Search

Ruthenium nanoparticles (NPs) supported over carbon thin films (Ru/C thin films) catalysts were synthesized by pulsed laser deposition and used as catalysts for hydrolysis of ammonia borane (AB). Highly irregular and porous carbon films with high surface area were deposited by varying Ar gas pressures during the deposition. By taking the advantage of phase explosion phenomena, occurring at high laser fluence, the surface of the carbon films were decorated with crystalline Ru NPs with size below ∼10 nm. Ru/C thin film catalyst produced H 2 with 6 times higher H 2 generation rate as compared to unsupported Ru NPs assembled film, and with a high turnover frequency value of 70.5 mol H 2 mol −1 Ru min −1 . A combination of morphological features and high content of sp 2 bonded C atoms provides good dispersion of Ru NPs over a large surface area. Both these features contribute in generating large number of active sites leading to the increase in catalytic efficiency. A possibility of using the present form of catalyst as an ON/OFF switch for H 2 production was also tested. Although the catalytic activity decreased with the number of hydrolysis cycles, Ru/C thin film catalyst was able to generate the expected amount of H 2 gas in each cycle when it was reused several times. The observed low activation energy (∼28 kJ mol −1 ) and high H 2 generation rate (15.5 L H 2 min −1 g −1 of Ru) by hydrolysis of AB suggest that Ru/C thin film catalyst is highly efficient. [ABSTRACT FROM AUTHOR]

Nanoparticles assembled Co-B-O thin film catalysts were synthesized by pulsed laser deposition (PLD) technique for hydrolysis of Sodium Borohydride (SBH). Surface morphology of the deposited films was investigated using SEM and TEM, while compositional analysis was studied using XPS. Structural properties of Co-B-O films were examined using XRD and HRTEM. Laser process is able to produce well separated and immobilized Co-B-O NPs on the film surface which act as active centers leading to superior catalytic activity producing hydrogen at a significantly higher rate as compared to bulk powder. Co-B-O thin film catalyst produces hydrogen at a maximum rate of ∼4400 ml min −1 g −1 of catalyst, which is four times higher than powder catalyst. PLD parameters such as laser fluence and substrate-target distance were varied during deposition in order to understand the role of size and density of the immobilized Co-B-O NPs in the catalytic process. Films deposited at 3–5 cm substrate-target distance showed better performance than that deposited at 6 cm, mainly on account of the higher density of active Co-B-O NPs on the films surface. Features such as high particle density, polycrystalline nature of Co NPs and good stability against agglomeration mainly contribute towards the superior catalytic activity of Co-B-O films deposited by PLD. [ABSTRACT FROM AUTHOR]

Nanocatalysts, in the form of nanoparticles assembled coatings (NPACs) of Co 3 O 4 , were synthesized by pulsed laser deposition (PLD) with optimized parameters. Phase explosion phenomena occurring at high laser fluences produce nanoparticles (NPs) with an average size of ∼5 nm having narrow size distribution (3–10 nm) and low degree of agglomeration, which are randomly arranged in the form of coating on the substrate surface. In comparison with chemically synthesized Co 3 O 4 crystalline powder, the NPACs deposited by PLD showed significantly higher catalytic activity for H 2 generation by hydrolysis of NaBH 4 . Maximum H 2 generation rate obtained by NPACs (5010 ml min −1 g cat −1 ) is about 5 times higher than that produced by Co 3 O 4 powder (1000 ml min −1 g cat −1 ), which is mainly attributed to high surface area and large number of active sites provided by the Co 3 O 4 NPs in the coating owing to their size and shape. By varying the O 2 pressure during PLD, two different cobalt oxide phases, namely Co 3 O 4 and CoO, were formed in NPACs and found that Co 3 O 4 phase is more active for hydrolysis than CoO phase with lower oxidation number. The morphology and crystallinity of Co 3 O 4 NPACs were tuned by varying the laser fluence and substrate temperature respectively, and their effect on H 2 generation rate was studied. The results showed that the NPs with mixed amorphous-nanocrystalline phase on the surface act as active sites for favorable interaction and NaBH 4 conversion. [ABSTRACT FROM AUTHOR]