Search

Nickel composite coating reinforced with reduced graphene oxide is fabricated by pulse electrodeposition method from a surfactant‐free bath at different current densities. The reduction of graphene oxide is done by an ecofriendly method which uses chlorophyll (CHL) as the reducing agent. The CHL also acts as a stabilizer because of its amphiphilicity. Auger electron spectroscopy is used to study the surface morphology and characteristics of the deposited coatings. Nanoindentation is used to study the mechanical properties. Electrochemical techniques such as potentiodynamic polarization and electrochemical impedance spectroscopy are used to study the corrosion behavior in 3.5 wt% NaCl solution. The coatings are found to exhibit superior hardness, Young's modulus, and corrosion resistance when compared with the pure Ni coating. Hardness and corrosion resistance are found to improve almost tenfold at optimized condition. Scanning electron microscopy of the corroded surface of the coatings provides an insight into the corrosion process. [ABSTRACT FROM AUTHOR]

Vanadium oxide films, deposited on aluminium (Al), titanium (Ti) and tantalum (Ta) metal substrates by pulsed RF magnetron sputtering at a working pressure of 1.5 x10−2 mbar at room temperature are found to display mixed crystalline vanadium oxide phases viz., VO2, V2O3, V2O5. The films have been characterized by field-emission scanning electron microscopy, X-ray diffraction, differential scanning calorimetry (DSC) and X-ray photoelectron spectroscopy, and their thermo-optical and electrical properties have been investigated. Studies of the deposited films by DSC have revealed a reversible-phase transition found in the temperature range of 45–49 °C. [ABSTRACT FROM AUTHOR]

Solar selective colored chromium oxide coatings were prepared on the SS304 substrate through the electrochemical deposition route to provide more options and flexibility in aesthetically design solar absorbers with acceptable energy performance. The variation of colors in the coatings was achieved by varying the coating thickness as a function of deposition time. Color changes in the coatings were also evident in the samples that were annealed under vacuum. Electron microscopic images show that nanometer sized pores are present on the coating surfaces. The pore-density, pore-size distribution and surface roughness exhibit significant changes with variations in deposition time and annealing temperature. Initially, the selectivity factor of 6.08 was recorded in the as prepared sample coated for 30 min, which improved to 7.36 on annealing the samples under vacuum at 700 °C, however, it drops to 4.22 when annealed at 900 °C. A similar trend was also observed for samples that are coated for 60 min. The results indicate that the pore-density, pore-size distribution and surface roughness play a dominant role in governing the solar selectivity of the coatings. Nanoindentation tests were performed on the coated samples and the results show that mechanical properties of the solar absorber coatings degrades with the increase in coating thickness but improve significantly with increase in annealing temperature. [ABSTRACT FROM AUTHOR]

Smooth, uniform and crystalline vanadium oxide thin films were deposited on quartz by spin coating technique with four different rpm i.e., 1000, 2000, 3000 and 4000 and subsequently post annealed at 350, 450 and 550 °C in vacuum. Transmission electron microscopy (TEM), Field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) techniques were utilized for microstructural characterizations and phase analysis, respectively, for vanadium oxide powder and deposited film. Nanorods were observed to be grown after vacuum annealing. X-ray photoelectron spectroscopy (XPS) technique was utilized to study the elemental oxidation state of deposited vanadium oxide films. Thermo-optical and electrical properties such as solar transmittance (τ s ), reflectance (ρ s ), absorptance (α s ), infrared (IR) emittance (ε ir ) and sheet resistance (R s ) of different thin films were evaluated. Based on the optical characteristics the optimized condition of the film processing was identified to be spin coated at 3000 rpm. Subsequently, the nanoindentation technique was utilized to measure hardness and Young's modulus of the optimized film. The measured nanomechanical properties were found to be superior to those reported for sputtered vanadium oxide films. Finally, temperature dependent phase transition characteristics of optimized vanadium oxide films were studied by differential scanning calorimetry (DSC) technique. Reversible and repeatable phase transition was found to occur in the range of 44–48 °C which was significantly lower than the phase transition temperature (i.e., 68 °C) of bulk VO 2 . [ABSTRACT FROM AUTHOR]

