Search

Abstract This study evaluated how Er,Cr:YSGG laser, associated or not with 5% fluoride varnish, influences the surface roughness and volume loss of bovine root dentin submitted to erosive and/or abrasive wear. One hundred and twenty dentin specimens were divided into the groups: without preventive treatment (WPT), 5% fluoride varnish (FV); Er,Cr:YSGG laser irradiation (L), and varnish combined with laser (FV + L). The specimens (n = 10) were subdivided into: 1 = erosion (E); 2 = abrasion (A); and 3 = erosion followed by abrasion (E + A). The erosive solution used was a soft-drink (pH = 2.42 at 4ºC) applied in 5-min cycles twice a day for 10d. Abrasive wear involved brushing for 60s with an electric brush (1,600-oscillations/s) at a load of 2.0N. Surface roughness and volume loss were evaluated using a laser scanning confocal microscope. Roughness data were submitted to one-way ANOVA and Tukey post-hoc test. For volume loss, the Kruskal-Wallis and Dunn’s post-hoc tests were used (α = 5%). The lowest values of roughness were found in the control areas of all subgroups (p > 0.05). In the experimental area, the [(WPT) + (E+A)] subgroup had a significantly higher roughness (5.712 ± 0.163 μm 2 ) than the other subgroups (p < 0.05). The L and (FV + L) groups had statistically similar roughness, regardless of the type of wear. The (FV + L) group had the lowest volume loss, regardless of the type of wear performed: [(FV + L) + (E)] = 7.5%, [(FV + L) + (A) = 7.3%, and [(FV + L) + (E + A)] = 8.1%. The subgroup [(WPT) + (E + A)] had the highest volume loss (52.3%). The proposed treatments were effective in controlling dentin roughness. Laser irradiation can be an effective method to increase root dentin resistance after challenges and limit problems related to non-carious lesions.

The use of erbium lasers to prevent caries in enamel has shown positive results. However, it is not known if Er,Cr:YSGG laser can also be used to increase acid resistance of root dentine, which is another dental tissue susceptible to the action of cariogenic bacteria. Objective: To analyze the effects of the Er,Cr:YSGG laser (λ=2.78 μm, 20 Hz) irradiation associated with 2% neutral sodium fluoride (NaF) to prevent root dentin demineralization. Material and Methods: One hundred human root dentin samples were divided into 10 groups (G) and treated as follows: G1: no treatment; G2: NaF; G3: laser (4.64 J/cm2) with water cooling (WC=5.4 mL/min); G4: laser (4.64 J/cm2) without WC; G5: laser (8.92 J/cm2) with WC; G6: laser (8.92 J/cm2) without WC; G7: laser (4.64 J/cm2) with WC and NaF; G8: laser (4.64 J/cm2) without WC and NaF; G9: laser (8.92 J/cm2) with WC and NaF; G10: laser (8.92 J/cm2) without WC and NaF. The NaF gel was applied alone or after 4 min of irradiation. After 14 days of acid challenge, the samples were sectioned and the Knoop microhardness (KHN) test was done at different depths (30, 60, 90 and 120 μm) from the outer dentin surface. Data were analyzed by one-way ANOVA and Fisher’s test (α=5%). Results: The results showed that G8 and G10 presented higher KHN than the G1 for the depths of 30 and 60 μm, indicating an increase of the acid resistance of the dentin in up to 35% (p

