Search

Polylactic acid/Polycarbonate (PLA/PC) blend was prepared via twin screw extruder by taking the bio-based content as much as possible and the better mechanical, thermal, and impact properties into consideration. Flame retardant (FR) performance of the PLA/PC blend was improved by using the mixture of ammonium polyphosphate, triphenyl phosphate, and zinc borate. FR properties of PLA/PC blend was evaluated according to the UL 94 test standard. The variations in tensile and flexural strength, and Izod-notched impact strength values were determined. In order to reduce the total amount of flame retardant additive, instead of using a mixture of TPP and APP (weight ratio of 2/1) at 21 wt% weight fraction, 1 wt% Zinc borate together with 18 wt% TPP-APP mixture was used and obtained V0 rating for the thickness of 1.5 mm. It was reported that weight fraction of flame retardant additives (APP and TPP) was successfully reduced by using a mixture of APP, TPP and ZnB without degrading the mechanical properties such as tensile and flexural strengths. Using less total FR additive weight (19 wt%) led to 15 and 24% higher tensile and flexural strength values, respectively, compared to higher FR additive weight (21 wt%).

In this study, ground wastes of Nettle (Urtica dioica L.) fiber (GWN), which contains cellulose of 52.2 wt%, hemicellulose of 28.9 wt%, and lignin of 18.9 wt%, filled polypropylene (PP) composites were fabricated by using a high-speed kinetic mixer. The effect of filling GWN into PP at different weight fractions on density, crystallization behavior, coefficient of thermal expansion, and thermal stability was investigated. In addition, tensile and flexural tests were performed to determine how the mechanical properties of PP were affected. Morphological observations were conducted using scanning electron microscopy (SEM). The flexural strength values of PP increased by 10%, 15%, and 31% with the addition of 7 wt%, 14 wt%, and 21 wt% GWN, respectively. However tensile strength value of PP decreased slightly with the addition of GWN. 21 wt% GWN addition into PP led to a considerable decrease (about 29%) in the thermal expansion coefficient of PP. The degree of crystallinity of PP was not affected by the addition of GWN.

Bu çalışmada, büyük oranda selüloz lifler ile inorganik katkılar (kalsit ve kil mineralleri) içeren kağıt üretim atıkları, farklı oranlarda (ağırlıkça %10-60) yüksek yoğunluklu polietilen (YYPE) kompozit üretiminde kullanılarak kağıt üretim atığı katkısının mekanik özellikler üzerindeki etkisi incelenmiştir. Kompozitler yüksek hızlı termo-kinetik mikseri ve kalıplama prosesi kullanılarak üretilmiştir. Üretilen kompozitlerin mekanik özellikleri standart test metotları kullanılarak analiz edilmiştir. Sonuçlara göre, kompozitlerin eğilme modül değerlerinin artan katkı oranıyla arttığı görülmüştür. Özellikle, eğilme dayanımının ağırlıkça %40 katkı içeren kompozitte %26.3 oranında arttığı ortaya konmuştur. Kağıt atık katkılı YYPE kompozitlerin çekme dayanımı YYPE matris ile kıyaslandığında %10-20 oranında artış görülmüştür. Sonuç olarak, sunulan çalışmada kağıt üretim atık katkıları hiçbir modifikasyon ajanı kullanılmadan kompozitlerin üretimi gerçekleştirilmiş ve buna rağmen kompozitlerin mekanik özelliklerinde gelişme sağlanmıştır. Bu sayede, endüstriyel atık olarak ekonomik bir değeri olmayan kağıt üretim atığı polimer kompozit yapı içerisinde kullanılarak iyi mekanik özelliklere sahip kompozitler üretilmiştir.