Scaffolds play a crucial role in bone tissue engineering to support the defect area through bone regeneration and defect reconstruction. Promising tissue regeneration without negative repercussions and avoidance of the lifelong presence inside the body make bioresorbable metals prosper in the field of regenerative medicine. Recently, Zn and its alloys have emerged as promising biodegradable materials for their moderate degradation rate and satisfactory biocompatibility. Nevertheless, it is very challenging for cells to adhere and grow over the Zn surface alone, which influences the tissue-implant integration. In this study, an attempt has been made to systematically investigate the bioactivity responses in terms of in vitro hemocompatibility, cytotoxicity, antibacterial activity, and in vivo biocompatibility of newly developed Zn-2Cu-0.5Mn/Mg alloy scaffolds with different surface roughness. The rough surface of Zn-2Cu-0.5Mg shows the highest degradation rate of 0.16 mm/yr. The rough surface exhibits a prominent role in the adsorption of protein, further enhancing cell adhesion. Concentration-dependent alloy extract shows the highest cell proliferation for 12.5% of the extract with a maximum cell viability of 101% in Zn-2Cu-0.5Mn and 108% in Zn-2Cu-0.5Mg after 3 d. Acceptable hemolysis percentages (less than 5%) with promising anticoagulation properties are observed for all of the conditions. Enhanced antibacterial ( Staphylococcus aureus and Escherichia coli ) activity due to a significant effect of ions illustrates the maximum killing effect on the bacterial colony for the rough Zn-2Cu-0.5Mg alloy. In addition, it is observed that for rough Zn-2Cu-0.5Mn/Mg alloys, the inflammatory response is minimal after subcutaneous implantation, and neo-bone tissue forms in the defect areas of the rat femur with satisfactory biosafety response. The osseointegration property of the Zn-2Cu-0.5Mg alloy is comparable to that of the Zn-2Cu-0.5Mn alloy. Therefore, the rough surface of the Zn-2Cu-0.5Mg alloy has the potential to enhance biocompatibility and promote better osseointegration activity with host tissues for various biomedical applications.

Zinc (Zn) and its alloys are considered futuristic biodegradable materials for their acceptable mechanical properties, suitable corrosion rate, and good biocompatibility. In this study, we report newly developed biodegradable Zn-2Cu -x Mn/Mg ( x = 0, 0.1, and 0.5) alloys, aiming to achieve good mechanical strength with excellent elongation, desirable wear resistance, and suitable corrosion rate. The effect of Mn/Mg addition on the structural, mechanical, wear, and degradation behaviors of the Zn-2Cu- x Mn/Mg alloys was thoroughly investigated. Degradation and tribological behaviors of the alloys were explored in the presence of simulated body fluid (SBF), Dulbecco's modified Eagle medium (DMEM), and DMEM with a 10% fetal bovine serum (FBS) solution. Alloy elements and hot rolling improve their mechanical properties significantly due to precipitation hardening, grain refinement, and solid solution strengthening owing to the formation of MnZn 13 and Mg 2 Zn 11 phases. Among all the alloys, the Zn-2Cu-0.5Mn alloy achieved the highest ultimate tensile strength (UTS) of ∼405 MPa and yield strength (YS) of ∼293 MPa with an excellent elongation of ∼51%. The corrosion behavior of the alloys as determined by a potentiodynamic polarization study under different solutions follows the sequence Zn-2Cu < Zn-2Cu-0.5Mn < Zn-2Cu-0.1Mn < Zn-2Cu-0.1Mg < Zn-2Cu-0.5Mg. The corrosion rate by immersion testing for 30 and 90 days also follows the same sequence. The corrosion rate in different solutions follows the order SBF > DMEM + 10%FBS > DMEM. The addition of Mn/Mg also improves the wear resistance and slows the wear rate under wet conditions. The bending test results also indicate the highest bending strength of ∼375 MPa for the Zn-2Cu-0.5Mn alloy, among all the alloys. The bending and tensile strengths deteriorate continuously after the immersion for 30 and 90 days in the solution of SBF, DMEM, and DMEM + 10%FBS. Therefore, the Zn-2Cu- x Mn/Mg ( x = 0.1 and 0.5) alloys can be considered potential biodegradable implant materials.