• Introduce the electron transport layer SnO 2 between NiFe LDH and conductive substrate NF was first reported. • SnO 2 nanosheets are interwoven to form a sponge-like 3D structure, which promotes the formation of relatively smaller and thinner NiFe LDH nanosheets, thereby generating more active sites and reducing electron transmission resistance. • It was verified that the electronic structure of Ni and Fe was optimizing via the introduction of SnO 2. • NiFe LDH@SnO 2 /NF possesses a low overpotential of 234 mV at 10 mA cm−2 for OER and 1.396 V at 10 mA cm−2 for methanol oxidation reaction. In an electrocatalyst with a heterointerface structure, the different interfaces can efficiently adjust the catalyst's conductivity and electron arrangement, thereby enhancing the activity of the electrocatalyst. Ultrathin and smaller NiFe LDH was successfully constructed on the surface of SnO 2 nanosheet supported NF by layer by layer assembly, and exhibits lower overpotential of 234 mV at a current density of 10 mA cm−2, which only increases by 6.4% even at a high current density of 100 mA cm−2. The excellent OER activity of catalyst is attributed to the contribution of the semiconductor SnO 2 electron transport layer. Through experiments and characterization, 3d structure SnO 2 nanosheets control the growth of ultra-thin nickel-iron, the hierarchical interface between SnO 2 and NiFe LDH can change the electron arrangement around the iron and nickel active centers at the interface, resulting the valence states of iron slightly increased and Ni3+ content increased. The result will promote the oxidation of water. Meanwhile, the SnO 2 semiconductor as electron transport layer is conducive to trapping electrons generated in oxidation reaction, promoting electrons transferring from the NiFe LDH active center to the Ni substrate more quickly, and enhance the activity of NiFe LDH. It also shows excellent activity in an electrolyte solution containing 0.5 M methanol and 1 M KOH, and only 1.396 V (vs. RHE) is required to drive a current density of 10 mA cm−2. [ABSTRACT FROM AUTHOR]

The interface engineering plays a key role in controlled optoelectronic properties of perovskite photovoltaic devices, and thus the electron transport layer (ETL) material with tailored optoelectronic properties remains a challenge for achieving high photovoltaic performance of planar perovskite solar cells (PSCs). Here, the fine and crystalline zirconium stanate (ZrSnO 4) nanoparticles (NPs) was synthesized at low temperature, and its optoelectronic properties are systematically investigated. Benefiting from the favorable electronic structure of ZrSnO 4 NPs for applications in ETL, efficient electron transport and extraction with suppressed charge recombination are achieved at the interface of perovskite layer. As a result, the optimized ZrSnO 4 NPs synthesized at room-temperature deliver the optimized power conversion efficiency up to 16.76 % with acceptable stability. This work opens up a new class of ternary metal oxide for the use in ETL of the planar PSCs and should pave the way toward designing new interfacial materials for practical optoelectronic devices. [ABSTRACT FROM AUTHOR]