Search

Crystalline metal boride powders were synthesized via low temperature method in inorganic molten salt medium, and binary and ternary metal boride composite powders were investigated using anhydrous metal chlorides and sodium borohydride powder mixtures. The reactions were carried out in an aluminum crucible placed in a silica tube under argon which was put in a vertical tube furnace. At the end of the reaction, the resulting powder mixture was leached with hot water to remove any undesirable chloride phases. In order to improve crystalline properties, some of pure powders were selected and annealed at 1100°C. Characterization of synthesized and annealed powders was carried out using X-ray diffractometer (XRD), X-ray fluorescence spectrometry (XRF), scanning electron microscopy (SEM / EDX) and dynamic light scattering technique (DLS). The results showed the positive effect of inorganic molten salt technique (LiCl/KCl eutectic mixture) on the formation of phases during the reaction between CoCl2, NiCl2 and NaBH4 powder mixtures. Following the reactions at between 750-950 °C, the binary and ternary metal boride powders consisting of CoB-Ni2B-CoBx, CoB-Ni4B3 ve CoB-NiB-Ni2Co0.67B0.33 phases were obtained. The measured particle size of the final particles had an average of 60 nm., Kristalin metal borür tozları inorganik ergimiş tuz ortamında düşük sıcaklık yöntemi ile sentezlenmiş, ikili ve üçlü metal borür kompozit tozlarının eldesi susuz metal klorürler ve sodyum borhidrür toz karışımları kullanılarak incelenmiştir. Reaksiyonlar, argon altında dikey bir tüp fırında silika tüp içine yerleştirilmiş alüminyum pota içinde gerçekleştirilmiştir. Reaksiyon sonunda elde edilen toz karışımına sıcak su ile liç işlemi yapılarak istenmeyen klorür fazları giderilmiştir. Seçilen bazı saf tozlar, kristalin özelliği geliştirmek amacıyla 1100°C’de tavlama işlemine tabi tutulmuştur. Sentezlenen ve tavlanmış tozların karakterizasyonu, X-ışını difraktometresi (XRD), X-ışını floresans spektrometresi (XRF), taramalı elektron mikroskobu (SEM/EDX) ve dinamik ışık saçma tekniği (DLS) kullanılarak analiz edilmiştir. Sonuçlar, inorganik ergimiş tuz tekniğinin (LiCl/KCl ötektik karışımı) CoCl2, NiCl2 ve NaBH4 toz karışımları arasındaki reaksiyon sırasında oluşan fazlar üzerindeki olumlu etkisini ortaya koymuştur. 750-950°C sıcaklıkları arasında gerçekleşen reaksiyonlarda CoB-Ni2B-CoBx, CoB-Ni4B3 ve CoB-NiB-Ni2Co0.67B0.33 fazlarını içeren ikili ve üçlü metal borür tozları nano boyutta elde edilmiştir. Sentezlenen tozların partikül boyutu ortalama 60 nm civarında hesaplanmıştır.

The present study has been carried out in order to investigate the microstructural properties of WCCo-Mo composite coatings deposited onto a SAE 4140 steel substrate by high velocity oxygen fuel (HVOF) thermal spray. For this purpose, the Mo quantity added to the WCCo was changed as 10, 20, 30 and 40 wt. % percents. The coatings are compared in terms of their phase composition, microstructure and hardness. Phase compound and microstructure of coating layers were examined using X-ray diffractometer (XRD) and scanning electron microscope (SEM). XRD results showed that WCCo-Mo composite coatings were mainly composed of WC, W2C, Co3W3C, Mo2C, MoO2, Mo and Co phases. The average hardness of the coatings increased with increasing Mo content., Bu çalışma, yüksek hızlı oksi yakıt (HVOF) ısıl püskürtme yöntemi ile SAE 4140 çeliği üzerinde üretilen WCCo-Mo kompozit kaplamaların mikroyapısal özelliklerini araştırmak için yapılmıştır. Bu amaç için WCCo tozlarına ilave edilen Mo miktarı % ağ. 10, 20, 30 ve 40 olarak değiştirilmiştir. Kaplamalar, faz bileşimi, mikroyapı ve sertlik özellikleri açısından karşılaştırılmıştır. Kaplama tabakalarının faz bileşimi ve mikroyapısı X-ışını difraktogramı (XRD) ve taramalı elektron mikroskobu (SEM) ile incelenmiştir. XRD sonuçları, WCCo-Mo kaplama tabakasının WC, W2C, Co3W3C, Mo2C, MoO2, Mo ve Co fazlardan oluştuğunu göstermiştir. Kaplamaların sertliği Mo artışı ile artmıştır.