Residual Stress (RS) pattern changes considerably depending on the width of the plates and the welding parameters, having effect on the fatigue strength. Most of the standards do not consider them and in some works, yield stress is taken as residual stress value. It results in a very conservative estimation of fatigue life. Authors developed recently a numerical model to predict more properly the value of RS pattern depending on the plate thickness. In a welded joint, considering the RS and alternating axial loads, the evolution of the stresses is multiaxial, becoming necessary its study. Therefore, the aim of this work is to analyse different fatigue indicator parameters (Smith-Watson-Topper, Fatemi-Socie, and Critical Plane implementation of the Basquin equation) in order to predict the fatigue behaviour of butt-weld components. For that purpose, the numerical model to predict the RS pattern in welded joint developed by this research group is used. more...

In casting parts, due to the manufacturing process, the presence of defects such as porosity, inclusions and oxide films is unavoidable. All these irregularities have a negative effect on the component performance. Several works have demonstrated that, among them, porosity is especially detrimental to the fatigue properties. As most fatigue failures nucleate at the surface of a material, casting defects at or near the surface and surface roughness become an extremely important factor in determining the fatigue strength of cast components. Very little research has been conducted into the influence of both surface quality and porosity on the fatigue behaviour of aluminium castings parts. In the present work, the effects of two different surface qualities (machined and as-cast) on fatigue behaviour of an A356 casting alloy were studied. The S-N curves obtained showed that the cast surface had higher fatigue strength than the machined one. The failure in cast specimens initiated predominantly from valleys of the rough surface near pores or inclusions. On the other hand, in machined surfaces, the cracks initiated directly from surface pores. Thus, the improvement in fatigue life was attributed to a longer crack “initiation” period. more...