Context: The knowledge of the reasons for the placement of direct restorations makes possible to trace an epidemiological profile of a specific population and to direct the teaching of dentistry to techniques that are commonly used today and will be continued performed in the future. Purpose: The aim of this study was to verify the reasons for placement and replacement of direct restorations in patients treated in the Dental Clinic of the Uberaba University - Brazil. Materials and Methods: This study evaluated 306 restorative procedures carried out on 60 patients. During the treatment planning, a form that contained information about the patient′s gender, tooth number, the classification of restorations, the reasons for placement and replacement of amalgam and tooth-colored restorations, the material that had to be removed and the new material used to fill the cavities was filled for each patient. Statistical analysis was carried out using Chi-square test (α = 0.05). Results: The data showed that most of the patients were female (66.7%). Of all the restorations placed, 60.45% were 1 st -time placements, while 39.55% were replacements. For 1 st -time restorations, the main reason for placement was primary caries (76.76%), followed by non-carious cervical lesions (15.14%). The amalgam restorations were replaced more frequently (67.77%). The primary reason for replacements was the presence of secondary caries (for both previous amalgam (42.68%) and composite (66.67%) restorations (P < 0.05). The resin composite was the most indicated material for the new restorations (98.04%) (P < 0.05). Conclusions: The main reason for placement of direct restorations was primary caries, while secondary caries was the main reason for replacements. In almost all cases, the material used to fill the cavities was the resin composite.

ABSTRACT Objective To describe e compare the specificity of IgA antibodies against bacteria extract of Klebsiella pneumoniae , Staphylococcus aureus , Escherichia coli , and Salmonella enteritidis . Methods Colostrum samples were aseptically collected in the first 12 hours after C-section delivery. The specificity of IgA against bacteria extracts was analyzed by the Western blot. Results The findings showed proteins of high molecular weight frequently detectable in the samples. S. aureus was the most frequently found bacterium in the samples (p

Abstract The objective of this study was to evaluate the effects of diode laser and a desensitizing dentifrice on dentin permeability. Fifty-two root dentin fragments were obtained (5 × 5mm) and treated with 24% EDTA gel. The samples were divided into 4 groups (n = 13): G1, control (no treatment); G2, diode laser (λ = 908 nm, 1.5 W, continuous mode, 20s); G3, application of abrasive dentifrice for 1 minute (Elmex Sensitive Professional (International Gaba); and G4, application of abrasive dentifrice for 1 minute followed by irradiation with diode laser. Ten samples per group were immersed in 2% methylene blue solution for 4h. The specimens were washed, longitudinally sectioned, observed under optical microscopy, photographed and assessed based on the degree of dye leakage. The remaining samples were observed under scanning electron microscopy (SEM). The leakage data were subjected to ANOVA test, followed by Tukey’s t-test (α = 5%). Groups 2, 3 and 4 showed less dye penetration than the control group (p < 0.05), but were similar among each other. SEM images showed that dentinal tubules were open in G1, and fused and occluded in G2. Group 3 showed dentinal tubules that were occluded by the metal ions from the toothpaste. G4 presented similar characteristics to G3, and the presence of fused dentin. The diode laser and the dentifrice were effective in reducing dentinal permeability, and the combination of the two treatments did not show better results than either one used alone.

Objective: To verify whether an infiltrant resin used to inactivate white spot lesions (WSL) on enamel can resist the abrasive challenges promoted by tooth brushing with different dentifrices. Material and Methods: WSL was induced on bovine enamel samples (pH cycling) and then treated with an infiltrant resin (ICON). Afterward, half of the sample was protected. The other half underwent an abrasive challenge using an electric toothbrush with soft bristles., using dentifrices with different abrasiveness (n=10): Group 1: Colgate Maximum Cavity Protection; Group 2: Sensodyne Repair & Protect; Group 3: Colgate Sensitive Pro-Relief; Group 4: Colgate 2 in 1 Watermelon Flavor; e Group 5: Colgate Luminous White Advanced. The wear profile after brushing was evaluated by confocal laser scanning microscopy (µm), and the enamel/resin interface was observed in scanning electron microscopy (SEM). Profilometry data were analyzed using one-way ANOVA followed by Tukey's test (α=5%). Results: Brushing produced more significant wear on group 5 (3.96±0.26) when compared to groups 1 (3.45±0.21), 2(3.22±0,4) and 4(3.11±0.34). Data from Group 3 (3.82±0.6) was similar to G5 but higher than G1, G2, and G4. SEM analysis showed that the adhesive interface remained intact in all groups after the abrasive challenge. Conclusion: Dentifrices with a higher relative dentin abrasiveness produced more significant wear of the infiltrant, but the composite/enamel interface was not altered after the abrasive challenges.

