Search

Problem statement. Conducting graphitization anti-friction nickel steel in different initial conditions, but with the same phase composition at different temperatures graphitic annealing. Method. Experimental samples were prepared by centrifugal casting, which provides a sufficient density of samples of the investigated steels. The number of martensitic component was measured using ferritometer FA−1. The number of inclusions of graphite annealing was determined using stereometrical analysis by counting the number of particles per mm2. Results. It is established that the kinetics of the graphitization process in cast samples and in samples which have been austenitization and cold processing, is significantly different, despite the same phase composition and the same temperature graphitic annealing. The cientific novelty lies in the definition of slowing down the process of graphitization in cast nickel steels containing different amount of nickel at the temperatures of 650 and 850 °C, namely, a slowing down of this process by reducing the content of nickel, despite the education of martеnsit the cast structure of these steels, as well as in determining the influence of the martensitic component on the process kinetics of graphitization in steel nickel, which has been austenitization and cold processing. Practical significance. The results can be considered in the development of the composition and mode of heat treatment of bearing steels for use in heavy-duty friction-slip of metallurgical units., Постановка проблемы. Проведение графитизации антифрикционной никелевой стали в различных исходных состояниях, но с одинаковым фазовым составом, при различных температурах графитизирующего отжига. Методика. Экспериментальные образцы получали путем центробежного литья, что обеспечивало достаточную плотность образцов исследуемых сталей. Количество мартенситной составляющей измеряли с помощью ферритометра ФА–1. Количество включений графита отжига определяли с помощью стереометрического анализа путем подсчета количества частиц на квадратный миллиметр. Результаты. Установлено, что кинетика процесса графитизации в литых образцах и в образцах, которые прошли аустенитизацию и обработку холодом, значительно отличается, несмотря на одинаковый фазовый состав и одинаковые температуры графитизирующего отжига. Научная новизна заключается в установлении замедления процесса графитизации в литых никелевых сталях, содержащих различное количество никеля, при температурах 650 и 850 °С, а именно – замедление этого процесса при уменьшении содержания никеля и увеличении количества мартенсита в литой структуре этих сталей, а также в установлении неоднозначного влияния мартенситной составляющей на кинетику процесса графитизации в никелевой стали, которая прошла аустенитизацию и обработку холодом. Практическая значимость. Результаты работы могут быть учтены при разработке состава и режима термической обработки антифрикционных графитизированных сталей для использования их в тяжелонагруженных узлах трения − скольжения металлургических агрегатов., Постановка проблеми. Проведення графітизації антифрикційної нікелевої сталі у різних вихідних станах, але з однаковим фазовим складом, за різних температур графітизуючого відпалу. Методика. Експериментальні зразки отримували шляхом відцентрового виливання, що забезпечувало достатню щільність зразків досліджуваних сталей. Кількість мартенситної складової вимірювали за допомогою феритометра ФА–1. Кількість включень графіту відпалу визначали за допомогою стереометричного аналізу шляхом підрахунку кількості частинок на квадратний міліметр. Результати. Встановлено, що кінетика процесу графітизації у литих зразках та у зразках, які пройшли аустенітизацію та обробку холодом, значно відрізняється, незважаючи на однаковий фазовий склад та однакові температури графітизуючого відпалу. Наукова новизна полягає у визначенні уповільнення процесу графітизації у литих нікелевих сталях, що вміщують різну кількість нікелю, за температур 650 та 850 °С, а саме – уповільнення цього процесу у разі зменшення вмісту нікелю та збільшення кількості мартенситу в литій структурі цих сталей. а також у визначенні неоднозначного впливу мартенситної складової на кінетику процесу графітизації в нікелевій сталі, яка пройшла аустенітизацію та обробку холодом. Практична значимість. Результати дослідження можуть бути враховані для розроблення складу та режиму термічної обробки антифрикційних сталей, що графітизуються, для використання їх у важконавантажених вузлах тертя-ковзання металургійних агрегатів.

