Search

The sulfur curing system, peroxide curing system and their combinations were applied for the cross-linking of unfilled and carbon black-filled rubber formulations based on ethylene-propylenediene-monomer rubber. The results demonstrated that the type of curing system influenced the course and shape of curing isotherms. This resulted in the change of curing kinetics of rubber compounds. The cross-link density of materials cured with combined vulcanization systems was lower than that for vulcanizates cured with the peroxide or sulfur system. Good correlation between the cross-link density as well as the structure of the formed cross-links and physical–mechanical characteristics of the cured materials was established. Both filled and unfilled vulcanizates cured with combined vulcanization systems exhibited a higher tensile strength and elongation at break when compared to their equivalents vulcanized in the presence of the peroxide or sulfur curing system. It can be stated that by proper combination of vulcanization systems, it is possible to modify the tensile behavior of vulcanizates in a targeted manner. On the other side, dynamical–mechanical properties were found not be significantly influenced by the curing system composition. [ABSTRACT FROM AUTHOR]

Calcium lignosulfonate in the amount 30 phr was incorporated into rubber compounds based on pure NBR and an NBR carbon black batch, in which the content of carbon black was 25 phr. Glycerine, as a cheap and environmentally friendly plasticizer, was applied into both types of rubber formulations in a concentration scale ranging from 5 to 20 phr. For the cross-linking of rubber compounds, a sulfur-based curing system was used. The work was aimed at the investigation of glycerine content on the curing process and rheological properties of rubber compounds, cross-link density, morphology and physical–mechanical properties of vulcanizates. The results show that glycerine influences the shapes of curing isotherms and results in a significant decrease between the maximum and minimum torque. This points to the strong plasticizing effect of glycerine on rubber compounds, which was also confirmed from rheological measurements. The application of glycerine resulted in better homogeneity of the rubber compounds and in the better dispersion and distribution of lignosulfonate within the rubber matrix, which was subsequently reflected in the significant improvement of tensile characteristics of vulcanizates. A higher cross-link density as well as better physical–mechanical properties were exhibited by the vulcanizates based on the carbon black batch due to the presence of a reinforcing filler. [ABSTRACT FROM AUTHOR]

Calcium lignosulfonate in different loadings was applied to the rubber matrix based on EPDM. A sulfur curing system, organic peroxide, and a combination of organic peroxide with two coagent types were used for cross-linking of rubber compounds. The work was focused on the investigation of filler content and curing system composition in the curing process, cross-link density, morphology, and physical–mechanical properties of composites. The achieved results demonstrated that the curing parameters of rubber compounds cured with the sulfur system were significantly different from those cured with peroxide systems. There was also an observed different influence of curing systems composition on cross link density, though in all cases, the degree of cross-linking showed a decreasing trend with increasing content of lignosulfonate. The tensile strength of the composites cured with sulfur system and organic peroxide was comparable, regardless of lignosulfonate loading. This points to the application of both curing systems in cross-linking of rubber compounds with biopolymer filler. However, the introduction of coagents in peroxide vulcanization led to the improvement of adhesion and compatibility between the rubber and the filler on the filler–rubber interface. This subsequently resulted in the improvement of the tensile characteristics of composites. The introduction of organic peroxide in combination with coagent seems to be a very simple and efficient way for the preparation of biopolymer-filled composites with applicable physical–mechanical properties. [ABSTRACT FROM AUTHOR]

Rubber magnetic composites were prepared by incorporation of barium ferrite in constant amount—50 phr into acrylonitrile-butadiene rubber. Dicumyl peroxide as the curing agent was used for cross-linking of rubber magnets alone, or in combination with four different types of co-agents. The main aim was to examine the influence of curing system composition on magnetic and physical-mechanical properties of composites. The cross-link density and the structure of the formed cross-links were investigated too. The results demonstrated that the type and amount of the co-agent had significant influence on cross-link density, which was reflected in typical change of physical-mechanical properties. The tensile strength increased with increasing amount of co-agents, which can be attributed to the improvement of adhesion and compatibility on the interphase filler-rubber due to the presence of co-agents. Magnetic characteristics were found not to be influenced by the curing system composition. The application of peroxide curing systems consisting of organic peroxide and co-agents leads to the preparation of rubber magnets with not only good magnetic properties but also with improved physical-mechanical properties, which could broaden the sphere of their application uses. [ABSTRACT FROM AUTHOR]