As the mine enters the deep mining stage, there is a need to enhance the compressive strength and toughness of the backfill. The objective of this study is to examine the mechanical properties of cemented tailings backfill after the incorporation of multi-size fibers and to validate the toughening mechanism of basalt fibers (BFs). To achieve this, a series of basic mechanical property tests for multi-size BFs mixing were devised, accompanied by industrial computerized tomography (CT) scanning and discrete element simulation. This study shows that the compressive strength increases and then decreases with the increase of BF dosage at a certain percentage of each size, and the splitting tensile strength gradually increases with the increase of BF dosage. The compressive strength tends to decrease and then increase, and the splitting tensile strength increases and then decreases as the fiber size ratio changes. The distribution of cemented tailings backfill and BF within the discrete element model is random. A few BF cannot play a bridging role; however, a moderate amount of BF is relatively uniformly distributed in the model to form a network structure, which generates a bond between the particles and the matrix and can effectively limit the expansion path of cracks and enhance the toughness. [ABSTRACT FROM AUTHOR]

Layering of filling body is common in large-scale filling areas. In this paper, the cement–sand ratio of 1:8 is based on the configuration of 68%, 70%, 72% and 74%; four concentrations; and filling layers of one-, two-, three- and four-layered cemented filling samples. Combined with a uniaxial compression test and two-dimensional particle flow software (PFC2D), the mechanical properties and failure modes were explored. The results show that the concentration can strengthen the uniaxial compressive strength of the filling body while increasing the filling times weakens its power; therefore, the constitutive damage model was constructed. It was found that the initial layered damage existed in the layered filling, and the total damage showed an upward trend of first fast and then slow; the main failure modes of one-layer and two-layer backfills showed prominent shear failure characteristics, and the three-layer and four-layer fillings were closer to tensile failure. From the crack generation to the specimen failure, there is a mutual conversion between different energies. [ABSTRACT FROM AUTHOR]