Search

This study aims at the characterisation of red and orange glass tesserae from the 4th-century Roman villa of Noheda (Spain). Due to the limited number of analyses available for such ancient materials, many questions remain unanswered about the production processes in the Roman period. Six samples were chosen for their hue variations, including two samples showing banded patterns of red and orange. Differences in copper speciation were investigated by X-ray absorption spectroscopy and compared with colour and compositional variations obtained by EPMA. The shapes and sizes of colouring crystals could be investigated using scanning and transmission electron microscope imaging. The brown-red colour is due to metallic copper nano-particles and corresponds to a low-copper and low-lead group usually described in the literature. The orange samples and bands are coloured by copper oxide C u 2 O nanoparticles with remaining Cu+ in the glass and have greater contents of Cu. Compositional analyses reveal that the same base glass is used in the red and orange bands with additions of Cu, Sn, Pb and probable Fe. Furthermore, based on our results and on the literature review, a high-copper low-lead group of glasses highlights the variability of compositions observed in cuprite colours. [ABSTRACT FROM AUTHOR]

Ceria nanoparticles (CeO2 NPs) are generally considered in various functional applications, such as catalysts in fuel cells, sensors, and antioxidant and oxidase-like enzymes in the biological environment. The CeO2 NPs were synthesized using the E. globulus leaf extract-mediated hydrothermal technique. The synthesized NPs were characterized by various analytical instruments including powder X-ray diffractometer (PXRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and dynamic light scattering (DLS) analysis. The XRD results showed an average NPs sizes of 13.7 nm. Cytotoxic study results showed an IC50 value of 45.5 µg/L for A549 and 58.2 µg/L for HCT 116, indicating that CeO2 NPs are more toxic to A549 compared to HCT116 cell lines. The generation of ROS was responsible for its cytotoxic activity against cancer cell lines. Specific surface area (40.96 m2/g) and pore diameter (7.8 nm) were measured using Brunauer-Emmett-Teller (BET) nitrogen adsorption-desorption isotherms. CeO2 NPs with a high surface area were used as photocatalyst in degrading sunset yellow (SY) dye under UV-irradiation and 97.3% of the dye was degraded within 90 min. These results suggest that the synthesized CeO2 NPs could be used as a good photocatalyst as well as a cytotoxic agent against human cancer cell lines. [ABSTRACT FROM AUTHOR]

In Fe-Mn-Al-Ni shape memory alloys, the stabilization of superelasticity would be affected by the undesired precipitation of B2 nano-particles during natural aging. In order to solve this problem, the effect of Mo alloying on the precipitation behavior of B2 nano-particles during the cooling and natural aging processes was performed by scanning electron microscope, transmission electron microscope and Vickers microhardness test in two Fe-Mn-Al-Ni-Mo shape memory alloys. The results showed that the formation of γ phase was completely suppressed after 15 °C and 80 °C water quenching as well as air cooling. However, B2 nano-particles were still precipitated after the three cooling processes, and their sizes and misfits increased with decreasing the cooling rates. In addition, the Vickers hardness increased after natural aging for 338 days, which indicated that it is not viable to inhibit the precipitation of B2 nano-particles during natural aging by Mo alloying in the Fe-Mn-Al-Ni shape memory alloys. [ABSTRACT FROM AUTHOR]