Problem statement. Using high-temperature thermal cycling in the field of peritectic transformation to obtain atomized high-speed steel structure during its crystallization. Method. Experimental samples were obtained using a structure and hardening test facility which makes it possible to use a computer-aided high-temperature thermal cycling + hardening combined mode, fix the structure at desired temperature and crush carbide phases. Results. It has been found that during thermal cyclic treatment the chemical composition of carbides and phase composition of steel change which results in crushing of carbide particles and their more uniform distribution in the austenitic matrix. The scientific novelty consists in determining the effect of thermal cyclic treatment that occurs in the liquid-solid region in R6M5F3 steel on the structure formation which is characterized by a decrease in dendritic segregation and the sizes of carbide phases and their more uniform distribution. Practical significance. High-temperature thermal cyclic treatment of cast billets during their crystallization makes it possible to obtain more uniform and atomized steel structure. This will reduce costs required for further multiple heat treatments which are still used at factories in the manufacture of cutting tools and therefore reduce the cost price of the finished tool. Moreover, a more uniform distribution of alloying elements and crushed carbide phases will ensure increased secondary hardness and durability of cutting tools made of R6M5F3 steel., Постановка проблемы. Проведение высокотемпературного термоциклирования в области перитектического превращения для получения измельченной структуры быстрорежущей стали еще во время кристаллизации. Методика. Экспериментальные образцы получали с помощью установки для структурнозакалочных исследований, которая позволяет осуществлять с помощью компьютерных программ комбинированный режим ВТЦО-закалка, фиксировать структуру при необходимой температуре, а также измельчать карбидные фазы. Результаты. Установлено, что при термоциклической обработке изменяется химический состав карбидов и фазовый состав стали, что приводит к измельчению карбидных включений и более равномерному их распределению в аустенитной матрице. Научная новизна заключается в определении влияния термоциклической обработки, которая осуществляется в жидкотвердой области в стали Р6М5Ф3, на структурообразование, которое характеризуется уменьшением дендритной ликвации, размеров карбидных фаз и их более равномерным расположением. Практическая значимость. Применяя высокотемпературную термоциклическую обработку литых заготовок в процессе их кристаллизации, можно получить более равномерную и измельченную структуру стали. Это позволит уменьшить затраты на дальнейшую многократную термическую обработку, которая используется до сих пор на предприятиях при изготовлении режущих инструментов, что снизит себестоимость готового инструмента. Кроме того, более равномерное распределение легирующих элементов и измельченных карбидных фаз обеспечит повышенную вторичную твердость и износостойкость режущего инструмента из стали Р6М5Ф3., Постановка проблеми. Проведення високотемпературного термоциклування в області перитектичного перетворення для отримання подрібненої структури швидкорізальної сталі ще під час кристалізації. Методика. Експериментальні зразки отримували за допомогою установки для структурно-гартівних досліджень, що дозволяє здійснювати за допомогою комп’ютерних програм комбінований режим ВТЦО + гарт, фіксувати структуру за необхідної температури, а також подрібнювати карбідні фази. Результати. Установлено, що під час термоциклічної обробки змінюється хімічний склад карбідів і фазовий склад сталі, що спричинює подрібнення карбідних включень та більш рівномірний їх розподіл в аустенітній матриці. Наукова новизна полягає у визначенні впливу термоциклічної обробки, що відбувається в рідко-твердій області в сталі Р6М5Ф3, на структуроутворення, яке характеризується зменшенням дендритної ліквації, розмірів карбідних фаз та їх більш рівномірним розташуванням. Практична значимість. Застосовуючи високотемпературну термоциклічну обробку литих заготовок під час їх кристалізації, можна отримати більш рівномірну та подрібнену структуру сталі. Це дозволить зменшити витрати на подальшу багаторазову термічну обробку, яка застостовується досі на підприємствах для виготовлення різальних інструментів, що знизить собівартість готового інструменту. Крім того, більш рівномірний розподіл легуючих елементів та подрібнених карбідних фаз забезпечить підвищену вторинну твердість та зносостійкість різального інструменту із сталі Р6М5Ф3.