Photocatalysts based on g-C3N4 have been investigated in the CO2 reduction reaction under visible light irradiation (λ = 397, 427, 452 nm). Photocatalysts were prepared by melamine calcination at 500–600 °C with further platinum deposition (0.1–1.0 wt.%). The effect of the preparation conditions of g-C3N4 and the method of platinum deposition on the physicochemical properties and activity of photocatalysts was studied. The photocatalysts were investigated by X-ray photoelectron spectroscopy, X-ray absorption spectroscopy, X-ray diffraction, high resolution transmission electron microscopy, UV-Vis spectroscopy, and low temperature nitrogen adsorption techniques. It has been found that the efficiency of CO2 reduction is governed by the surface area of g-C3N4 and the presence of platinum in the metallic state, while the optimal content of platinum is 0.5 wt. %. The highest rate of CO2 reduction achieved over Pt/g-C3N4 photocatalyst is 13.2 µmol h−1 g−1 (397 nm), which exceeds the activity of pristine g-C3N4 by 7 times. The most active photocatalysts was prepared by calcining melamine in air at 600 °C, followed by modification with platinum (0.5 wt.%). [ABSTRACT FROM AUTHOR]

The synthesis and characterisation of Ti–Zr mixed oxides containing 1 to 10 wt.% of Zr is herein reported. In addition, the samples were tested as photocatalysts in the generation of hydrogen from aqueous methanol solutions. The solids were prepared by sol-gel and then characterised by X-ray diffraction, high resolution electron microscopy, X-ray photoelectron spectroscopy, physisorption of nitrogen, scanning electron microscopy, UV-vis and Raman spectroscopies. The results show the presence of anatase as a predominant structure and the oxides present larger specific surface areas than that of pure titania. A maximum value of 168 m2/g was determined for the sample with 5 wt.% of zirconium. The calculated band gap energies varied from 3.05 to 3.15 eV. It was observed that the greater the zirconium content in the solid, the higher the generation rate of hydrogen when testing the Ti–Zr solids as photocatalysts. Under our experimental conditions, the best catalyst, Ti–Zr oxide with 10 wt.% Zr, showed a production rate of 2100 μmol of H2/h which was about tenfold higher than that observed for pure titania. [ABSTRACT FROM AUTHOR]