Search

As gallium oxide-based heterojunction devices gain prominence, low-resistance contacts to aluminum gallium oxide material are of increasing importance for high performance and access to modulation doped layers. Here, the activation of ion-implanted silicon donors is investigated as a function of donor density from 5 × 1018 cm−3 to 1 × 1020 cm−3, activation anneal duration from 6 s to 600 s, and activation temperature from 900°C to 1140°C. Importantly, ohmic behavior was achievable across a reasonably wide process window at moderate to high doping concentrations. Specific contact resistance of 1 × 10−3 Ω cm2 and sheet resistance of 2.8 kΩ/□ were achieved for a 60 nm-deep 1 × 1020 cm−3 box implant after activation at 1000°C for 6 s with standard Ti/Au contacts. Under these conditions, an activation efficiency of 7% was observed with Hall mobility of ~32 cm2/Vs. Furthermore, we demonstrate a Schottky diode formed of implanted material with a rectification ratio > 106 and further confirm the Hall carrier density results using capacitance–voltage profiling analysis. Finally, we show the significant impact of anneal duration and the potential for deleterious over-annealing which reduces the active carrier density, mobility, and resultant material conductivity. [ABSTRACT FROM AUTHOR]

Selective area doping via ion implantation is crucial to the implementation of most modern devices and the provision of reasonable device design latitude for optimization. Herein, we report highly effective silicon ion implant activation in GaN via Symmetrical Multicycle Rapid Thermal Annealing (SMRTA) at peak temperatures of 1450 to 1530 °C, producing a mobility of up to 137 cm2/Vs at 300K with a 57% activation efficiency for a 300 nm thick 1 × 1019 cm−3 box implant profile. Doping activation efficiency and mobility improved alongside peak annealing temperature, while the deleterious degradation of the as-grown material electrical properties was only evident at the highest temperatures. This demonstrates efficient dopant activation while simultaneously maintaining low levels of unintentional doping and thus a high blocking voltage potential of the drift layers for high-voltage, high-power devices. Furthermore, efficient activation with high mobility has been achieved with GaN on sapphire, which is known for having relatively high defect densities but also for offering significant commercial potential due to the availability of cheap, large-area, and robust substrates for devices. [ABSTRACT FROM AUTHOR]

We report selective area n-type doping using ion implantation of Si into semi-insulating, C-doped GaN samples activated using both conventional rapid thermal annealing (RTA) and 30 atm N2 overpressure annealing. Implanted regions were tested for Si activation using Circular Transmission Line Measurements (CTLM), while linear and circular photoconductive switches (PCSS) in the unimplanted regions were used as a test vehicle to separate implanted Si dopant activation from leakage paths generated by N vacancy formation due to damage and decomposition during annealing. We observed that at an optimal temperature around 1060 °C, a low contact resistivity of $1\times 10^{-6}\,\,\Omega $ -cm2 was obtained while preserving the breakdown of the unimplanted regions. [ABSTRACT FROM AUTHOR]

The activation of ion implanted p-type dopants in GaN is notoriously difficult as the extremely high temperatures required to activate implanted Mg also damage the GaN crystal. In this paper, we present refinements to our novel annealing process (symmetric multicycle rapid thermal annealing) to reduce surface damage and contamination responsible for elevated leakage currents and non-ideal diode behavior. Furthermore, we apply the technique to Mg-implanted bulk GaN substrates to enable vertical power device structures, demonstrating rectifying p-i-n junctions. In addition, the technique was applied for edge termination in both p-i-n and Schottky barrier diodes, realizing floating guard ring and junction termination extension structures. The processes demonstrated here represents a key enabling step for future GaN-based power devices. [ABSTRACT FROM AUTHOR]