Thermophotovoltaic conversion using heat to generate electricity in photovoltaic cells based on the detraction of thermal radiation suffers from many engineering challenges. The focus of this paper is to study the nanostructure of AlGaAsSb for thermophotovoltaic energy conversion using lattice-matched heterostructures of GaSb-based materials in order to overcome the current challenges. The XAFS spectroscopy technique was used to analyze electronic structures and optical properties of GaSb, (Al, In) GaSbAs. The XAFS spectroscopy analysis showed a powerful decay at peak intensity that reveals to be related to a loss in Sb amount and light As atoms replaced in Sb atoms by 25%. Moreover, it was found that Al/In doped samples have highly symmetric data features (same atomic species substitution). The narrow direct bandgap energy, Eg of Al0.125Ga0.875Sb0.75As0.25 material raised (0.4–0.6 eV) compared to conventional photovoltaic cell bandgap energy (which is generally less than 0.4 eV) with weak absorption coefficients. The thermoelectric properties of AlGaAsSb computed via Botlztrap code showed that the electrons made up the majority of the charge carriers in AlGaAsSb. This nanostructure material exhibited a higher and acceptable figure of merit and demonstrated a promising thermoelectric material for solar thermophotovoltaic applications.

A design for midinfrared diode lasers based on interband type-II miniband-to-bound state transitions is proposed and has been demonstrated experimentally. Type-II miniband-to-bound state laser structures emitting at 3.25 mu with active regions consisting of 5 and 10 W periods were grown by solid-source molecular-beam epitaxy and processed into ridge waveguide lasers. Substrate-side down mounted devices with a 10 period active region and uncoated facets could be operated in continuous-wave (cw) mode up to 185 K and as high as 260 K in pulsed mode. A high characteristic temperature of 100 K has been achieved for heat-sink temperatures below 140 K, decreasing to 33 K for the 140 to 185 K interval. At 110 K, a 5 period laser structure exhibited a threshold current density of 177 A/cm2and a slope efficiency of 61 mW/A. Single-ended output powers of 144 mW in cw mode and exceeding 330 mW in pulsed operation were obtained for a substrate-side down mounted 5 period diode laser with high-reflection/antireflection coated mirror facets, operated at 110 K.