The droplet evaporation effect on the preparation of polyetherimide (PEI) nanoparticles by thermally induced phase separation (TIPS) was studied. PEI nanoparticles were prepared in two routes. In route I, the droplet evaporation process was carried out after TIPS. In route II, the droplet evaporation and TIPS processes were carried out simultaneously. The surface tension and shape parameters of samples were measured via a drop shape analyzer. The Z-average particle diameter of PEI nanoparticles in the PEI/dimethyl sulfoxide solution (DMSO) suspension at different time points was tested by dynamic light scattering, the data from which was used to determine the TIPS time of the PEI/DMSO solution. The natural properties of the products from both routes were studied by optical microscope, scanning electron microscope and transmission electron microscope. The results show that PEI nanoparticles prepared from route II are much smaller and more uniform than that prepared from route I. Circulation flows in the droplet evaporation were indirectly proved to suppress the growth of particles. At 30 °C, PEI solid nanoparticles with 193 nm average particle size, good uniformity, good separation and good roundness were obtained. Route I is less sensitive to temperature than route II. Samples in route I were still the accumulations of micro and nanoparticles until 40 °C instead of 30 °C in route II, although the particle size distribution was not uniform. In addition, a film structure would appear instead of particles when the evaporation temperature exceeds a certain value in both routes. This work will contribute to the preparation of polymer nanoparticles with small and uniform particle size by TIPS process from preformed polymers. [ABSTRACT FROM AUTHOR]

A binary carbonate salt eutectic (Li2CO3-K2CO3)-based nanofluid was in situ synthesized by mixing with a precursor material, aluminum nitrate nonahydrate (Al(NO3)3·9H2O). Thermal decomposition of the precursor was successfully carried out to synthesize alumina (Al2O3) nanoparticles at 1 wt.% concentration. A thermogravimetric analysis (TGA) confirmed a complete thermal decomposition of aluminum nitrate nonahydrate to alumina nanoparticles. A transmission electron microscope (TEM) was employed to confirm the size and shape of the in situ formed nanoparticles; the result showed that they are spherical in shape and the average size was 28.7 nm with a standard deviation of 11.7 nm. Electron dispersive X-ray spectroscopy (EDS) confirmed the observed nanoparticles are alumina nanoparticles. A scanning electron microscope (SEM) was employed to study microstructural changes in the salt. A differential scanning calorimeter (DSC) was employed to study the heat capacity of the in situ synthesized nanofluid. The result showed that the heat capacity was enhanced by 21% at 550 °C in comparison with pure carbonate salt eutectic. About 10–11 °C decrease of the onset melting point of the binary carbonate salt eutectic was observed for the in situ synthesized nanofluids. [ABSTRACT FROM AUTHOR]

This study assessed the antimicrobial efficacy of synthesized zinc oxide nanoparticles produced using aqueous extracts of pomegranate leaves and flowers designated ZnO-NPs-PL, ZnO-NPs-PF. In the study, oxides of zinc were successfully employed to fabricate nanoparticles using extracts from leaves and flowers of pomegranate (Punica granatum). The nanoparticles obtained were characterized spectroscopically. X-ray diffractive analysis (XRD) revealed the elemental components and nature of the synthesized particles. The fabricated zinc oxide nanoparticle (ZnO-NPs) showed a crystalline structure. The morphology of the nanoparticles as shown by scanning electron microscopy (SEM) was unevenly spherical and the functional groups involved in stabilization, reduction and capping were confirmed using Fourier Transform Infra-Red (FT-IR) Spectroscopy. Confirmation of the nanoparticles by UV–Vis analysis showed absorption bands of 284 and 357 nm for pomegranate leaf and flower extract, respectively, mediated ZnO-NPs. Evaluation of the antimicrobial efficacy of the fabricated nanoparticles showed that ZnO-NPs were effective against all selected pathogenic strains, Staphylococcus aureus, Bacillus cereus, Pseudomonas aeruginosa, Klebsiella pneumoniae, Streptococcus pneumoniae, Salmonella diarizonae, Salmonella typhi, Enterococcus faecalis, Enterococcus faecium, Escherichia coli, Moraxella catarrhalis, Aeromonas hydrophila and Listeria monocytogenes, used in the analysis. The effectiveness of these nanoparticles could be linked to their sizes and shapes as obtained using a transmission electron microscope (TEM) and scanning electron microscope (SEM). Our reports revealed that increasing the concentration of the nanoparticles resulted in an increase in the antibacterial activity exerted by the nanoparticles, thus suggesting that both ZnO-NPs can effectively be used as alternative antibacterial agents. Further research is required to assess their mechanisms of action and toxicity. [ABSTRACT FROM AUTHOR]