Search

Copyright of Necmettin Erbakan University Dental Journal (NEU Dent J) is the property of Necmettin Erbakan University Dental Journal (NEU Dent J) and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Copyright of Yildiz Journal of Educational Research is the property of KARE Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Various heat treatments are applied to improve the mechanical properties of steels depending on the intended use. In this study, the variation of fatigue strength of H13 hot work tool steel with heat treatment in a GS 550 bath was investigated. It was investigated by applying four different heat treatments as first preheating, second preheating, hardening and second hardening. Each batch of samples was subjected to rotating bending fatigue test at room temperature after heat treatment. The fatigue strength of the untreated samples was determined as 470 MPa. The fatigue strength of the second hardened untempered samples (Group 1) increased to 610 MPa. The fatigue strength of the samples (Group 2), which were annealed for two hours at 550ºC as a second heat treatment after hardening, was measured as 630 MPa. The fatigue strength of the samples (Group 3) was found to be 720 MPa by applying the third heat treatment, which was annealing at 550ºC for two hours and at 610ºC for two hours. The fatigue strength of the samples (Group 4), which were subjected to the fourth heat treatment and tempered for two hours at 550ºC and then at 635ºC for two hours after hardening, was determined as 710 MPa. It has been observed that all applied heat treatments positively affect the fatigue strength of H13 hot work tool steel. While all heat treatments resulted in increased fatigue strength, the highest fatigue strength was obtained with double annealing heat treatment (550 °C and 610 °C two hours) after initial preheating and quenching. [ABSTRACT FROM AUTHOR]

n this study, the effect of induction surface hardening on the fatigue limit of austempered ductile iron was investigated. For this purpose, samples of grade GGG70 ductile iron were austenitized at 900°C for 90 minutes and then austempered in a salt bath at 375 ° C for 120 minutes. Then, surface hardening was performed to the fatigue samples in cast and austempered conditions with high frequency induction. The fatigue strengths of the as cast, austempered, as cast+induction surface hardened and austempered+induction surface hardened specimens were determined by the rotational bending fatigue method. Experimental results show that austempered + surface induction hardened specimens exhibited the best fatigue strength results among the tested samples.