Search

A series of single phase spinel ferrites having chemical formula Mg 0.5 Zn 0.5 Pr x Fe 2− x O 4 ( x =0.00, 0.05, 0.10, 0.15, 0.20, 0.25) were prepared using the sol–gel technique after sintering at 700 °C. The thermal decomposition behavior of an as prepared powder was investigated by means of DTA/TGA analyses. The sintered powders were then characterized by Fourier transform infrared spectroscope, X-ray diffraction, scanning electron microscope, energy dispersive X-ray spectroscope and vibrating sample magnetometer. X-ray diffraction patterns confirm the single phase spinel structure of prepared ferrites without the presence of any impurity phase. The value of lattice parameter ( a ) increases with the increase of Pr contents ( x ) into the spinel lattice. The grain size estimated from electron microscope images is in the range of 2.75–5.4 µm which confirms the spinel crystalline nature of the investigated samples. The saturation magnetization ( M s ) decreases whereas coercivity ( H c ) increases with the increase of Pr contents ( x ). The measured parameters suggest that these materials are favorable for high frequency applications and as core materials. [ABSTRACT FROM AUTHOR]

Abstract: CoHo x Fe2−x O4 ferrites (x=0.00–0.1) were prepared by the co-precipitation technique and the effect of holmium substitution on the magnetic properties was investigated. X-ray diffraction reveals that the substituted samples show a second phase of HoFeO3 along with the spinel phase. The magnetic properties such as the saturation magnetization (M s ), coercivity (H c ) and remanence (M r ) are obtained from the hysteresis loops. It is observed that the M s decreases while H c increases with Ho3+ substitution. The decrease of saturation magnetization is attributed to the weakening of exchange interactions. The coercivity increases with increase of the Ho3+ concentration, which is attributed to the presence of an ultra-thin layer at the grain boundaries that impedes the domain wall motion. Low field AC susceptibility was also measured over the temperature range 300–600K at the frequency of 200Hz. It decreases with the increase of temperature following the Curie–Weiss law up to the Curie temperature. Above the Curie temperature it shows paramagnetic behavior. The increase in coercivity suggests that the material can be used for applications in perpendicular recording media. [Copyright &y& Elsevier]

Abstract: A series of Al-substituted Co2W hexaferrites BaCo2Al x Fe16 − x O27 (x = 0, 0.2, 0.4, 0.6, 0.8, 1) synthesized by sol-gel autocombustion method have been investigated. The samples were characterized by DTA/TGA analysis, FTIR spectroscopy, X-ray Diffractometer and field emission gun scanning electron microscopy (FEGSEM). Magnetic behavior of a selected sample was examined up to a magnetic field of 9T between a temperature range of 4.2 K–400 K. The values of saturation magnetization were calculated by the law of approach to saturation. The coercivity of the investigated sample has a value of about hundred oersteds at room temperature which is favorable for EM materials. The complex permittivity and complex permeability of a composite sample have been measured in the frequency range of 0.5–13 GHz. Based on the theoretical calculation of reflection loss; the microwave absorption properties have been investigated. The results indicate that the attenuation peak frequency of these compounds can be tuned for the desired frequency by varying the thickness of the absorber. [Copyright &y& Elsevier]

Abstract: Nano-sized and single phase W-type hexaferrite (BaCo2Fe16O27) powders synthesized by sol–gel autocombustion method have been investigated. The samples were sintered in a temperature range of 1000–1200°C for 5h. The thermal decomposition behavior of as-prepared powder was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of powders were investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). The grain size calculated by Scherer equation was found in the range of 36–47nm which is small enough to obtain a suitable signal-to-noise ratio in high density recording media. Hysteresis loop measurements show that the coercivity values lie in the range of 210.61–1602.6Oe with increasing sintering temperature. Magnetization studies show a significant increase in the values from 15 to 22emu/g. The dc electrical resistivity is observed to decrease up to a certain value as the temperature increases and then rises at higher temperature. [Copyright &y& Elsevier]

Abstract: Lanthanum doped W-type hexaferrites BaZn2La x Fe16−x O27 (x =0, 0.2, 0.4, 0.6, 0.8, 1.0) were synthesized by co-precipitation and sintered at 1320°C. The X-ray diffraction reveals W-type hexagonal structure with few traces of secondary phase. The decrease in grain size as a function of La-concentration is attributed to the fact that La acts as a grain inhibitor. The saturation magnetization and remanance decrease due to spin canting on B-sites. The increase in coercivity follows 1/r behavior where r is the radius of grain. The DC resistivity was observed to increase from 0.59×107 to 8.42×107 Ωcm with increasing La-contents due to the unavailability of Fe3+ ions. This enhancement in resistivity makes these materials promising candidates for use at high frequencies in order to reduce eddy current losses. [Copyright &y& Elsevier]

Abstract: A series of BaHo x Fe16−x O27 (x =0.0, 0.2, 0.4, 0.6, 0.8, 1.0) W-type hexagonal ferrites were prepared by co-precipitation technique at high annealing temperature of 1320°C. XRD reveals single W-type hexagonal phase in these ferrites. The grain size is measured by SEM analysis using line intercept method. Saturation magnetization, retentivity and coercivity were measured from MH-loops taken on VSM. It was observed that magnetization increases with the increase of Ho content due to difference in ionic radii of Ho3+ (0.901Å) and Fe3+ (0.67Å) ions. Room temperature dc resistivity increases as a function of Ho3+ that may be due to separation between grains. The dc electrical resistivity decreases as a function of temperature which indicates the semi-conducting behavior of the samples. [Copyright &y& Elsevier]

Abstract: We have prepared BaCd2−x Sr x Fe16O27 (x =0, 0.5, 1, 1.5 and 2.0) W-type hexagonal ferrites by standard ceramic method. In this work, the structural, dielectric and magnetic properties have been studied of the prepared samples. The XRD analysis of the samples reveals single phase behavior sintered at 1400°C for 6h. The saturation magnetization (M s ) shows increasing behavior with the increasing concentration of Sr2+. While the coercivity (H c ) decreases rapidly up to 409G for x =1.5 and then increases for (x >1.5) due to the preference of Cd2+ for tetrahedral sites and the number of spin-down magnetic ions. The real and imaginary parts of the dielectric constant (ɛ′,ɛ″) and dielectric loss tangent (tan δ) are determined in the frequency range 0.1–107 Hz. It is observed that both the real and imaginary parts of the dielectric constant and tan δ decrease with the increasing concentration of Sr2+, which is due to the contribution of Cd2+ ions in addition to Fe3+ and Fe2+ ions to interfacial polarization. [Copyright &y& Elsevier]