Dy 3+ and Sm 3+ doped Li 4 CaB 2 O 6 materials were prepared by the solid state reaction. The phase analysis of all phosphors were determined using the X- Ray Powder Diffraction Analysis. The photoluminescence (PL) properties of both phosphors were investigated using spectrofluorometer at room temperature. The first luminescent material, Li 4 CaB 2 O 6 : Dy 3+ emits 489, 577 and 674 nm upon excitation with 345 nm. The second luminescent material, Li 4 CaB 2 O 6 : Sm 3+ , emits (565–570), (602–609), 650 and 712 nm upon excitation with 404 nm. Also, the dependence of the emission intensity on the activator ions (Dy 3+ and Sm 3+ ) concentration for the Li 4 CaB 2 O 6 were studied in detail. It was observed that the concentration quenching of Dy 3+ and Sm 3+ in Li 4 CaB 2 O 6 are 0.05 and 0.06 mol, respectively. [ABSTRACT FROM AUTHOR]

Pure, Pb 2+ and Bi 3+ doped Li 4 SrCa(SiO 4 ) 2 materials were prepared by using a conventional solid state reaction. The phase of Li 4 SrCa(SiO 4 ) 2 was determined using the powder XRD. The photoluminescent properties of Pb 2+ and Bi 3+ doped Li 4 SrCa(SiO 4 ) 2 materials were investigated using a spectrofluorometer at room temperature. The emission bands of Li 4 SrCa(SiO 4 ) 2 : Pb 2+ and Li 4 SrCa(SiO 4 ) 2 : Bi 3+ were observed at 290 and 380 nm, respectively. Li 4 SrCa(SiO 4 ) 2 with different Pb 2+ and Bi 3+ doping concentrations were analyzed at room temperature. The Stokes shifts of Li 4 SrCa(SiO 4 ) 2 : Pb 2+ and Li 4 SrCa(SiO 4 ) 2 : Bi 3+ were calculated to be 5678 and 5942 cm −1 , respectively. [ABSTRACT FROM AUTHOR]

Pure and Pb 2+ doped Ba 2 Be 2 B 2 O 7 materials were prepared by a solution combustion synthesis method. The phase analysis of all synthesized materials was carried out using the powder XRD. The synthesized phosphors were investigated using spectrofluorometer at room temperature. The excitation and emission bands of Ba 2 Be 2 B 2 O 7 :Pb 2+ were observed at 284 and 396 nm, respectively. The dependence of the emission intensity on the Pb 2+ concentration for the Ba 2 Be 2 B 2 O 7 was studied in detail. It was observed that the concentration quenching of Pb 2+ in Ba 2 Be 2 B 2 O 7 is 0.04 mol. The Stokes shifts of Ba 2 Be 2 B 2 O 7 :Pb 2+ phosphor were calculated to be 9959 cm −1 . [ABSTRACT FROM AUTHOR]

Pure and Pb 2+ doped Li 4 CaB 2 O 6 materials were prepared by the solid state reaction. The phase analysis of all synthesized materials were determined using the powder XRD. The synthesized materials were investigated using spectrofluorometer at room temperature. The excitation and emission bands of Li 4 CaB 2 O 6 :Pb 2+ were observed at 263 and 298 nm, respectively. The dependence of the emission intensity on the Pb 2+ concentration for the Li 4 CaB 2 O 6 were studied in detail. It was observed that the concentration quenching of Pb 2+ in Li 4 CaB 2 O 6 is 0.01 mol. The Stokes shifts of Li 4 CaB 2 O 6 :Pb 2+ phosphor was calculated to be 4466 cm −1 . Also, the photoluminescence properties of Pb 2+ in various lithium calcium borates (LCB) with different structure was discussed. [ABSTRACT FROM AUTHOR]