Both softwood (southern yellow pine) and hardwood (red oak) can be completely dissolved in the ionic liquid 1-ethyl-3-methylimidazolium acetate ([C2mim]OAc) after mild grinding. Complete dissolution was achieved by heating the sample in an oil bath, although wood dissolution can be accelerated by microwave pulses or ultrasound irradiation. It has been shown that [C2mim]OAc is a better solvent for wood than 1-butyl-3-methylimidazolium chloride ([C4mim]Cl) and that variables such as type of wood, initial wood load, particle size, etc.affect dissolution and dissolution rates; for example, red oak dissolves better and faster than southern yellow pine. Carbohydrate-free lignin and cellulose-rich materials can be obtained by using the proper reconstitution solvents (e.g., acetone/water 1 : 1 v/v) and approximately 26.1% and 34.9% reductions of lignin content in the reconstituted cellulose-rich materials (from pine and oak, respectively) have been achieved in one dissolution/reconstitution cycle. The regenerated cellulose-rich materials and lignin fractions were characterized and compared with the original wood samples and biopolymer standards. For pine, 59% of the holocellulose (i.e., the sum of cellulose and hemicellulose) in the original wood can be recovered in the cellulose-rich reconstituted material; whereas 31% and 38% of the original lignin is recovered, respectively, as carbohydrate-free lignin and as carbohydrate-bonded lignin in the cellulose-rich material. [ABSTRACT FROM AUTHOR]

Lignocellulosic biomass composite fibers (southern yellow pine and bagasse) were successfully prepared directly from the ionic liquid, 1-ethyl-3-methylimidazolium acetate ([C2mim]OAc) with a dry-jet wet spinning process using short dissolution times (10–30 min) and temperatures above the glass transition temperature of lignin. Fibers could not be spun at all from solutions of pine dissolved using previously reported dissolution methods (110 °C, 16 h), while bagasse fibers spun using the higher temperature/shorter time method were stronger than those obtained using the lower temperature/longer time method. [ABSTRACT FROM AUTHOR]