Search

ABSTRACT The pore structure of the hardened concrete and the microscopic changes of a few selected pores throughout the freeze-thaw test were investigated by a method combining RapidAir and digital [...]

When assessing the sliding stability of a concrete dam, the influence of large-scale asperities in the sliding plane is often ignored due to limitations of the analytical rigid body assessment methods provided by current dam assessment guidelines. However, these asperities can potentially improve the load capacity of a concrete dam in terms of sliding stability. Although their influence in a sliding plane has been thoroughly studied for direct shear, their influence under eccentric loading, as in the case of dams, is unknown. This paper presents the results of a parametric study that used finite element analysis (FEA) to investigate the influence of large-scale asperities on the load capacity of small buttress dams. By varying the inclination and location of an asperity located in the concrete-rock interface along with the strength of the rock foundation material, transitions between different failure modes and correlations between the load capacity and the varied parameters were observed. The results indicated that the inclination of the asperity had a significant impact on the failure mode. When the inclination was 30° and greater, interlocking occurred between the dam and foundation and the governing failure modes were either rupture of the dam body or asperity. When the asperity inclination was significant enough to provide interlocking, the load capacity of the dam was impacted by the strength of the rock in the foundation through influencing the load capacity of the asperity. The location of the asperity along the concrete-rock interface did not affect the failure mode, except for when the asperity was located at the toe of the dam, but had an influence on the load capacity when the failure occurred by rupture of the buttress or by sliding. By accounting for a single large-scale asperity in the concrete-rock interface of the analysed dam, a horizontal load capacity increase of 30%–160% was obtained, depending on the inclination and location of the asperity and the strength of the foundation material.

The location and geometry of large-scale asperity present at the foundation of concrete gravity dams and buttress dams affect the shear resistance of the concrete-rock interface. However, the parameters describing the frictional resistance of the interface usually do not account for these asperities. This could result in an underestimate of the peak shear strength, which leads to significantly conservative design for new dams or unnecessary stability enhancing measures for existing ones. The aim of this work was to investigate the effect of the location of first-order asperity on the peak shear strength of a concrete-rock interface under eccentric load and the model discrepancy associated with the commonly used rigid body methods for calculating the factor of safety (FS) against sliding. For this, a series of direct and eccentric shear tests under constant normal load (CNL) was carried out on concrete-rock samples. The peak shear strengths measured in the tests were compared in terms of asperity location and with the predicted values from analytical rigid body methods. The results showed that the large-scale asperity under eccentric load significantly affected the peak shear strength. Furthermore, unlike the conventional assumption of sliding or shear failure of an asperity in direct shear, under the effect of eccentric shear load, a tensile failure in the rock or in the concrete could occur, resulting in a lower shear strength compared with that of direct shear tests. These results could have important implications for assessment of the FS against sliding failure in the concrete-rock interface.

Common analytical assessment methods for concrete dams are unlikely to predict material fracture in the dam body because of the assumption of rigid body behavior and uniform- or linear stress distribution along a predetermined failure surface. Hence, probabilistic non-linear finite element analysis, calibrated from scale model tests, was implemented in this study to investigate the impact of concrete material parameters (modulus of elasticity, tensile strength, compressive strength, fracture energy) on the ultimate capacity of scaled model dams. The investigated dam section has two types of large asperities, located near the downstream and/or upstream end of the rock–concrete interface. These large-scale asperities significantly increased the interface roughness. Post-processing of the numerical simulations showed interlocking between the buttress and the downstream asperity leading to fracture of the buttress with the capacity being determined mainly by the tensile strength of the buttress material. The capacity of a model with an asperity near the upstream side, with lower inclination, was less dependent on the material parameters of the buttress as failure occurred by sliding along the interface, even with inferior material parameters. Results of this study show that material parameters of the concrete in a dam body can govern the load capacity of the dam granted that significant geometrical variations in the rock–concrete interface exists. The material parameters of the dam body and their impact on the capacity with respect to the failure mechanism that developed for some of the studied models are not commonly considered to be decisive for the load capacity. Also, no analytical assessment method for this type of failure exists. This implies that common assessment methods may misjudge the capacity and important parameters for certain failure types that may develop in dams.

Low-carbon materials, products and services are explicitly definedLow-carbon materials reduce carbon footprint and promote circular economy modelLow-carbon products have parts with low embedded GHG emissions and are recyclableLow-carbon services retain ownership of long-lasting materials/products by lendingStrategies to develop low-carbon materials, products and services are provided