechanisms of water adsorption in this class of materials are presented: reversible and continuous pore filling, irreversible and discontinuous pore filling through capillary condensation, and irreversibility arising from the flexibility and possible structural modifications of the host material. Water adsorption properties of more than 60 MOF samples are reported. The applications of MOFs as materials for heat-pumps and adsorbent-based chillers and proton conductors are also reviewed. Some directions for future work are suggested as concluding remarks. [ABSTRACT FROM AUTHOR]

Experiment and molecular simulation are used to investigate adsorption in heterogeneous porous media consisting of hierarchical solids (combining different porosity scales) or composite solids (such as silver nanoparticles adsorbed at the external surface of zeolite). It is shown that adsorption in such heterogeneous materials can be written as a linear combination of the adsorption isotherms in its different domains (i.e. porosity scales for the hierarchical sample and constituents for the composite sample). In the case of the composite material, we also show that the linear combination can be used with weighing parameters obtained for a different adsorbate. Such a superimposition principle , which is validated using well-characterized experimental samples, is of interest for characterization purpose as well as industrial applications as they can be used to determine accurately the amount of phases in a given sample (volume corresponding to a given porosity scale or constituent). In contrast, significant departure between the experimental adsorption isotherm and the linear combination can be used to detect coupling effects between the different domains or restrained access to a given domain type. Such a characterization strategy of complex heterogeneous media is complementary to other experiments, such as those probing capillary hysteresis shapes, scanning curves and subloops, which allow determining the distribution of domains within the framework of the independent domain theory. [ABSTRACT FROM AUTHOR]

Selective Xe adsorption on regenerable porous materials such as activated carbons, MOFs and zeolites has been found to be promising and economically attractive. The beneficial effect of silver doping of zeolites on Xe adsorption and Xe/Kr separation has been studied for numerous zeolites such as Ag-ZSM-5, Ag-mordenite and Ag-chabazite. Among them, we had shown that Ag-exchanged ZSM-5 is the most effective material for atmospheric Xe capture and selective separation at very low pressure (ppm level). A linear tendency was observed with a ratio of 2 mol of Ag for 1 mol of strong adsorption sites. Based on this observed tendency, we hypothesize that increasing the number of exchangeable sites by lowering the Si/Al ratio could be an approach to improve silver loading and selective xenon adsorption. The aim of this study is to evaluate the impact of desilication of ZSM-5 zeolites on decreasing their Si/Al ratio and increasing the concentration of sodium-exchanged sites and, possibly, strong silver-based adsorption sites. We have shown here that light desilication of this parent ZSM-5 makes it possible to significantly increase xenon uptake at very low pressure. The desilication creates a larger concentration of Al in the zeolite and thus enables a larger concentration of silver to be loaded. Yet we found that for severe desilication, decreased xenon uptake is observed, likely due to the facilitated formation of silver particles in which the core atoms are not accessible for xenon uptake. It appears that a concentration of 0.5 mmol g−1 of strong adsorption sites is a maximum achievable value for the Ag-ZSM-5 system. Surprisingly, we found that the parent ZSM-5 zeolite prepared by organic templating yields Ag-ZSM-5 with a similar concentration of strong adsorption sites but at higher silver loading. We could hypothesize that silanol defects present in commercial zeolites may be responsible for the stabilization of silver clusters. [Display omitted] • Higher xenon adsorption capacity for xenon atmospheric capture (ppm level). • Light desilication of ZSM-5 increases the concentration of adsorption sites. • Silanol defects present in commercial zeolites may stabilize silver clusters. • Severe desilication decreases Xe uptake due to the formation of larger silver NPs. [ABSTRACT FROM AUTHOR]