Abstract The present study compared IgA specificity against oral streptococci in colostrum and saliva samples. Sixty-two mother-and-child pairs were included; samples of colostrum (C) and saliva (MS) were collected from the mothers and saliva samples were collected from babies (BS). The specificity of IgA against Streptococcus mutans and S. mitis were analyzed by western blot. Only 30% of babies’ samples presented IgA reactivity to S. mutans, while 74 and 80% of MS and C, respectively, presented this response. IgA reactivity to S. mutans virulence antigens (Ag I/II, Gtf and GbpB) in positive samples showed differences between samples for Gtf and especially for GbpB (p < 0.05), but responses to Ag I/II were similar (p > 0.05). The positive response of Gtf-reactive IgA was different between C (90%) and MS (58%) samples (p < 0.05), but did not differ from BS (p > 0.05). GbpB was the least detected, with 48 and 26% of C and MS, and only 5% of BS samples presenting reactivity (p > 0.05). Eight percent of MS and C samples presented identical bands to SM in the same time-point. In conclusion, the differences of IgA response found between C and MS can be due to the different ways of stimulation, proliferation and transportation of IgA in those secretions. The colostrum has high levels of IgA against S. mutans virulence antigens, which could affect the installation and accumulation process of S. mutans, mainly by supplying anti-GbpB IgA to the neonate.

Abstract This study aimed to evaluate the influence of the Er,Cr:YSGG irradiation and 980-nm diode lasers on the surface roughness (SR) and volume loss (VL) of dentin subjected to cariogenic challenge. Subsequently, 130 specimens of bovine dentin were divided into the following 13 groups: NT: no treatment; FG: fluoride gel; FV: fluoride varnish; Di: 980-nm diode; Di + FG; Di + FV; FG + D; FV + Di; Er: Er,Cr:YSGG; Er + FG; Er + FV; FG + Er and FV + Er. Er,Cr:YSGG laser parameters were as follows: 0.25 W; 5.0 Hz; 4.46 J/cm2 without water and 55% air. Furthermore, the 980-nm diode laser parameters were 2.0 W; 2.0 Hz; 21.41 J/cm2. The samples from each group were subjected to pH cycling. A confocal laser scanning microscope was used to evaluate SR and VL. Difference between the volume of the reference and treated areas + DES/RE was used to determine SR and VL. The mean values of the different groups were subjected to analysis of variance and Tukey’s post-hoc test. The VL values were analyzed using the Kruskal–Wallis and Dunn post-hoc test (p < 0.05). The SR of the reference area did not show a statistically significant 1807-3107-bor-38-e025treatment and cariogenic challenge (p > 0.05). Moreover, VL in the FV + Di and FV + Er groups showed a statistically significant difference compared with areas submitted to different types of treatment and cariogenic challenge (p > 0.05). Er,Cr:YSGG and 980-nm diode lasers associated with fluoride varnishes decreased dentin VL in bovine teeth submitted to cariogenic challenge.

ABSTRACT Objective To detect Streptococcus mutans in colostrum and saliva of neonates and compare with its detection in saliva of mothers. Methods Forty-three healthy women, full-term gestations with no complications, submitted to elective Cesarean section, and their newborns were included in the study. Samples were investigated by polymerase chain reaction to detect S. mutans in genetic material from the samples. Results Approximately 16% of colostrum samples showed S. mutans , but not correlated with the presence of the bacteria in both samples of saliva. S. mutans was detected in 49 and 30% of saliva samples of mothers and neonates, respectively. There was a positive correlation in S. mutans detection between types of saliva. The number of maternal samples of saliva with detectable S. mutans was smaller in women receiving dental treatment during pregnancy. Tooth brushing, three times a day, influenced the detection of S. mutans in both the saliva and the colostrum. Conclusion Although maternal saliva may present S. mutans , few samples of colostrum present the bacteria. The presence of bacteria in neonate saliva may be related to contact before birth. Dental treatment and hygiene habits seem to influence the detection of S. mutans in samples of maternal saliva and colostrum.