The practical application of sodium-ion hybrid capacitors is limited by their low energy densities resulted from the kinetics mismatch between cathodes and anodes, and the fire safety related to the flammable electrolyte-separator system. Hence, we report a rational design of metal-organic frameworks (MOFs, UiO-66) modified PVDF-HFP separator. High tensile strength and dimensional thermal stability of the separator reduce the risk of electrode short circuit caused by the separator deformation. MCC test demonstrates a reduction of 75% in peak heat release rate (pHRR), indicating an enhanced fire-resistant property of the separator. This is due to the transformation of UiO-66 into ZrO2 accompanied by the consumption of oxygen and the formation of the barrier char that suppresses further heat release. Quasi-solid-state electrolyte prepared based on this separator presents an enhanced ionic conductivity of 2.44 mS*cm-1 and Na-ion transference number of 0.55, which are related to the high porosity ( >70%) and electrolyte uptake (~ 320%) of the separator. Moreover, the open metal sites of UiO-66 can capture PF6- and consequently liberate the Na+ for faster migration, thus reducing the kinetics mismatch between cathodes and anodes. Such multifunctional separator enables the quasi-solid-state Na-ion hybrid capacitor to achieve high energy density (182 Wh*kg-1 @31 W*kg-1) and power density (5280 W*kg-1 @22 Wh*kg-1), as well as excellent cyclic stability (10000 cycles @1000 mA*g-1). Keywords: Quasi-solid-state; PVDF-HFP; Metal-organic frameworks; Dimensional thermal stability; Fire safety; Selective charge transfer

High-performance anodes for rechargeable Li-ion battery are produced by nanostructuring of the transition metal oxides on a conductive support. Here, we demonstrate a hybrid material of MnO2 directly grown onto fabrics of carbon nanotube fibres, which exhibits notable specific capacity over 1100 and 500 mAh/g at a discharge current density of 25 mA/g and 5 A/g, respectively, with coulombic efficiency of 97.5 %. Combined with 97 % capacity retention after 1500 cycles at a current density of 5 A/g, both capacity and stability are significantly above literature data. Detailed investigations involving electrochemical and in situ synchrotron X-ray scattering study reveal that during galvanostatic cycling, MnO2 undergoes an irreversible phase transition to LiMnO2, which stores lithium through an intercalation process, followed by conversion mechanism and pseudocapacitive processes. This mechanism is further confirmed by Raman spectroscopy and X-ray photoelectron spectroscopy. The fraction of pseudocapacitive charge storage ranges from 27% to 83%, for current densities from 25 mA/g to 5 A/g. Firm attachment of the active material to the built-in current collector makes the electrodes flexible and mechanically robust, and ensures that the low charge transfer resistance and the high electrode surface area remain after irreversible phase transition of the active material and extensive cycling., Comment: 28 pages,7 figures