Search

To optimize the insulation design of high-temperature superconductivity (HTS) cable, the multilayer wrapping cable insulation properties in the liquid nitrogen should be studied. In this paper, we investigated the breakdown properties of multilayer wrapping of cable insulation in liquid nitrogen. AC and dc breakdown tests of a minimodel cable with an insulation floor composed of polypropylene laminate paper (PPLP), PPLP/100HN (DuPont polyimide film), PPLP/100CR (DuPont polyimide film), and PPLP/150FCR019 (DuPont polyimide film) and of singer-layer sheets, including PPLP, 100HN, 100CR, and 150FCR019, respectively, were performed in liquid nitrogen. The breakdown characteristics of the sheets and model cable insulation consisting of PPLP and composite insulation schemes according to the arrangement of PPLP/HN, PPLP/100CR, and PPLP/150FCR019 were compared. For the sheets, the ac breakdown strength of 100HN is greater than that of 100CR; this may be because there are large amounts of organic-inorganic interface in 100CR. The dc breakdown strength of 100CR is greater than that of 100HN, which may be because the space charge of 100CR homogenizes the electric field. For the minimodel cable insulation, the dc and ac breakdown strengths of the composite insulation in which the third layer of wrapping tape insulation material was composed of three layers of 100HN, which is overlapped completely, are greater than those of the insulation consisting of PPLP and other composite insulations. [ABSTRACT FROM PUBLISHER]

Flexible supercapacitor with all components monolithically integrated into an on-chip paper substrate demonstrates excellent electrochemical and mechanical performance. Supercapacitors are drawn with a conductive ink of nitrogen-doped carbon nanotube and graphene ink, which has been prepared without assistance of surfactant. The engineering strategy is intrinsically scalable toward flexible paper devices. [Display omitted] • A surfactant-free ink of nitrogen-doped carbon nanotubes and graphene is prepared. • The electrodes are integrated onto a paper in mirror image. • The resultant supercapacitor presents a high volumetric capacitance of 0.45 F cm−3. • The strategy is intrinsically scalable toward flexible supercapacitors. We demonstrate a facile strategy to fabricate flexible paper-based supercapacitors, in which all the components are integrated onto a paper with poly (vinyl alcohol)/H 3 PO 4 as the gel electrolyte. The electrodes are drawn on both sides of the paper in a mirror image with a surfactant-free ink of nitrogen-doped carbon nanotubes and graphene. The resultant supercapacitors present a high volumetric capacitance of 0.45 F cm−3 and an energy density of 40.0 μWh cm−3. Moreover, this strategy is intrinsically scalable toward flexible energy devices while maintaining their electrochemical and mechanical performance. [ABSTRACT FROM AUTHOR]

In this work, we report a rational design and facile synthetic process for the construction of a 3-dimensional N, S co-doped reduced holey graphene oxide/carbonized cellulose paper as interlayer in Li–S batteries. The interlayer has a labyrinth-like structure with plenty of nanosized holes to achieve the permselectivity for Li ions and effective intercept for polysulfides. The coin cell with the interlayer shows a high initial discharge capacity of 1263.5 mAh/g at 0.2 C, a low capacity fading rate of 0.0487% per cycle for 300 cycles at 1 C, and an excellent rate performance of 864.6 mAh/g at 2 C. Moreover, this cell also has excellent anti-self-discharge property and a high areal capacity of 6.1 mA h/cm2 at a sulfur loading of 8.1 mg/cm2 using aluminum foil as the current collector. Thus, this work suggests the permselective and multifunctional interlayer as a practical and effective strategy for the application in the high-performance Li–S battery. The labyrinth-like N and S co-doped reduced holey graphene oxide/carbonized cellulose paper, as the interlayer of lithium-sulfur batteries, achieved the excellent permselectivity toward Li ions and effective intercept toward polysulfides and exhibited significant cycle stability, anti-self-discharge property and a high areal capacity. Image 1 • A labyrinth-like NS-RHGO-CCP was constructed as interlayer for Li–S batteries. • The NS-RHGO-CCP possessed high permselectivity of Li+ to raise rate capability. • The NS-RHGO-CCP achieved interception of polysulfides to enhance cycle stability. • The NS-RHGO-CCP improved conductivity of S and Li 2 S to give a high areal capacity. [ABSTRACT FROM AUTHOR]

Corrections to “The Dielectric Strength of Nomex 410 Paper in Liquid Nitrogen under Boiling Situations” [ABSTRACT FROM AUTHOR]