Abstract: Effect of Pr–Ni substitution on structural and magnetic properties of Ca0.5Ba0.5−x Pr x Ni y Fe12−y O19 (x=0.00–0.10 and y=0.00–1.00) prepared by the sol–gel auto combustion method were investigated. The XRD analysis confirmed the single phase M-type hexa-ferrite structure. The lattice parameters were found to increase as Pr–Ni content increases, which is attributed to the ionic size of the implicated cations. The Pr–Ni seems to be completely soluble in the lattice. Transmission electron microscopy reveals that the grain size decreases with increase of Pr–Ni substitution. The coercivity and remanent magnetization ranges from 1511 to 1925 (Oe) and 21.4 to 26.5 (emu/g), respectively. The coercivity values of all the samples fall in the range of M-type hexa-ferrites. [Copyright &y& Elsevier]

Holmium (Ho 3+ ) substituted W-type hexagonal ferrites (BaCo 2 Fe 16 O 27 ) were prepared by sol gel auto-combustion technique. The precursors were prepared by Ba 2+ , Fe 3+ nitrates solutions with citric acid as chelating agent. The prepared powder was sintered at 950 °C for 8 h to produce a single phase of W-type hexa ferrite with corresponding crystallite size ranging from 34 nm to 44 nm. The thermal decomposition of nitrate-citrate gel of as-prepared powder was investigated by TGA and DTA. The FTIR spectral study reveals the presence of two absorption bands which are characteristics of hexaferrites. DC electrical resistivity increases from 3.01×10 9 to 5.69×10 10 (ohm-cm). The real and imaginary parts of dielectric constant (ɛʹ, ϵ״) and dielectric loss tangent (tan δ) are determined in the frequency range of 20 Hz–1 MHz. It was observed that both real and imaginary parts of the dielectric constant and tanδ decrease with the increase of frequency on the basis of Wagner and Koop's theory. [ABSTRACT FROM AUTHOR]