Search

It is an effective way to develop basswood (Tilia americana, hardwood)-derived thick carbon electrode for high energy density supercapacitors. The wood-derived anisotropic structural carbon electrodes have different transfer kinetics of the electrolyte, which will significantly affect the electrochemical performance especially at high current density. Therefore, the relationship between the sectional wood-derived electrodes and the electrochemical performance of supercapacitors were systematically studied. The results show that the high specific surface area (542 m2 g−1) of cross-sectional wood-derived carbon contributes to the excellent electrochemical performance (specific/area capacitance ~ 3040 mF cm−2/118 F g−1 at 1 mA cm−2, cycle stability ~ 82.2% after 10,000 cycles at 50 mA cm−2, and capacitive contribution of 76.64% at 5 mV s−1), which is attributed to the hierarchical porous structure and easily allows electrolytes to enter the interior even at high current density. This work provides a fundamental understanding of the dynamic behaviors of electrolyte at different wood sections, and it is expected to be extended to other wood species and wood-like structures for energy storage applications. [ABSTRACT FROM AUTHOR]

[Display omitted] • The effect of electrode thickness on the supercapacitance performance is studied. • Bass wood with hierarchical pores is easy processed to thick electrode. • The thick electrodes have high specific/areal/volumetric energy/power densities. • The SSC shows excellent cycling performance of 81% (20 mA cm−2, 15 000 cycles). The practical application of energy storage device requires high areal/volumetric energy density. One of the strategies is to design bulk electrode with hierarchical porous structure for the application of supercapacitor. Significantly, the energy storage electrochemical performance of the bulk electrode is highly influenced by the pore structure regulation and electrolyte infiltration. Therefore, it is necessary to design thick electrodes with proper pore structures and investigate the effect of thickness on the supercapacitance performance. In this work, bass wood is selected as the carbon source of electrode because of its hierarchical porous structure and easy processing into different thicknesses. The wood-derived carbon thick electrode with a thickness of 1.532 mm (CWT1.532) presents the best supercapacitance performance. Such electrode possesses a high active material loading of 54.75 mg cm−2. The symmetrical supercapacitor from CWT1.532 electrode displays remarkable specific capacitance of 65 F g−1 and areal/volumetric capacitance of 0.846 F cm−2 and 2.67 F cm−3 at 1.0 mA cm−2, respectively. It also exhibits mass/areal/volumetric power densities of 38.47 W kg−1, 500 mW cm2 and 1580 mW cm−3 as well as the corresponding energy densities of 9.04 Wh kg−1, 117.5 mWh cm−2 and 0.374 mWh cm−3, respectively. Moreover, the symmetrical supercapacitor shows an attractive cycling stability with a supercapacitance retention of 81.48% at 20 mA cm−2 even after 15 000 long-term cycles. This work provides an essential understanding about the effect of different thicknesses on the thick electrode-assembled supercapacitance and inspires future practical application in other energy storage areas. [ABSTRACT FROM AUTHOR]