Search

Highlights: [•] Sr-substituted Y-type hexaferrites synthesized by sol–gel method have been investigated. [•] Platelet grains with well defined hexagonal shape are suitable for microwave absorbers. [•] Saturation magnetization values were calculated by the law of approach to saturation. [•] Coercivity of a few hundred oersteds found for all samples is suitable for EM materials. [ABSTRACT FROM AUTHOR]

Highlights: [•] W-type hexagonal ferrites substituted with different divalent ions have been investigated. [•] Platelets like grains with hexagonal shape are suitable for microwave absorbers. [•] Saturation magnetization was calculated by the law of approach to saturation. [•] The low value of coercivity for the investigated sample is favorable for EM materials. [•] The materials are good for suppression of EMI and as radar absorbing materials (RAMs). [ABSTRACT FROM AUTHOR]

Highlights: [•] Al-substituted W-type hexaferrites with formula BaCo2Al x Fe16−xO27 were investigated. [•] DC resistivity increased with increasing Al contents due to unavailability of Fe3+ ions. [•] The increased value of resistivity is favorable for microwave absorption. [•] The coercivity (Hc ) values for all the samples lie in the range of a few hundred oersteds. [•] The low value of Hc is suitable for EM materials, switching and sensing applications. [ABSTRACT FROM AUTHOR]

Highlights: [•] A series of X-type hexagonal ferrites were prepared by sol–gel method. [•] The XRD analysis showed that the X-type hexagonal structure. [•] The c/a ratio of these samples falls in the range of X-type hexagonal ferrites. [•] The magnetic properties enhances with the increase of Nd–Co contents. [•] The samples show the reflection loss at smaller frequencies. [Copyright &y& Elsevier]

Abstract: A series of single phased Y-type hexagonal ferrites Sr2Ni2−x Mg x Fe12O22 (x=0.0, 0.1, 0.2, 0.3, 0.4, 0.5) were synthesized by the sol–gel auto combustion method. The effects on structural, magnetic and electrical properties have been investigated by substituting Mg2+ at Ni2+ sites. The X-ray diffraction (XRD) patterns confirm single phase Y-type hexaferrite and various parameters such as lattice constants, cell volume, X-ray density, bulk density and porosity have been calculated from XRD data. The Fourier transform infrared (FTIR) spectra show the characteristics absorption ferrite peaks of the sintered sample. The microstructure was studied by scanning electron microscopy (SEM). All the ferrites show a hexagonal platelet-like shape which is a most suitable shape for microwave absorption. The dielectric constant followed the Maxwell–Wagner interfacial polarization and relaxation peaks were observed in the dielectric loss properties. The room temperature dc electrical resistivity and activation energy were found to decrease for samples x=0.1, 0.2 and increase for the rest of samples hence making these materials suitable for multilayer chip inductors (MLCIs). A soft magnetic behavior was revealed by M–H loops. Saturation magnetization (M s), retentivity (M r), coercivity (H c) and magnetic moment (n B) were found to decrease as the Mg2+ contents increased. [Copyright &y& Elsevier]

Abstract: Nano-sized and single phase W-type hexaferrite (BaCo2Fe16O27) powders synthesized by sol–gel autocombustion method have been investigated. The samples were sintered in a temperature range of 1000–1200°C for 5h. The thermal decomposition behavior of as-prepared powder was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of powders were investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). The grain size calculated by Scherer equation was found in the range of 36–47nm which is small enough to obtain a suitable signal-to-noise ratio in high density recording media. Hysteresis loop measurements show that the coercivity values lie in the range of 210.61–1602.6Oe with increasing sintering temperature. Magnetization studies show a significant increase in the values from 15 to 22emu/g. The dc electrical resistivity is observed to decrease up to a certain value as the temperature increases and then rises at higher temperature. [Copyright &y& Elsevier]

Abstract: We have prepared BaCd2−x Sr x Fe16O27 (x =0, 0.5, 1, 1.5 and 2.0) W-type hexagonal ferrites by standard ceramic method. In this work, the structural, dielectric and magnetic properties have been studied of the prepared samples. The XRD analysis of the samples reveals single phase behavior sintered at 1400°C for 6h. The saturation magnetization (M s ) shows increasing behavior with the increasing concentration of Sr2+. While the coercivity (H c ) decreases rapidly up to 409G for x =1.5 and then increases for (x >1.5) due to the preference of Cd2+ for tetrahedral sites and the number of spin-down magnetic ions. The real and imaginary parts of the dielectric constant (ɛ′,ɛ″) and dielectric loss tangent (tan δ) are determined in the frequency range 0.1–107 Hz. It is observed that both the real and imaginary parts of the dielectric constant and tan δ decrease with the increasing concentration of Sr2+, which is due to the contribution of Cd2+ ions in addition to Fe3+ and Fe2+ ions to interfacial polarization. [Copyright &y& Elsevier]