The 17-4 PH stainless steel is widely used in the aerospace, petrochemical, chemical, food, and general metallurgical industries. The present study was conducted to analyze the mechanical properties of two types of 17-4 PH stainless steel—commercial cold-rolled and direct metal laser sintering (DMLS) manufactured. This study employed linear and nonlinear tensile FEM simulations, combined with various materials characterization techniques such as tensile testing and nanoindentation. Moreover, microstructural analysis was performed using metallographic techniques, optical microscopy, scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). The results on the microstructure for 17-4 PH DMLS stainless steel reveal the layers of melting due to the laser process characterized by complex directional columnar structures parallel to the DMLS build direction. The mechanical properties obtained from the simple tension test decreased by 17% for the elastic modulus, 7.8% for the yield strength, and 7% for the ultimate strength for 17-4 PH DMLS compared with rolled 17-4 PH stainless steel. The FEM simulation using the experimental tension test data revealed that the 17-4 PH DMLS stainless steel experienced a decrease in the yield strength of ~8% and in the ultimate strength of ~11%. A reduction of the yield strength of the material was obtained as the grain size increased.

DIN 16MnCr5 is commonly used in mechanical engineering contact applications such as gears, joint parts, shafts, gear wheels, camshafts, bolts, pins, and cardan joints, among others. This study examined the microstructural and mechanical properties and tribological behavior of different surface treatments applied to DIN 16MnCr5 steel. The samples were hardened at 870 °C for 15 min and then quenched in water. The surface conditions evaluated were as follows: quenched and tempered DIN 16MnCr5 steel samples without surface treatments (control group), quenched and tempered DIN 16MnCr5 steel samples with gas-nitriding at 560 °C for 6 h, quenched and tempered DIN 16MnCr5 steel samples with pack boriding at 950 °C for 4 h, and quenched and tempered DIN 16MnCr5 steel samples with duplex gas-nitriding and pack boriding. Microstructure characterization was carried out using metallographic techniques, optical microscopy, scanning electron microscopy with energy-dispersive spectroscopy, and X-ray diffraction. The mechanical properties were assessed through microhardness and elastic modulus tests using nanoindentation. The tribological behavior was evaluated using pin-on-disc tests following the ASTM G99-17 standard procedure under dry sliding conditions. The results indicated that the surface treated with duplex gas-nitriding and pack boriding exhibited the highest wear resistance and a reduced coefficient of friction due to improved mechanical properties, leading to increased hardness and elastic modulus.